The fiber-reinforced composite stringer is commonly used in large civil aircraft wing structures. Under compression loads, it exhibits complex failure modes, with matrix cracking being one of the most common. The quantitative analysis of matrix failure is important and difficult. To address this issue, a multiscale method combining the generalized method of cells (GMC) and macroscopic FEM models is employed to quantitatively predict matrix damage and failure. The extent of matrix damage in the composite structure is represented by the number of failed matrix subcells within the repeating unit cells. The 3D Tsai–Hill failure criterion is established for the matrix phase, and the maximum stress failure criterion is applied to the fiber subcell. Upon meeting the criterion, the stiffnesses of the failed subcells are immediately reduced to a nominal value. In the current study, the ultimate loads, failure modes and load–displacement curves of composite stringers subjected to compressive load are obtained by the experiment approach and the proposed multiscale model. The experimental and simulation results show good agreement, and the multiscale analysis method successfully predicts the extent of matrix damage in the composite stringer under compressive load. The number of failed matrix subcells quantitatively evaluates the damage extent within a 2 × 2 GMC model. The findings reveal that matrix subcell failures primarily occur in the 45° and −45° plies of the middle part of the stringer composite.

Carbon fiber-reinforced composite stringers, which support aircraft skins in resisting tensile, compressive, and shear loads, are widely used in aircraft structures. These composite structures play a crucial role in enhancing the performance and safety of the structural integration of aircrafts. To better understand the load-bearing capacity of composite stringer structures, this study developed a novel model to study the complex failure and load transmission behavior of T800/3900S-2B fiber-reinforced composite skin-stringer structures under compressive loading. Compression strength tests were conducted on a composite stringer/skin structure, and a three-dimensional FEM was developed using Abaqus/Standard 2022. The model incorporated the modified 3D Hashin initiation criteria and Tserpes degradation law through a UMAT subroutine, which can effectively capture the in-plane ply failure and interlaminar damage. The results revealed a high degree of similarity between the load–displacement curves and failure modes (i.e., matrix compressive cracking, fiber compressive failure, and fiber–matrix shear-out failure) obtained from the simulations and those from the experiments. This study provides an efficient and accurate model to simulate the failure and load transfer of composite skin-stringer structures, offering significant advancements in understanding and predicting the behavior of these critical components.

The waviness defect, a common manufacturing flaw in composite structures, can significantly impact the mechanical performance. This study investigates the effects of wrinkles on the ultimate load and failure modes of two Carbon Fiber Reinforced Composite (CFRC) laminates through compressive experiments and simulation analyses. The laminates have stacking sequences of [0]_10S and [45/0/−45/90/45/0/−45/0/45/0]_S. Each laminate includes four different waviness ratios (the ratio of wrinkle amplitude to laminate thickness) of 0%, 10%, 20% and 30%. In the simulation, a novel multiaxial progressive damage model is implemented via the user material (UMAT) subroutine to predict the compressive failure behavior of wrinkled composite laminates. This multiscale analysis framework innovatively features a 7 × 7 generalized method of cells coupled with stress-based multiaxial Hashin failure criteria to accurately analyze the impact of wrinkle defects on structural performance and efficiently transfer macro-microscopic damage variables. When any microscopic subcell within the representative unit cell (RUC) satisfies a failure criterion, its stiffness matrix is reduced to a nominal value, and the corresponding failure modes are tracked through state variables. When more than 50% fiber subcells fail in the fiber direction or more than 50% matrix subcells fail in the transverse or thickness direction, it indicates that the RUC has experienced the corresponding failure modes, which are the tensile or compressive failure of fibers, matrix, or delamination in the three axial directions. This multiscale model accurately predicted the load–displacement curves and failure modes of wrinkled composites under compressive load, showing good agreement with experimental results. The analysis results indicate that wrinkle defects can reduce the ultimate load-carrying capacity and promote local buckling deformation at the wrinkled region, leading to changes in damage distribution and failure modes.