Reaction of a series of (E)-3-phenyl-4-(p-substituted phenyl)-3-buten-2-ones with p-sulfamylphenyl hydrazine in glacial acetic acid gave the corresponding hydrazones, subsequent treatment of which with 30% HCl afforded pyrazole-1-sulphonamides. On the other hand, refluxing of chalcones with either thiosemicarbazide or isonicotinic acid hydrazide in ethanol containing a few drops of acetic acid gave pyrazoline-1-thiocarboxamides and isonicotinoyl pyrazolines, respectively. The structures of the synthesized compounds were determined on the basis of their elemental analyses and spectroscopic data. The antimicrobial activity of the newly isolated heterocyclic compounds was evaluated against Gram-positive, Gram-negative bacteria and fungi. Most of the compounds showed a moderate degree of potent antimicrobial activity.

A series of 3,5-disubstituted pyrazole-1-carboxamides were obtained by treatment of chalcones with semicarbazide hydrochloride in dioxane containing sodium acetate/acetic acid as a buffer solution. N-acetyl derivatives of pyrazole-1-carboxamides were isolated in good yields either by treatment of the carboxamide derivatives with acetic anhydride or refluxing chalcones with semicarbazide in ethanol containing few drops of acetic acid to give the corresponding hydrazones. Subsequent treatment of hydrazones with acetic anhydride gave the desired N-acetyl pyrazole-1-carboxamides derivatives. When chalcones were refluxed with dioxane containing few drops of acetic acid, 4,5-dihydropyrazole-1-carboxamides were isolated, which were subsequently oxidized using 5% sodium hypochlorite in dioxane to afford pyrazole-1-carboxamides. The structures of isolated compounds were confirmed by elemental analyses and spectral methods. The isolated compounds were tested for their antimicrobial activities.

Some new heterocyclic compounds containing isoxazole, pyrazole and oxadiazole ring systems were prepared from various chalcones. The synthesized compounds have been characterized by elemental analysis and spectral methods. These compounds were screened for their antimicrobial activities.

A series of novolac phenolic polymeric networks (NPPN) were prepared via an acid-catalyzed polycondensation reaction of formaldehyde with chalcones possessing a p-phenolic OH group. When p-hydroxybenzaldehyde was treated with formaldehyde under the same conditions, a phenolic polymer (PP) was obtained. The resulting polymers were isolated in excellent yields (83–98%). Isolated polymers (NPPN, PP) were characterized using FTIR, TGA, and XRD. The results obtained from the TGA revealed that all prepared phenolic polymers have high thermal stability at high temperatures and can act as thermosetting materials. XRD data analysis showed a high degree of amorphousness for all polymers (78.8–89.2%). The electrical conductivities and resistivities of all chalcone-based phenolic networks (NPPN) and p-hydroxybenzaldehyde polymer (PP) were also determined. The physical characteristics obtained from the I-V curve showed that the conductivity of phenolic polymers has a wide range from ultimately negligible values of 0.09 µS/cm up to 2.97 μS/cm. The degree of polarization of the conjugated system’s carbonyl group was attributed to high, low, or even no conductivity for all phenolic polymers since the electronic effects (inductive and mesomeric) could impact the polarization of the carbonyl group and, consequently, change the degree of the charge separation to show varied conductivity values.

Two polyesteramides were synthesized via polycondensation reactions involving 4′-amino-4-hydroxychalcone 3a with succinic acid (4) and terephthalic acid (5), utilizing phosphoryl chloride as a chlorinating agent. A parallel reaction with (E)-1,3-bis(4-hydroxyphenyl) prop-2-en-1-one chalcone (3b) yielded two polyesters under identical conditions. The resultant polymers were obtained with excellent yields ranging from 93 % to 98 %. Characterization of the obtained polyesteramides and polyesters was conducted using various analytical techniques. Fourier-transform infrared spectroscopy (FTIR) evidenced the disappearance of the OH group's broad band from the initial monomers, providing strong support for polymer formation. Thermal gravimetric analysis (TGA) results indicated high thermal stability of all prepared polymers at elevated temperatures, designating them as potential thermoplastic polymers. Powder X-ray diffraction (XRD) outcomes demonstrated a significant amorphous nature for all synthesized polymers, with degrees ranging from 67.56 % to 74.75 %. Analysis of current/voltage (I-V) curves revealed a wide spectrum of electrical conductivity for polymers containing chalcone in their repeating units, ranging from negligibly low values of 0.08 µS/cm to 0.31 μS/cm, indicating their potential as semiconducting materials. Variations in conductivity across synthesized polymers were attributed to the degree of conjugation in polymeric chains and their crystallinity levels.