Metallic nanoparticles with virucidal properties dispersed in a polymeric matrix have gained prominence in the scientific community as a rapid and effective alternative that employs the additive manufacturing (AM) or 3D printing method. This study aims to produce filaments for 3D printing using polymer nanocomposites based on polylactic acid (PLA) and copper nanoparticles (CuNPs) in different proportions. The virucidal activity of various proportions of nanoparticles in PLA was investigated. The composites were produced following a mixture design (DOE) with concentrations ranging from 1% to 2% copper nanoparticles, which were blended with PLA using a single-screw extruder. The samples were characterized by thermogravimetry (TG), differential scanning calorimetry (DSC), tensile strength testing, and fracture analysis using scanning electron microscopy (SEM). A thermal analysis of the composites indicated that the CuNPs contributed to an increase in the degradation temperature and crystallization of the PLA. Sample S7 (1.25% of CuNPs) exhibited a 4% increase in the degradation temperature compared to pure PLA. The best tensile strength results were observed in sample S7 (1.25% of CuNPs), 30% more than sample S3 (1.33% of CuNPs) due to good material cohesion, as evidenced by microscopy analyses. Regarding virucidal analyses, most composites demonstrated virus inhibition activity.

This research presents the results of different periods of T6 heat treatment (homogenization and artificial aging) for A356 aluminum alloy used in the fabrication of motorcycles. The samples were cast using gravity die casting, and industrial furnaces for T6 were used in the experiment. Two heat treatment conditions were used, with a total time of 7 h and 12 h, and the results were compared with the alloy without heat treatment. The effects of the reduction of treatment time on mechanical behavior were evaluated in terms of hardness, Charpy and tensile tests, as well as morphological analysis of fractures and microstructural behavior via optical microscopy, SEM-EDS, measurement of eutectic Si evolution, and XRD. Excellent mechanical properties were achieved with a treatment period of 7 h, which achieved a yield strength of 226.58 (±3.76) MPa, tensile strength limit of 264.78 (±4.27) MPa and elongation of 3.41 (±0.47) %. This is competitive with other cast alloys subjected to T6 heat treatment in longer treatment cycles. The peak of hardness and highest impact resistance was recorded for the sample treated for 12 h; however, in the impact test, there was no significant difference between the two experiments.

This study explores the production of composites based on polylactic acid (PLA) reinforced with microcrystalline cellulose (MCC), using Additive Manufacturing technology via LCD. Polylactic acid, being biodegradable and possessing good mechanical properties, was combined with microcrystalline cellulose, which has a high modulus of elasticity, aiming to further improve its performance. Composites with different microcrystalline cellulose contents (1, 3, 5, and 10%) were obtained and compared to pure PLA. Characterization involved thermal, mechanical, morphological, and structural tests. The results showed that the addition of microcrystalline cellulose increases hardness, tensile strength, and modulus of elasticity. Scanning electron microscopy revealed more heterogeneous fracture surfaces in the composites compared to pure polylactic acid. Thermal stability varies according to the microcrystalline cellulose content, with increased degradation observed in some samples, reaching 1%. Increased water absorption was also detected with increasing microcrystalline cellulose concentration, indicating potential limitations in humid environments. The incorporation of microcrystalline cellulose, especially at moderate concentrations such as 3%, proved to be an effective strategy for improving the mechanical properties of polylactic acid.

The aim of this study is to obtain poly(lactic acid) polymeric nanocomposites and carbon nanotubes for application in drone propellers produced through 3D printing. In this work, a filament based on poly(lactic acid)—PLA/functionalized carbon nanotube (CNT) composites was prepared for the fused deposition modeling (FDM) process. The effects of CNT content (0.2–1.0%), temperature variation, and extruder screw rotation variation were applied in the Design of Experiments (DOE) tool, where the main factors contributing to filament quality, focusing on mechanical strength, were identified. Through this tool, an optimum point for the material’s mechanical strength was reached, showing a value of 48.87 MPa, 43.17% above the initial value of 27.77 MPa. The response surface curve revealed a region where new filaments with similar mechanical strength values to those found in this work could be obtained. The results demonstrate that CNT content, extruder screw rotation, and extruder temperature directly influence filament quality. The data obtained from Thermogravimetry (TG) and Derivative Thermogravimetry (DTG) curves show that the addition of 0.6% CNT by weight does not significantly modify PLA degradation resistance, despite slight differences in temperatures. The main reason for these alterations is the dispersion of CNTs in the PLA matrix and CNT agglomeration. Through the demonstrated simulation, it is possible to confirm the application of the developed material in drone propeller manufacturing, facilitating access and providing new opportunities for users.