Background: Surface roughness associated with improper finishing/polishing of restorations can result in plaque accumulation, gingival irritation, surface staining, and poor esthetic of restored teeth. The study aimed to evaluate the efficiency of various finishing and polishing systems and time using various procedures on surface roughness of some esthetic restorative materials. Materials and Methods: In this in vitro study, samples of two composite materials, compomer and glass ionomer cement (GIC) materials, were fabricated. Finishing and polishing were done immediately (n = 40) and after 1 week (n = 40) using four systems (diamond bur + soflex discs; diamond bur + Astropol polishing brush; tungsten carbide bur + soflex discs; tungsten carbide bur + Astropol polishing brush). Surface roughness was measured using surface profilometer. Data were statistically analyzed by t-test (for each material and time period) and one-way analysis of variance followed by Tukey's post hoc (for finishing and polishing systems) at a significant level of P < 0.05. Results: Analysis of time period, irrespective of finishing and polishing system showed that Ra values were greater (P < 0.05) in delayed polishing in GIC > Z100 > Filtek P90 > Dyract AP, suggesting immediate polishing is better. Among the materials, Filtek P90 had the least Ra values indicating the smoothest surface among all materials, followed by Z100, Dyract AP, and GIC. Comparison of polishing and finishing systems irrespective of materials showed that Ra values were lower (P > 0.05) in diamond + Astropol combination whereas diamond + soflex had the greatest Ra values. Conclusion: It might be concluded that: (i) Filtek P90 showed least Ra values followed by < Z100 < Dyract < GIC; (ii) immediate (24 h) finishing/polishing of materials is better than delayed; and (iii) among all these polishing systems, diamond bur–Astropol and Astrobrush showed good surface finish.

L-4V (Ti 31). Materials and Methods: In the present in vitro study, cytotoxicity of Ti 12 and Ti 31 in human gingival fibroblast by MTT assay and the corrosion behavior by potentiodynamic polarization technique in aqueous solutions of 0.1 N NaCl, 0.1 N KCl, and artificial saliva with and without NaF were studied. Results: The independent t-test within materials and paired t-test with time interval showed higher cell viability for Ti 12 compared to Ti 31. Over a period, cell viability found to stabilize in both Ti 12 and Ti 31. The effects of ions of Ti and alloying elements aluminum and vanadium on the cell viability were found with incubation period of cells on samples to 72 h. The electrochemical behavior of Ti 12 and Ti 31 in different experimental solutions showed a general tendency for the immersion potential to shift steadily toward nobler values indicated formation of TiO2 and additional metal oxides. The multiphase alloy Ti-6Al-4V showed more surface pitting. Conclusion: The commercially pure Ti showed better cell viability compared to Ti 31. Less cell viability in Ti 31 is because of the presence of aluminum and vanadium. A significant decrease in cytotoxicity due to the formation of TiO2 over a period of time was observed both in Ti 12 and Ti 31. The electrochemical behavior of Ti 12 and Ti 31 in different experimental solutions showed a general tendency for the immersion potential to shift steadily toward nobler values indicated formation of TiO2 and additional metal oxides. Ti 31 alloy showed surface pitting because of its multiphase structure....

Objective: The aim is to study the effect of plasma working gas on composition, crystallinity, and microstructure of hydroxyapatite (HA) coated on Ti and Ti-6Al-4V metal substrates. Materials and Methods: Ti and Ti-6Al-4V metal substrates were coated with HA by plasma spray using four plasma gas atmospheres of argon, argon/hydrogen, nitrogen, and nitrogen/hydrogen. The degree of crystallinity, the phases present, and microstructure of HA coating were characterized using X-ray diffraction and scanning electron microscopy. Results: Variation in crystallinity and the microstructure of HA coating on plasma gas atmosphere was observed. Micro-cracks due to thermal stresses and shift in the 2θ angle of HA compared to feedstock was seen. Conclusion: Plasma gas atmosphere has a significant influence on composition, crystallinity, and micro-cracks of HA-coated dental implants.

Objective: The objective of this study was to compare the sorption and solubility of heat-cure and self-cure acrylic resins in different solutions. Materials and Methods: One heat-cure acrylic resin (Trevalon) and one self-cure acrylic resin (Rapid Repair) were studied. Five groups of square-shaped specimens (20 mm × 20 mm × 2 mm) were prepared for each acrylic resin and then immersed in five solutions: distilled water, artificial saliva, denture cleansing solution, distilled water, and denture cleaning solution for 12 h alternatively, artificial saliva and denture cleaning solution for 12 h alternatively at 37 ± 2°C, and tested sorption and solubility by weight gain/loss method, respectively, after 1, 6, and 11 weeks. The data were analyzed by one-way analysis of variance followed by post hoc Tukey's test. Results: Water sorption mean values varied from 17.5 ± 0.88 to 27.25 ± 1.04 μg/mm ³ for heat cure and from 12.75 ± 0.55 to 19.75 ± 1.04 μg/mm ³ for self-cure in the different solutions after different interval periods of 1, 6, and 11 weeks. These values were statistically significant (P< 0.001). Water solubility mean values varied from 0.25 ± 0.55 to 1.5 ± 0.55 μg/mm ³ for heat cure and from 1.5 ± 0.55 to 6.5 ± 0.55 μg/mm ³ for self-cure in the different solutions after different interval periods of 1, 6, and 11 weeks. These values were statistically not significant (P > 0.05). There was no linear correlation between sorption and solubility values. Overall, analysis of results showed the maximum sorption value in denture cleansing solution followed by alternative soaking in distilled water and artificial saliva. Least sorption was observed with artificial saliva followed by distilled water. Conclusion: Both heat-cure and self-cure acrylic resins showed varying water sorption and solubility. The results of both water sorption and solubility showed compliance with the International Standards Organization specification. No correlation was found between water sorption and solubility. Artificial saliva solution is a better storage medium than distilled water and denture cleansing solution for both heat-cure and self-cure acrylic resins.

Color stability throughout the functional lifetime of restorations is important for the durability of treatment and of cosmetic importance. The purpose of this study was to evaluate the discoloration properties of a silorane-based (Filtek P90) and methacrylate-based (Z100) composites upon exposure to different staining solutions that are used on day to day basis (turmeric, tea, coffee, cocoa, lime, yoghurt and distilled water) for different immersion periods (1, 7, 14 and 28 days). The colors of all specimens before and after storage in the solutions were measured by a reflectance spectrophotometer based on CIE Lab system and the color differences were calculated. Data were statistically analyzed by repeated measures of ANOVA and sidak post hoc test (for immersion period); 't' test (for each material) and one way ANOVA (for staining agents). All the staining agents showed significant difference in staining over time in both the materials. However, Z100 showed higher quantum of discoloration at all time periods at each staining agents (p<0.005). In conclusion, the silorane-based resin (Filtek P90) composites exhibited better color stability (less change in ΔE) after exposure to the staining solutions. Among the staining agents cocoa was found to be least staining followed by lime, yoghurt, coffee, tea whereas turmeric discolored the composites to the maximum. Highest discoloration was seen at day 28 in all staining agents. Cocoa and lime discolored to maximum at early stages but remained stable thereafter whereas tea, coffee and turmeric progressively discolored the composite over time.