In this study, polypyrrole-based activated carbon was prepared by the carbonization of polypyrrole at 650 °C for 2 h in the presence of four-times the mass of KOH as a chemical activator. The structural and morphological properties of the product (polypyrrole-based activated carbon (PPyAC4)), analyzed by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and thermogravimetric analysis, support its applicability as an adsorbent. The adsorption characteristics of PPyAC4 were examined through the adsorption of lead ions from aqueous solutions. The influence of various factors, including initial ion concentration, pH, contact time, and adsorbent dose, on the adsorption of Pb²⁺ was investigated to identify the optimum adsorption conditions. The experimental data fit well to the pseudo-second-order kinetic model (R² = 0.9997) and the Freundlich isotherm equation (R² = 0.9950), suggesting a chemisorption pathway. The adsorption capacity was found to increase with increases in time and initial concentration, while it decreased with an increase in adsorbent dose. Additionally, the highest adsorption was attained at pH 5.5. The calculated maximum capacity, q_m, determined from the Langmuir model was 50 mg/g.

Herein, a facile green synthesis route was reported for the synthesis of Ag–ZnO nanocomposites using potato residue by simple and cost effective combustion route and investigated the photocatalytic degradation of methylene blue (MB) dye. In the preparation potato extract functioned as a biogenic reducing as well as stabilizing agent for the reduction of Ag + , thus eliminating the need for conventional reducing/stabilizing agents. Ag–ZnO nanocomposites with different Ag mass fractions ranging from 2 to 10% were characterized by using XRD, FT-IR, XPS, SEM, TEM, and UV–Vis spectroscopy. XRD analysis revealed that the as prepared Ag–ZnO nanocomposites possessed high crystallinity with hexagonal wurtzite structure. TEM and SEM images showed that the Ag–ZnO nanocomposites in size ranging from 15 to 25 nm have been obtained, and the particle size was found to increase with the increase in percentage of Ag. FTIR results confirmed the characteristics band of ZnO along with the Ag bands. XPS analysis revealed a pair of doublet with peaks corresponding to Ag and a singlet with peaks corresponding to ZnO. With the increase of concentration of Ag in ZnO, the intensity of NBE emission in the PL spectra was observed to be decrease, resulted to the high photocatalytic activity. Photocatalytic properties of Ag–ZnO nanocomposites evaluated against the MB dye under visible-light irradiation showed superior photodegradation of ~ 96% within 80 min for 2% Ag–ZnO nanocomposites. The apparent reaction rate constant for 2% Ag–ZnO nanocomposites was higher than that of other nanocomposites, which proved to be the best photocatalyst for the maximum degradation of MB. Furthermore, various functional parameters such as dosing, reaction medium, concentration variation were performed on it for better understanding. The enhancement in photocatalytic degradation might be due to the presence of Ag nanoparticles on the surface of ZnO by minimizing the recombination of photo induced charge carriers in the nanocomposites.

In this study, we report the fabrication of graphitic carbon nitride doped zinc oxide nanocomposites, g-C₃N₄/ZnO, (Zn-Us) by using different amount of urea. They were further characterized by X-ray Diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), Raman, UV-vis, Scanning electron microscopy (SEM), and Transmission electron microscopy (TEM) techniques. The prepared nanocomposites were used as photocatalysts for the mineralization of the light sensitive dyes Methylene Blue (MB) and Rose Bengal (RB) under UV light irradiation, and corresponding photo-mechanism was proposed. Benefiting from these photocatalytic characteristics, urea derived g-C₃N₄/ZnO photocatalysts have been found to have excellent photodegradation activity against the MB and RB for 6 h and 4 h, respectively. Under the given experimental conditions, the degradation percentage of fabricated Zn-Us were shown ~90% for both model dyes. Compared to cationic MB dye, anionic RB dye is more actively degraded on the surface of prepared photocatalysts. The results obtained can be effectively used for future practical applications in wastewater treatment

The construction of a UV-Vis and direct sunlight functioning photocatalyst is a puzzling task for organic pollutant removal.