Cyanide is an extreme hazard and extensively found in the wastes of refinery, coke plant, and metal plating industries. A simple, fast, cost-effective, room-temperature wet chemical route, based on cyclohexylamine, for synthesizing zinc oxide nanoparticles in aqueous and enthanolic media was established and tested for the photodegradation of cyanide ions. Particles of polyhedra morphology were obtained for zinc oxide, prepared in ethanol (ZnOE), while spherical and some chunky particles were observed for zinc oxide, prepared in water (ZnOW). The morphology was crucial in enhancing the cyanide ion photocatalytic degradation efficiency of ZnOE by a factor of 1.5 in comparison to the efficiency of ZnOW at an equivalent concentration of 0.02 wt.% ZnO. Increasing the concentration wt.% of ZnOE from 0.01 to 0.09 led to an increase in the photocatalytic degradation efficiency from 85% to almost 100% after 180 min and a doubling of the first-order rate constant (k).

Activated carbon has been synthesized from local palm shell, cardboard and plastics municipal waste in the Kingdom of Saudi Arabia. It exhibits a surface area of 930 m²/g and total pore volume of 0.42 cm³/g. This pristine activated carbon has been further anchored with nickel, palladium and platinum metal particles by ultrasound-assisted impregnation. Deposition of nanosized Pt particles as small as 3 nm has been achieved, while for Ni and Pd their size reaches 100 nm. The solid-gas hydrogenation properties of the pristine and metal-anchored activated carbon have been determined. The pristine material exhibits a reversible hydrogen storage capacity of 2.3 wt% at 77 K and 3 MPa which is higher than for the doped ones. In these materials, the spillover effect due to metal doping is of minor importance in enhancing the hydrogen uptake compared with the counter-effect of the additional mass of the metal particles and pore blocking on the carbon surface.