Sandwich structured (SS) composites demonstrate considerable flexural stiffness and high strength-to-weight ratios and can be tailored as functional materials. Historically they have been constrained to specific material types and geometry due to limitations in manufacturing methods. However, employing additive manufacturing (AM), specifically direct ink writing (DIW), can provide an alternative method for making SS composites with complex and controllable micro and mesostructures with multifunctionality targeted at desired mechanical, thermal, and electrical properties. DIW, an extrusion-based AM technique, uses a viscous and thixotropic ink with desired components that, once printed, is cured to obtain the final complex net shape parts. In this paper, a novel hybrid AM technique is employed to manufacture SS composite materials containing bisphenol A-based epoxy core and carbon fiber reinforced polymer (CFRP) face sheets that are fabricated via DIW and vacuum infusion process (VIP), respectfully. We demonstrate that the fabrication of these SS composites can be tailored from a thermosetting material, from which additives and/or various lattice structures can be manufactured to achieve enhanced and desirable mechanical integrity with functional properties. Surface topology and mechanical testing techniques are used to characterize the fabricated hybrid SS composites to study and assess mechanical stability. A rheo-kinetic cure model was developed for the core material to allow for additive manufacturing process requirements while ensuring complete cross-linking for the thermoset-based core material. Because of the ability to obtain relatively small core-thickness and controlled architecture, this method now allows for fabricating layered micro-sandwich structures for realizing further light-weighting in relevant applications.

Pultruded carbon fiber-reinforced composites are attractive to the wind energy industry due to the rapid production of highly aligned unidirectional composites with enhanced fiber volume fractions and increased specific strength and stiffness. However, high volume carbon fiber manufacturing remains cost-prohibitive. This study investigates the feasibility of a pultruded low-cost textile carbon fiber-reinforced epoxy composite as a promising material in spar cap production was undertaken based on mechanical response to four-point flexure loading. As spar caps are primarily subjected to flexural loading, large-span four-point flexure was considered, and coupon testing was restricted to tensile modulus and compression strength assessment. High-resolution spatial fiber optic strain sensing was utilized to determine spatial strain distribution during four-point flexure, revealing consistent strain along the length of the part and proved to be an excellent option for process manufacturing quality examination. Additionally, holes with diameters of 2.49 mm, 5.08 mm, and 1.93 mm were drilled through the thickness of full-width parts to determine the feasibility of structural health monitoring of pultruding parts internal to wind blades via fiber optic strain sensing.

Infusible thermoplastic Elium® family of resins from Arkema have garnered much attention in recent years as a possible replacement for thermoset resins in laminate and sandwich composite manufacturing for wind blade applications due to its ease of recyclability and the ability to utilize existing manufacturing processes without imposing complicated variations. However, physical and mechanical properties of the proposed Elium® based thermoplastic composites must be comparable to existing epoxy (thermoset) based composites using manufacturing processes relevant for large wind turbine blades. A 13-meter-long demonstration blade was manufactured for that purpose and sandwich samples were obtained from that project for a detailed study. This paper details three-point flexural properties of unidirectional E-glass fiber reinforced acrylic and epoxy based sandwich panels with identical balsa wood core materials. In addition, to evaluate the relative merit considering debond failure mode, the interfacial critical strain energy release rate, predominantly in mode-1, was compared via single cantilever beam testing. In sandwich composites constructed with balsa wood core material, resin uptake by the balsa core is traditionally impeded via the insertion of a scrim material at the facesheet to core interface. Results revealed that inclusion of scrim mesh layer at the facesheet to core interface reduced flexural properties and strain energy release rates in panels infused with acrylic resin but did not significantly reduce these properties in epoxy infused facesheets.