The influence of different concentrations of salt-added polyethylene oxide (PEO) on the spinnability of chitosan (CS)/PEO + NaCl blends that could be used as a component part of filters for water treatment or nanofiber membranes as well as for medical applications was investigated in this study. The morphological properties of manufactured nanofibers were analyzed as well. It was determined that an increase of PEO concentration resulted mostly in thin and round nanofibers formed during electrospinning, but the manufacturing process became complex, because many wet fibers reached the collector while spinning. Also, it was noticed that the salt was not dissolved completely in the polymer solutions and some crystals were seen in the SEM images of manufactured fiber mats. However, the addition of salt resulted in lower viscosity and better conductivity of solution and fiber mats as well. The opposite effect was observed as the concentration of PEO was increased. The orientation of produced nanofibers as well as their diameter were analyzed with commercially available software. It was determined that the results obtained by software and microscopically are repeatable. The difference among the results of diameter calculated with software and taken by microscope varied from 0% to approximately 12%. The FTIR analyses indicated that alterations in polymer concentrations or the addition of salt did not induce any discernible changes in the chemical composition or nature of the materials under investigation. The sodium chloride present in the solutions enhanced electrical properties and increased conductivity values more than 50 times for PEO solutions and six times for CS/PEO blend solutions, compared to conductivity values of solutions without salt. To assess the thermal characteristics of the PEO/CS blend nanofibers, measurements using a differential scanning calorimeter (DSC) to determine melting (Tm) and crystallization (Tc) temperatures, as well as specific heat capacities were conducted. These parameters were derived from the analysis of endothermic and exothermic peaks observed in the DSC data. It showed that all produced nanofibers were semicrystalline.

This study presents the effect of non-thermal plasma modification on the changes of surface morphology, color characteristics and electrical conductivity of wool fabric dyed with intrinsically conductive polymer (ICP) poly (3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT: PSS). The wool fabric was treated with an aqueous dispersion of PEDOT: PSS, Clevios F ET, providing electrically conductive properties to textiles. The wool fabric, containing basic groups of amines (NH₂), was pre-activated with low-pressure plasma of non-polymer forming nitrogen (N₂) gas before exhaust dyeing with PEDOT: PSS at 90 °C was applied. This treatment imparted hydrophilicity, reduced felting, increased adhesion, improved dye ability and ensured that more PEDOT: PSS negatively charged sulfonate $\left(-{\mathrm{SO}}_3-\right)$ counter ions would be electrostatically bounded with the cationic protonated amine groups of the wool fiber. Initially, before (N₂) plasma treatment and after fabrics were evaluated according to the test method for aqueous liquid repellency, the surface morphology of the plasma-modified and -unmodified wool dyed fabric was observed with scanning electron microscopy (SEM). The functional groups introduced onto the surface after N₂ gas plasma treatment of wool fabric were characterized by X-ray photoelectron and FTIR-ATR spectroscopy. The results of color difference measurements show that N₂ gas plasma treatments provide more intense color on Clevios F ET dyed wool fabric and retain its electrical conductivity.

The most important functional purpose of knitted fabrics used for the protective non-flammable underwear worn in contact with the skin is to ensure wearing comfort by creating and maintaining a constant and pleasant microclimate at the skin surface independently from the environmental conditions. Protective non-flammable underwear may be used by firefighters or sportsmen, e.g., racing (Formula) sportsmen, where a risk of burn injuries (when the car is on fire after a car crash) is present. In order to investigate the flammability and thermal comfort properties of two-layer knitted fabrics, two groups of aramids and flame-retardant (FR) viscose fiber fabrics of different combined patterns and surface structures (porosity and flatness) were designed and manufactured for this research. Aramid fiber spun yarns (METAFINE.X.95^®) formed the inner layer (contacting with human skin) of fabrics and aramid/viscose FR fiber spun yarns (METALEN^®) formed the outer layer. For the evaluation of the functional characteristics of the manufactured fabrics, the flammability and thermoregulating properties, such as liquid moisture management, water vapor and air permeability, and thermal resistance were investigated. The results show that all tested fabrics are non-flammable, breathable, permeable to air, and can be assigned to moisture management fabrics. Their obtained overall moisture management capacity (OMMC) values are in the range 0.59–0.88. The knitted fabrics with an embossed porous surface to skin had a higher OMMC (0.75–0.88). The thermoregulation comfort properties were mostly influenced by the structure of the fabrics, while the burning behavior was found to be independent from the structure, and the non-flammability properties were imparted by the fiber content of the knits.

Socks are an important part of our clothing used in everyday activities. In order to ensure thermal comfort during wear in cool outdoor or indoor conditions, and for health improvement, socks must have effective thermoregulation properties. Chemical far-infrared (FIR) fibers with different bio-ceramic compounds incorporated into socks’ structures can provide an improved thermoregulation effect to the wearer of the socks. Fibers with silver and carbon additives incorporated in their structures can also affect the thermoregulation properties of socks. Moreover, these conductive additives avoid the unpleasant effect of static electricity of socks. The main parts of the different investigated structures of the socks were made in a plush pattern. The plush loops were formed by using functional Resistex^® Bioceramic, Shieldex^® and two modifications of Nega-Stat^® fiber yarns. The main thermal comfort (thermal efficiency, microclimate and heat exchange temperatures, thermal resistance, water vapor permeability) and electrostatic (surface and vertical resistances, shielding factor, half time decay of charge) properties of the socks were investigated. Based on the obtained results of the thermal comfort and electrostatic characteristics of the different investigated structures of socks, the optimal static dissipative (half-time decay <0.01 s, shielding factor—0.96) plush knitting structure with 55% Resistex^® Bioceramic and 31% bicomponent Nega-Stat^® P210 fibers yarns was selected. Comparing the control sample without FIR and the knitted structure with conductive additives, we can draw the conclusion that the heat retention capability of the selected socks was improved by 1.5 °C and the temperature of their created microclimate was improved by 2 °C.

The way to improve the properties (resistance to washing, delamination, and rubbing off) of the PEDOT:PSS coating applied on wool fabric without reduction of its electrical conductivity by introducing a commercially available combination of low formaldehyde content melamine resins into the printing paste is presented in this paper. Primarily, to improve the hydrophilicity and dyeability of wool fabric, the samples were modified using low-pressure nitrogen (N₂) gas plasma. Two commercially available PEDOT:PSS dispersions were used to treat wool fabric by the exhaust dyeing and screen printing methods, respectively. Spectrophotometric measurements of the color difference (ΔE*_ab) and visual evaluation of woolen fabric dyed and printed with PEDOT:PSS in different shades of the blue color showed that the sample modified with N₂ plasma obtained a more intense color compared to the unmodified one. SEM was used to examine the surface morphology and a cross-sectional view of wool fabric that had undergone various modifications. SEM image shows that the dye penetrates deeper into the wool fabric after plasma modification using dyeing and coating methods with a PEDOT:PSS polymer. In addition, with a Tubicoat fixing agent, HT coating looks more homogeneous and uniform. The chemical structure spectra of wool fabrics coated with PEDOT:PSS were investigated using FTIR-ATR characterization. The influence of melamine formaldehyde resins on the electrical properties, resistance to washing, and mechanical effects of PEDOT:PSS treated wool fabric was also evaluated. The resistivity measurement of the samples containing melamine-formaldehyde resins as an additive did not show a significant decrease in electrical conductivity, while the electrical conductivity was maintained after the washing and rubbing test as well. The best results of electrical conductivity for investigated wool fabrics before and after washing and mechanical action were determined for samples subjected to the combined processing–surface modification by low-pressure N₂ plasma, dyeing by exhaust with PEDOT:PSS, and coating by the screen-printing method of PEDOT:PSS and a 3 wt.% melamine formaldehyde resins mixture.

According to the global strategy of Green course, the production of sustainable textiles using different biodegradable fibres has immense potential for the development of sustainable products. Using one of the most sustainable biobased pure hemp and polylactide fibers yarns, four new biodegradable three-layer weft knitted fabrics with good thermal comfort properties were developed. The inner layer (worn next to the skin) and the middle layer of the knits were formed of hydrophobic polylactide fibers, the outer layer of different amounts (36–55%) of hydrophilic natural hemp fibers. Biodegradable polylactide fiber yarns were used as a replacement for conventional petroleum-based synthetic fibers. Natural hemp fibers are one of the most sustainable fibers derived directly from Cannabis sativa L. plants. The properties of the knitted fabrics were analysed and compared under thermoregulatory-moisture management, thermal resistance, air and water vapour permeability-properties. The results showed that all newly developed knits are ascribed to ‘moisture management’ fabrics according to the summary grading of all indices of moisture management parameters. In addition, it was found that the highest overall moisture management capability is related to the quantity of natural hemp fiber composition in different knitting structures. Based on the overall moisture management capacity (OMMC) index and thermal resistance values of developed knitted fabrics, the performance levels for these materials contacting the skin and intended for the intermediate layer were determined.