In the present study, inflation tests with free axial extension of 15 human vena saphena magna were conducted ex vivo to obtain data suitable for multi-axial constitutive modeling at overloading conditions (pressures up to approximately 15kPa). Subsequently the data were fitted with a hyperelastic, nonlinear and anisotropic constitutive model based on the theory of the closed thick-walled tube. It was observed that initial highly deformable behavior (up to approximately 2.5kPa) in the pressure-circumferential stretch response is followed by progressive large strain stiffening. Contrary to that, samples were much stiffer in longitudinal direction, where the observed stretches were in the range 0.98-1.03 during the entire pressurization in most cases. The effect of possible residual stress was evaluated in a simulation of the intramural stress distribution with the opening angle prescribed to 0°, 10°, 20°, 30°, 40°, and 50°. The result suggests that the optimal opening angle making the stress distribution through the wall thickness uniform is about 40°. The material parameters presented here are suitable for use in mechanobiological simulations describing the adaptation of the autologous vein wall after bypass surgery.

The effects of the polyvinyl alcohol (PVA) concentration on mechanical properties of hydrogels based on blends of native or denatured collagen / PVA were examined. Blends of PVA with collagen were obtained by mixing the solutions in different ratios, using glycerol as a plasticizer. The solutions were cast on polystyrene plates and the solvent was allowed to evaporate at room temperature. Uniaxial tensile tests were performed in order to obtain the initial modulus of elasticity (up to deformation 0.1), the ultimate tensile stress and the deformation at failure of the material in the water-saturated hydrogel form. It was found that the material was elastic and the addition of PVA helped to enhance both the ultimate tensile stress and modulus of elasticity of the films. Samples prepared from denaturated collagen showed the higher ultimate tensile stress and the deformation at failure in comparison with those prepared from native collagen. The results suggest that we could expect successful application of the collagen/PVA biomaterial for tissue engineering.

Modern tissue engineering requires not only degradable materials promoting cell growth and differentiation, but also vascularization of the engineered tissue. Porous polylactide/polycaprolactone (PLA/PCL, ratio 3/5) foam scaffolds were prepared by a combined porogen leaching and freeze-drying technique using NaCl (crystal size 250–500 µm) and a water-soluble cellulose derivative (Klucel^TM E; 10–100% w/w relative to the total PLA/PCL concentration) as porogens. Scanning electron microscopy, micro-CT, and Brunauer–Emmett–Teller analysis showed that all scaffolds contained a trimodal range of pore sizes, i.e., macropores (average diameter 298–539 μm), micropores (100 nm to 10 μm), and nanopores (mostly around 3.0 nm). All scaffolds had an open porosity of about 90%, and the pores were interconnected. The size of the macropores and the nanoporosity were higher in the scaffolds prepared with Klucel. Nanoporosity increased water uptake by the scaffolds, while macroporosity promoted cell ingrowth, which was most evident in scaffolds prepared with 25% Klucel. Human adipose-derived stem cells co-cultured with endothelial cells formed pre-vascular structures in the scaffolds, which was further enhanced in a dynamic cell culture system. The scaffolds are promising for the engineering of pre-vascularized soft tissues (relatively pliable 10% Klucel scaffolds) and hard tissues (mechanically stronger 25% and 50% Klucel scaffolds).

Pulmonary artery banding is a surgical procedure performed when there is a shunt between the left and right ventricle. Its aim is to constrict the lumen of the pulmonary artery by using a band to reduce blood flow to the lungs. In this study, we report the results of investigating the mechanical properties of a composite composed of poly(L-lactide-co-ε-caprolactone) layers and a collagen matrix (PLCL-COLL). PLCL layers were obtained by electrospinning, impregnated with collagen solution, and finally cross-linked to increase the stiffness of the material. Bands of PLCL-COLL were implanted into a rat peritoneum and explanted after 1, 3, and 6 months in vivo. The mechanical properties of the material before and after implantation were determined using uniaxial tensile tests. The same was done with samples of strips prepared from GORE-TEX material. By comparing the results of tensile tests before implantation and after explantation, it was found that PLCL-COLL degrades in the rat's body and that it exhibits a mechanical response showing of elastic modulus values that correspond well to arterial biomechanics (elastic modulus measured in the initial linear region of the deformation was found to be: 4.14 MPa ± 1.11 MPa, 2.34 MPa ± 1.02 MPa, 1.11 MPa ± 0.77 MPa, and 0.88 MPa ± 0.60 MPa before implantation, and 1, 3, and 6 months after implantation respectively). Similar to the elastic modulus, the strength of the PLCL-COLL composite decreased during in vivo exposure (1.32 ± 0.32 MPa, 0.60 ± 0.26 MPa, 0.44 ± 0.11 MPa, and 0.46 ± 0.28 MPa before implantation, and 1, 3, and 6 months after implantation respectively). In our experiments, PLCL-COLL material was always more compliant than GORE-TEX (elastic modulus 34.7 MPa ± 2.06 MPa before implantation, and 9.35 MPa ± 6.80 MPa after implantation). The results suggest that PLCL-COLL could be a suitable candidate for the development of artery banding tapes, and also for further use in cardiovascular surgery.