Niobium pentoxides are promising acid catalysts for the conversion of biomass into fuels and chemicals. Developing new synthesis routes is essential for designing niobium pentoxide catalysts with improved activity for specific practical processes. Here we show a synthesis approach in acetophenone, which produces nanostructured niobium pentoxides with varying structure and acidity that act as efficient acid catalysts. The oxides have orthorhombic structures with different extents of distortions and coordinatively unsaturated metal atoms. A strong dependence is observed between the type and strength of the acid sites and specific structural motifs. Ultrasmall niobium pentoxide nanoparticles, which have strong Brønsted acidity, as well as Lewis acidity, give product yields of 96% (3 h, 140 °C, 100% conversion), 85% (3 h, 140 °C, 86% conversion), and 100% (3 h, 110 °C, 100% conversion) in the reactions of furfuryl alcohol, 5-(hydroxymethyl)furfural, and α-angelica lactone with ethanol, respectively.

Nanocomposites of SO₃H-functionalized carbon/non-porous silica solid acid catalysts for the synthesis of useful bio-products.

Mesoporous aluminosilicates of the type Al-TUD-1, prepared via “green”, low-cost, non-surfactant templating routes, are effective and versatile heterogeneous acid catalysts for the production of useful bio-based furanic ethers and levulinate esters, via the reactions of the biorenewable substrates 5-hydroxymethyl-2-furfural (Hmf) or furfuryl alcohol (FA) with aliphatic alcohols. The identification of reaction intermediates and products by comprehensive two-dimensional gas chromatography combined with time-of-flight mass spectrometry was carried out, giving mechanistic insights. Ethyl levulinate (EL) was formed from FA or Hmf as substrates, with higher EL yields being reached in the former case. Different types of alkyl levulinates may be synthesized from FA using Al-TUD-1 catalysts. On the other hand, 5-(ethoxymethyl)furan-2-carbaldehyde may be formed as the main product from Hmf. Modifications of the properties of Al-TUD-1 involved varying the Si/Al ratio and applying a post-synthesis acid treatment. The influence of these factors and of the reaction conditions on the catalytic reactions was investigated. The efficient regeneration and recyclability of Al-TUD-1 was assessed.