The main aim of this study was to investigate the improved autogenous healing of concrete caused by a crystalline admixture in combination with textile reinforced concrete (TRC). This phenomenon (improved healing) has not yet been described by any independent study, and not at all in relation to TRC. The results of the study confirmed that the interaction between TRC and the crystalline admixture’s self-healing ability is advantageous and usable. The application of crystalline admixture could ensure the long-term entirety of the TCR element, where microcracks could occur. This allows for the creation of advantageous, thin (achieved by TRC) and waterproof (achieved by the crystalline admixtures) concrete structures. Moreover, this does not depend on temperature in the range of 4–30 °C (lower temperatures are of course problematic, as for most other cementitious materials). However, the interaction of both materials has its limits; the cracks must not be too wide (max. 0.1 mm), otherwise they will not heal. On the other hand, the advantage is that it does not matter what type of cement is used (CEM I and CEM II showed the same results), and the composition of the newly formed crystals in the cracks corresponds to the composition of the C-S-H gel, so it can be assumed that secondary hydration of the Portland cement occurred in the crack area.

The use of recycled aggregate concrete is mainly negatively affected by its poorer mechanical and long-term properties. However, there are few structural applications for which recycled aggregates can be used. In this case study, the possibility of use as massive external reinforcement wall is verified. For this structural application, the most important characteristics are freeze–thaw resistance, and carbonation resistance and then the mechanical properties such as compressive strength. Durability characteristics of the materials have been tested and improved in the study. The mechanical properties and durability of recycled aggregated concrete have been verified and crystalline mixture has been used to improve durability. The specific structural application of the massive external reinforcement wall is for the renovation of the Czech WW2 concrete fortification, which is one of the most important cultural heritages of the Czech Republic of the 20th century. However, these buildings have not yet been professionally rebuilt, but this research project aims to change this trend. The thickness of the bunker wall is between 0.5 and 3.5 m (depending on the type of bunker) which leads to a huge amount of concrete and primary resources consumption; however, the security function is not necessary today, so the reconstruction could be provided by recycled aggregate concrete. The results showed a positive effect of the crystalline mixture on the essential properties of recycled aggregate concrete. Recycled aggregate concrete with a complete replacement of aggregate by recycled concrete or masonry aggregate is possible to use for the reconstruction of the Czech WW2 concrete fortification and save natural aggregate as a primary resource.

The use of recycled masonry aggregate for concrete is mostly limited by the worse properties in comparison with natural aggregate. For these reasons it is necessary to find ways to improve the quality of recycled masonry aggregate concrete and make it more durable. One possibility is utilization of crystalline admixture which was verified in this study by laboratory measurements of key material properties and durability. The positive influence of mineral admixture was proved for freeze-thaw resistance. The positive impact to carbonation resistance was not unambiguous. In conclusion, the laboratory evaluation shows how to improve the durability of recycled masonry aggregate concrete, however, it is necessary to investigate more about this topic.

Concrete is a relatively new structural material, hence the remediation of concrete structures is very rare. There are a lot of concrete fortifications in the Czech Republic, which were built just before WW2. These bunkers formed a long defensive line along the Czechoslovak borders as a protection against Hitler’s army. Today, after 80 years, many of the bunkers are listed as Czech national technical monuments with a strict protection of their historical authenticity. The article describes the technical survey and the possible conservation method of a selected concrete fortification, which exhibits a number of moisture related problems. The studied two-storey, heavily fortified bunker is situated close to the northern border of the Czech Republic, former Czechoslovakia. A detailed survey of the building includes the analysis of the interior environment parameters and laboratory testing of the used concrete. A long-term diagnosis identified the main problem, which lies in the inhomogeneity of the used concrete and the relating massive water ingress. However, the monitored bunker currently does not serve as a military structure and, therefore, a simple solution to improve the internal environment was suggested on the basis of the conducted measurements. With respect to the main causes of failures, the authors suggested a conservation method based on using a crystallizing coating. The suitability of the method was first verified under laboratory conditions and then also on the real bunker.

The aim of the research was focused on the functionality of three types of waterproofing screeds from the perspective of their use in building structures. Bitumen, polymer, silicate (mineral) were studied in terms of their cohesion with the substrate and their sealing ability, used in combination with different building materials—ceramics, concrete, lime-sand bricks and marl stone, the permeability properties of which were taken into consideration, too. The cohesion was also studied after the freeze-thaw exposure to take into account the aspects of durability. During the experimental program, the basic waterproofing ability of all types of tested screeds applied on building materials was confirmed. Comparing the overall tested screeds, despite the best adhesion of the polymer-based screed, this material exhibited the lowest durability after the freeze-thaw exposure. The bitumen and silicate (mineral) screed attained similar values of adhesion to the studied base materials. However, they differ in their ability to withstand freeze-thaw cycles over time. The modified water permeability test on model masonry specimens was performed. No leakage of water during the test was monitored for the specimens with all types of applied screeds over time, and, in addition, water had not penetrated through the bricks, nor through the joints. The waterproofing effect of the screed is not affected by the joints in masonry.

The impact of fire on natural stone structures is a critical concern, particularly for historical buildings. This study examines the residual mechanical properties of sandstone after exposure to high temperatures. Cylindrical sandstone samples were heated to temperatures up to 900 °C and subsequently tested under uniaxial compression. The results indicate that mechanical degradation becomes significant beyond 460 °C, with compressive strength decreasing by up to 43% at 900 °C. Young’s modulus also declined substantially, while axial strain increased, indicating progressive structural weakening. Additionally, visible colour changes suggest mineralogical transformations. These findings provide essential insights into the fire-induced deterioration of sandstone, offering valuable guidance for the preservation and restoration of historical stone structures.