This work investigated the wear behavior of ultrafine-grained Ti₆₅Nb_23.33Zr₅Ta_1.67Fe₅ (at.%, TNZTF) and Ti₆₅Nb_23.33Zr₅Ta_1.67Si₅ (at.%, TNZTS) alloys fabricated by high-energy ball milling and spark plasma sintering. Wear tests were conducted in a simulated physiological solution under both reciprocating sliding and fretting wear conditions with different loads, frequencies, and stroke lengths. The microstructures, mechanical properties, and anti-wear properties of the investigated alloys were characterized. The results showed that the TNZTF and TNZTS alloys had much less wear volume than the commonly used Ti-6Al-4V (TC4) alloy and commercially pure titanium (CP-Ti). The TNZTF and TNZTS alloys exhibited much more smooth wear surfaces and shallower wear scars compared with TC4 and CP-Ti. The investigated alloys exhibited different wear mechanisms under the reciprocating sliding wear conditions, while they were similar under the fretting wear conditions. Compared with TC4 and CP-Ti, the fabricated TNZTF and TNZTS alloys showed a substantially higher wear resistance, owing to their ultrafine-grained microstructure and superior hardness. Additionally, the addition of Nb and Zr further enhanced the wear resistance by forming a protective Nb₂O₅ and ZrO₂ oxide film. This work provides guidance for designing new biomedical titanium alloys with excellent wear resistance.

To quickly repair the inner-surface damage to the hydraulic support cylinder caused by frequent scratches, corrosion, and wear in the process of fully mechanized coal mining, this paper proposes a method of high-frequency induction cladding (HIC) copper alloy on inner-wall of cylinder (IWC) to improve the corrosion, sealing and pressure retention performance of hydraulic cylinders combined with numerical simulation and experimental study. Firstly, a numerical temperature field model for HIC of copper alloy on the IWC is established to investigate various distribution patterns and influencing factors including frequency of induction heating, gap between coil and cladding, power supply rating, cladding thickness and side length of square section of induction coil, etc. Subsequently, an HIC test experiment is conducted to rigorously validate the numerical temperature field model and the experiment employs a meticulously collected dataset of temperature measurements, confirming the model’s accuracy and consistent alignment with anticipated changing trends. In addition, the experiment results were verified through microstructure observation, microhardness testing, friction-wear testing, and electrochemical corrosion parameters, which shows that the factors of induction heating frequency and others have obvious effects on the temperature field distribution of HIC copper alloy on the IWC. Under these working conditions (cladding thickness 1.5 mm, power supply rating 120 kW, heating frequency 120 kHz, gap between the cylindrical workpiece and the induction coil 3 mm, induction coil cross-sectional side length of 10 mm), the thermal impact on the cylinder barrel matrix is minimal, the metallurgical bonding between the cladding layer and the matrix is good, and there are no over burning and porosity defects.