As a main component of the magnetic pulse welding (MPW) system, the working coil exerts a great influence on the electromagnetic force and its distribution, which, in turn, affects the quality of the MPW joints. This study proposes a structural parameter optimization of the MPW coil, with the objective of achieving a higher induced current density on the flyer plate. The optimal Latin hypercube sampling technique (OLHS), Kriging approximate model, and the Non-Linear Programming by Quadratic Lagrangian (NLPQL) algorithm were employed in the optimization procedure, based on the finite element model built in LS-DYNA. The results of the sensitivity analysis indicated that all the selected parameters of the coil had a specific influence on the induced current density in the flyer plate. The optimized coil structure serves to refine the pulse current flowing path within the coil, effectively reducing the current loss within the coil. Additionally, the structure reduces the adverse effect of the current within the coil on the induced current within the flyer plate. Numerical results show the peak-induced current of the flyer plate increasing by 25.72% and the maximum Lorentz force rising by 58.10% at 25 kJ with the optimized coil structure. The experimental results show that with the same 25 kJ discharge energy, the optimized coil could increase the collision velocity from 359.92 m/s to 458.93 m/s. Moreover, 30 kJ of discharge energy should be needed to achieve the failure mode of base material failure with the original coil, while only 15 kJ should be applied to the optimized coil. These findings verify the optimization model and give some outline for coil design.

Three-way tube with single-side flanged features has been widely used in automobile and airplane fields. The susceptibility of lightweight alloys to crack at room temperature makes the preparation of aluminum alloy Three-way tubes a challenge. In this paper, the numerical model of electrohydraulic forming process was established and validated. The deformation process was analyzed. Three-way tubes of different design heights were prepared. The clearance and wall thickness were used to characterize the forming quality. The effect of discharge voltage on forming quality was explored. Results showed that the increase of discharge voltage could improve the shape accuracy of three-way tube. Spring-back was observed, but the maximum clearance in straight-wall area was controlled within 0.16 mm. With the increase of discharge voltage, the thickness decreased. This process enables the preparation of three-way tubes of different design heights without cracking.

A structure for joining thin-walled 6061-T6 aluminum alloy tube (outer tube) and Q195 steel tube (inner tube) by electromagnetic flanging process was proposed. The formation process, mechanical properties, failure modes, and morphology of the joint were investigated. The results showed that the outer tube impacted the inner tube, the flanges of the prefabricated holes on the outer tube were embedded into the prefabricated holes of the inner tube under the action of Lorentz force, and thus the mechanical locking joint was obtained. There were two tensile failure modes for the joints: Pull-out and fracture. Specifically, when the discharge energy was relatively high, the failure mode changed from pull-out to fracture. Combining the results of tensile tests and morphology observations, the maximum loads of the joints increased with the discharge energy. However, excessive discharge energy would lead to the brittle fracture of the inner tube, which was not beneficial to the service. Better discharge energy and the maximum load of the joint at this discharge energy were obtained.