This study focuses on the development of environmentally sustainable polypropylene (PP)-based composites with the potential for biodegradability by incorporating cellulose and the oligomeric siloxane ES-40. Targeting industrial applications such as fused deposition modeling (FDM) 3D printing, ES-40 was employed as a precursor for the in situ formation of silica particles via hydrolytic polycondensation (HPC). Two HPC approaches were investigated: a preliminary reaction in a mixture of cellulose, ethanol, and water, and a direct reaction within the molten PP matrix. The composites were thoroughly characterized using rotational rheometry, optical microscopy, differential scanning calorimetry, and dynamic mechanical analysis. Both methods resulted in composites with markedly reduced crystallinity and shrinkage compared to neat PP, with the lowest shrinkage observed in blends prepared directly in the extruder. The inclusion of cellulose not only enhances the environmental profile of these composites but also paves the way for the development of PP materials with improved biodegradability, highlighting the potential of this technique for fabricating more amorphous composites from crystalline or semi-crystalline polymers for enhancing the quality and dimensional stability of FDM-printed materials.

In this study, polymer composites based on a polypropylene (PP) matrix with the addition of cellulose and ES-40, used as a silica precursor, were investigated. These composites were designed to achieve enhanced biodegradability through the incorporation of bioavailable cellulose and to enable subsequent carbonization into carbon–silicon carbide systems. Rheological investigations revealed that the multicomponent mixtures exhibited pseudoplastic behavior over the shear rate range typical of injection molding, ensuring process stability without additional plasticization. Morphological analysis demonstrated that an optimal balance of PP, cellulose, and ES-40 promoted the formation of a three-dimensional network structure, leading to a significant increase in flexural modulus at the equal flexural strength despite some reduction in tensile strength. It was further shown that substituting fibrous cellulose with microcrystalline cellulose improved the composite homogeneity, thereby enhancing the density and mechanical properties, especially in systems with low polymer contents. Preliminary pyrolysis experiments indicated that these injection-molded composites can serve as precursors for fabricating bulk thermally stable products containing silicon carbide particles. The obtained results underscore the high potential of the developed materials for applications in conventional injection molding, the possibility of additive manufacturing, and processes requiring subsequent carbonization.

Betulin is a promising natural organic substance due to its antibacterial, fungicidal, and antitumor properties, as are their derivatives. The particle size of betulin can reach several tens of micrometers, and its thickness is several microns. There are various ways of processing betulin, but the most promising are solution methods (applying thin layers, impregnation, etc.). Application or impregnation of various materials is carried out using betulin; however, currently known solvents do not allow obtaining solutions with the necessary content of it. Since a number of direct solvents are already known for betulin, which provides only low-concentration solutions, the use of complex systems based on two solvents can become the optimal solution to the problem. The literature data show that the use of mixtures of solvents allows for the preparation of homogeneous solutions, for example, for natural polymers like cellulose, etc. This approach to obtaining solutions has become the basis for the processing of betulin. The use of a mixed solvent based on ethanol and DMSO for the preparation of betulin solutions has been proposed for the first time. The solubility of betulin in a mixture system with a ratio of components of 50 wt.% to 50 wt.% was studied, and a solubility curve was plotted. It is shown that the use of a two-component solvent makes it possible to transfer up to 10% of betulin into solution, which is almost twice as much as compared to already known solvents. The rheological properties of the obtained solutions have been studied. The viscosity of betulin solutions in a complex solvent depends on its content and temperature, so for 7% solutions at 70 °C, it is approximately 0.008 Pa*s. Applying betulin to the surface of the cardboard increases its hydrophobic properties and repellency.

Depending on the method of cellulose production, the proportion of alpha fraction in it can vary significantly. Paper pulp, unlike dissolving cellulose, has an alpha proportion of less than 90%. The presence of cellulose satellites in the system does not impede the formation of concentrated solutions of N-methylmorpholine-N-oxide (NMMO). In the current study, spinning solutions based on cellulose with a low alpha fraction (up to 90%) (pulp cellulose) are investigated. The morphological features and rheological behavior of such solutions are examined. It is suggested to roll the obtained solutions in order to obtain cellulose membranes. X-ray diffraction, IR spectroscopy, AFM and SEM were used to investigate the resulting structure and morphology of the obtained membranes. It is shown that the degree of crystallinity for the membranes varies based on the impurity content in the sample. The morphology of the films is characterized by a dense texture and the absence of vacuoles. The highest strength and elastic modulus were found for membranes made of bleached hardwood sulfate cellulose, 5.7 MPa and 6.4 GPa, respectively. The maximum values of the contact angle (48°) were found for films with a higher proportion of lignin. The presence of lignin in the membranes leads to an increase in rejection for the anionic dyes Orange II and Remazol Brilliant Blue R.

Cellulose and copolymers of acrylonitrile (PAN) are characterized by their chemical resistance to several conventional solvents. Therefore, these polymers are often used to obtain membranes for the recovery of such solvents. In this work, for the first time, composite membranes formed from highly concentrated mixed solutions based on cellulose and PAN are considered (the total content of polymers is 18 wt.%). For mixed solutions, the morphology and rheological behavior were evaluated. It is shown that the resulting solutions are two-phase, and their morphology depends on the components’ ratio and the system’s history. The non-monotonous change in the viscosity with the PAN content indicates a specific interaction of cellulose and PAN in N-methylmorpholine-N-oxide solutions. The rheological behavior of mixed solutions allows for their processing in conditions identical to those of cellulose solutions. The introduction of PAN into the cellulose matrix promotes a decrease in the structural order in the system, affecting the membranes’ transport properties. For composite membranes, it was found that with an increase in the content of the PAN phase, the retention of Remazol and Orange decreases, while the observed values are several times higher than those for cellulose membranes. The permeability of ethanol increases with increasing terpolymer content.

The present paper provides a compound having high acid corrosion protection properties based on amine-containing compounds. The amine used is the condensation of individual polyethylenepolyamines (PEPA), in particular diethylenetriamine (DETA) and isobutyric acid, followed by alkylation of the resulting compound by means of alkenylsuccinic acid. The structure of obtained amidoimide has been confirmed by IR spectrum. The physicochemical parameters of the compound were studied; amidoimide tests were carried out to assess the inhibitory ability by gravimetric and electrochemical methods.