A series of NiO/C nanocomposites with NiO concentrations ranging from 10 to 90 wt% was synthesized using a simple and efficient two-step method based on non-isothermal decomposition of Nickel(II) bis(acetylacetonate). X-ray diffraction (XRD) measurements of these NiO/C nanocomposites demonstrate the presence of β-NiO. NiO/C nanocomposites are composed of spherical particles distributed over the carbon support surface. The average diameter of nickel oxide spheres increases with the NiO content and are estimated as 36, 50 and 205 nm for nanocomposites with 10, 50 and 80 wt% NiO concentrations, respectively. In turn, each NiO sphere contains several nickel oxide nanoparticles, whose average sizes are 7–8 nm. According to the tests performed using a three-electrode cell, specific capacitance (SC) of NiO/C nanocomposites increases from 200 to 400 F/g as the NiO content achieves a maximum of 60 wt% concentration, after which the SC decreases. The study of the NiO/C composite showing the highest SC in three- and two-electrode cells reveals that its SC remains almost unchanged while increasing the current density, and the sample demonstrates excellent cycling stability properties. Finally, NiO/C (60% NiO) composites are shown to be promising materials for charging quartz clocks with a power rating of 1.5 V (30 min).

Determining the age of ancient architectural and cultural monuments is a significant scientific problem. An approach based on the transformation of portlandite into calcite and subsequent recrystallization of calcite is considered, which allows for estimating the relative age of ancient brickworks for local groups of historic buildings based on the results of diffraction studies of powder samples of carbonate mortars and measurements of samples with a known age. This article presents the results of the study of lime mortars of ancient brickwork. Under natural conditions, the process of transformation of portlandite into calcite takes from 100 to 200 years. The rate of this process is influenced by temperature, humidity, peculiarities of interaction with carbon dioxide contained in the air, etc. Examples show that portlandite is completely transformed into calcite in masonry mortars of the 18th century and that portlandite is not found in older mortars. It was determined that after the transformation of portlandite into calcite, an increase in the degree of recrystallization of calcite is observed, which manifests itself in powder diffraction patterns in the relative broadening of the diffraction peak of calcite hkl 104. In a detailed study, an estimate of the peak width at half maximum (FWHM) associated with the degree of crystallinity is effective. The actual data are given, which show that in older lime mortars the degree of recrystallization of calcite is higher than in younger ones. This fact makes it possible to indirectly determine the relative age of brickwork and masonry of various buildings of architectural heritage, which is especially relevant for the objects with the use of lime mortars of the northern provinces of the Byzantine Oecumene and other periods of various cultures.

For Li₃Q₂SbO₆, the ground state below T_f = 5 K is spin-clusters, whereas Na₃Q₂SbO₆ stays paramagnetic down to 2 K. Polyhedral view of Li₃Q₂SbO₆: (Q_0.67Li_0.33)O₆ cyan, SbO₆ yellow, (Li_0.74Q_0.26)O₆ grey, and (Li_0.81Q_0.19)O₆ pink.