The aim of this research was to study the impact of using a short fiber-reinforced composite (SFRC) core on the fatigue performance and fracture behavior of direct large posterior composite restorations. Moreover, the influence of the consistency (flowable or packable) of occlusal composite coverage was assessed. A total of 100 intact molars were collected and randomly distributed into five groups (n = 20). Deep mesio-occlusal-distal (MOD) cavities were prepared in all groups. After adhesive treatment and rebuilding the missing interproximal walls with conventional composite, the specimens in four experimental groups were restored by an SFRC core (everX Flow), which was applied and cured either in bulk or in oblique layers (each 2 mm thick). Packable (G-aenial Posterior) or flowable (G-aenial Injectable) conventional composites were used as a final occlusal layer. The control group was restored with only packable conventional composite. Fatigue survival was measured for all specimens using a cyclic loading machine until a fracture occurred or a total of 25,000 cycles was achieved. Kaplan–Meyer survival analyses were conducted, followed by pairwise log-rank post hoc comparisons. The static load-bearing capacity of surviving teeth was tested using a universal testing machine. Fracture patterns were evaluated visually. There was no statistically significant (p > 0.05) difference in terms of survival between the tested groups. All groups for which flowable SFRC was used showed statistically significantly higher load-bearing capacities compared to the control group (p < 0.05). There were no significant differences regarding fracture resistance among the fiber-reinforced study groups. Regarding the fracture pattern during the survival analysis, all specimens that received SFRC showed a dominantly restorable type of fracture, while the control specimens presented a dominantly non-restorable type. The use of flowable SFRC as a reinforcing core for large MOD direct restorations showed promising achievements regarding fracture behavior.

Excessive cavity preparation and root canal treatment leads to a weakened tooth structure with a lower resistance to fracture. Fiber reinforcement is frequently used to reinforce such teeth, and multiple fiber types and possible applications exist. Various methods for utilizing long fibers to internally splint the remaining cavity walls in the case of large mesio-occluso-distal (MOD) cavities have been proposed; however, no summary of their performance has been written up to now. Our study aims to review the available literature to evaluate and compare the mechanical performance of the different materials and methods utilized for horizontal splinting in large MOD cavities. Three independent authors performed a thorough literature search using PubMed, ScienceDirect, and Google Scholar up until January 2022. The authors selected in vitro studies that used long fibers placed horizontally in posterior teeth with large MOD cavities to reinforce these teeth. From 1683 potentially relevant articles, 11 publications met our inclusion criteria. Seven out of eleven studies showed that horizontal splinting with long fibers improved the fracture resistance of the restored teeth. Three articles showed no significant difference between the fracture resistance of the restored groups. Only one article reported a lower fracture resistance to the horizontally splinted group, compared to conventional direct composite restoration. Within the limitations of this review, evidence suggests that long fiber reinforcement could be used to improve the fracture resistance of heavily restored teeth.

In recent years, composite resin materials have been the most frequently used materials for direct restorations of posterior teeth. These materials have some clinically relevant limitations due to their lack of fracture toughness, especially when used in larger cavities with high volume factors or when utilized as direct or indirect overlays or crown restorations. Recently, short-fiber-reinforced composite materials have been used in bi-structure restorations as a dentine substituting material due to their superior mechanical properties; however, there is no scientific consensus as to whether they can be used as full restorations. The aim of our review was to examine the available literature and gather scientific evidence on this matter. Two independent authors performed a thorough literature search using PubMed and ScienceDirect up until December 2023. This study followed the PRISMA guidelines, and the risk of bias was assessed using the QUIN tool. The authors selected in vitro studies that used short-fiber-reinforced composite materials as complete restorations, with a conventional composite material as a comparison group. Out of 2079 potentially relevant articles, 16 met our inclusion criteria. All of the included studies reported that the usage of short-fiber-reinforced composites improved the restoration’s load-bearing capacity. Fifteen of the included publications examined the fracture pattern, and thirteen of them reported a more favorable fracture outcome for the short-fiber-reinforced group. Only one article reported a more favorable fracture pattern for the control group; however, the difference between groups was not significant. Within the limitations of this review, the evidence suggests that short-fiber-reinforced composites can be used effectively as complete restorations to reinforce structurally compromised teeth.

The aim of this research was to evaluate the mechanical impact of different direct restorations in terms of fracture resistance, and subsequent fracture pattern, in occlusal high C-factor cavities. Furthermore, the adaptation of different direct restorations in the form of gap formation was also evaluated. Seventy-two intact mandibular molars were collected and randomly distributed into three groups (n = 24). Class I occlusal cavities with standardized dimensions were prepared in all specimens. After adhesive treatment, the cavities were restored with direct restorations utilizing three different materials. Group 1: layered conventional packable resin composite (Filtek Ultimate), Group 2: bulk-fill resin composite (SDR), Group 3: bulk-fill short fibre-reinforced composite (SFRC; everX Posterior) covered with packable composite occlusally. Half of the restored specimens underwent static load-to fracture testing (n = 12/group), while the rest underwent sectioning and staining for microleakage evaluation and gap formation analysis. Fracture patterns were evaluated visually among the mechanically tested specimens. The layered composite restoration (Group 1) showed significantly lower fracture resistance compared to the bulk fill groups (Group 2, p = 0.005, Group 3, p = 0.008), while there was no difference in fracture resistance between the other groups. In terms of gap formation values, the layered composite restoration (Group 1) produced significantly higher gap formation compared to the bulk-fill groups (Group 2, p = 0.000, Group 3, p = 0.000). Regarding the fracture pattern, SFRC (Group 3) produced the highest number, while SDR (Group 2) produced the lowest number of repairable fractures. The use of bulk-fill resin composite (fibre or non-fibre-reinforced) for occlusal direct restorations in high C-factor cavities showed promising achievements regarding both fracture resistance and microleakage. Furthermore, the use of short fibre-reinforced bulk-fill composite can also improve the fracture pattern of the restoration-tooth unit. Bulk-fill materials provide a simple and effective solution for restoring and reinforcing high C-factor occlusal cavities.

Facial soft tissue esthetics is a priority in orthodontic treatment, and emerging of the digital technologies can offer new methods to help the orthodontist toward an esthetic outcome. This prospective study aimed to assess the soft tissue changes of the face after six months of retention following Rapid Maxillary Expansion (RME). The sample consisted of 25 patients (13 females, 12 males, mean age: 11.6 years) who presented with unilateral or bilateral posterior crossbite requiring RME, which was performed with a Hyrax expander. 3D facial images were obtained before treatment (T₀) and at the end of a six-month retention period after the treatment (T₁) using a structured-light 3D handheld scanner. Linear and angular measurements were performed and 3D deviation analyses were done for six morphological regions of the face. Significant changes in various areas of the nasal and the upper lip regions were observed. Based on the results of the study and within the limitations of the study, RME with a Hyrax expander results in significant morphological changes of the face after a six-month retention period.

The purpose of this study was to analyze the fracture resistance and marginal leakage of noncarious cervical lesion (NCCL) restorations made of different restorative materials. Eighty upper premolars were randomly divided into four groups (n = 20/group). Standardized NCCL cavity preparations were performed on the buccal surface of the teeth and then restored with four different materials. Group 1: Packable resin composite (PC); Group 2: Highly flowable resin composite (HF); Group 3: Low flowable resin composite (LF); Group 4: Resin modified glass ionomer cement (RMGIC). After restorations were completed, cyclic and static fracture behavior was evaluated using a loading testing machine. Extra restored teeth were sectioned and then stained (n = 5/group). The specimens were viewed under a stereo microscope and the percentage of microgaps at the tooth–restoration interface was calculated. All restored teeth survived after fatigue loading. There was no statistically significant (p > 0.05) difference between the tested restorations after the static loading test. NCCLs restored with highly filled flowable composite showed the least microleakage among the tested groups (p < 0.05). The investigated restorative materials are acceptable for NCCL restorations in terms of fracture resistance and microleakage.