We investigated the short-term (4 weeks) color stability of light-cure and dual-cure resin cements. Sixty disk-shaped test specimens of adhesive resin cement (10 × 1 mm) were prepared. One feldspathic porcelain test specimen (12 × 14 × 0.8 mm) was prepared from a prefabricated ceramic block. The feldspathic sample was placed on the resin cement disk and all the measurements were performed without cementation. Specific color coordinate differences (ΔL, Δa, and Δb), and the total color differences (ΔE) were calculated after immersion in distilled water for different periods. Data were compared using one-way analysis of variance (ANOVA) (α = 0.05). The test results revealed that different chemical structures and curing modes affected the ΔE values (P < 0.05). The highest ΔE values were obtained for RelyX Unicem dual-cure cement (2.14 ± 0.40), and the lowest for NX3 light-cure cement (0.78 ± 0.34). Third generation adhesive resin cement free of tertiary amines and benzoyl peroxide showed relatively slight color change in both test groups (light-cure and dual-cure resin cement). (J Oral Sci 58, 157-161, 2016).

Background: This study evaluated the effect of ceramic primers containing 10-methacryloyloxydecyl phosphate (10-MDP) and γ-methacryloxypropyl trimethoxysilane (γ-MPTS) agents on the shear bond strength (SBS) of CAD/CAM ceramics with different chemical structures and resin cement. Methods: A total of 640 CAD/CAM ceramic specimens were obtained from Vita Mark II (VM), IPS E.max CAD (EM), Vita Suprinity (VS) and Vita Enamic (VE). The specimens were divided into two groups: etched with hydrofluoric acid (HF) and unetched. Each group was treated with a different ceramic primer (Clearfil Ceramic Primer Plus, G-Multi Primer and Monobond S), except for an untreated group (n = 10). After ceramic primers and resin cement were applied to each ceramic surface, half of the specimens were thermally aged at 10,000 cycles, 5–55 ± 1 °C, with a dwell time of 30 s. The SBS was tested with a universal testing machine at a 0.5 mm/min crosshead speed. Data were analysed by using statistical software (SPSS 20). Normal data distribution was checked with the Shapiro‒Wilk test. Three-way ANOVA was used to analyse the difference between the numeric data of the HF etched and thermally aged groups. A post hoc Tukey test was applied in the paired comparison of significant difference. The statistical significance level was accepted as p < 0.05. Results: The highest SBS values were obtained in the HF etched G-Multi primer applied nonaged EM group (28.3 ± 2.62 MPa), while the lowest values were obtained in the nonetched and thermally aged EM group that received no treatment (2.86 ± 0.04 Mpa). The SBS significantly increased in all specimens on which the ceramic primer was applied (p < 0.001). Thermal ageing had a significant negative effect on the SBS values in all groups (p < 0.001). Conclusion: The positive combined effects of the 10-MDP and γ-MPTS agents resulted in a significant increase in the bonding strength of the resin cement to the CAD/CAM ceramics. In addition, the increase in the amount of inorganic filler provided a favourable effect on durable adhesion.

The aim of this in vitro study was to evaluate the adhesion strength of two new fiber post systems (FiberSite™ Post and Cytec™ Blanco Post) cemented with two different adhesive resin cements (Panavia™ SA and Maxcem™ Elite). Root canals of sixty extracted human mandibular premolars were prepared using ProTaper Universal™ rotary files (Dentsply Sirona Endodontics, York, PA, USA). The root canals were irrigated with 5.25% sodium hypochlorite (NaOCl) during instrumentation. After root canal preparation, the canals were irrigated with 2 mL of 17% EDTA (1 min), followed by 2 mL of 5.25% (5 min) NaOCI, and 2 mL saline. The root canals were dried with paper points and divided randomly into two study groups (n = 30) according to the type of post system: Group 1, FiberSite™ Post (MegaDental, Partanna, Italy); and group 2, Cytec™ Blanco Post (Hahnenkratt, Königsbach-Stein, Germany), with one of the two adhesive resin cements: Subgroup A, Panavia™ SA Cement Plus Automix (Kuraray, Osaka, Japan); subgroup B, Maxcem™ Elite (Kerr, Orange, CA, USA). Following thermocycling, the adhesion strength was evaluated using the push-out adhesion (bond) strength test. Fractographic analysis was performed using stereomicroscope. The data were analyzed using two-way analysis of variance (p = 0.05). The adhesion strength values of both the posts were significantly higher when cemented with subgroup B (Maxcem™ Elite). The highest adhesion strength value was demonstrated by group 1B (FiberSite™ post cemented with Maxcem™ Elite cement). The type of post did not have a significant impact on the bond strength values for either cement material.

The aim of the present study was to determine the effect of different surface treatments on light transmission of aesthetic feldspathic ceramics used in CAD-CAM chairside restorations. Forty eight feldspatic ceramic test specimens were prepared from prefabricated CAD-CAM blocks by using a slow speed diamond saw. Test specimens were prepared and divided into 4 groups (n = 12). In the control group, no surface treatments were applied on the feldspathic ceramic surfaces. In the hydrofluoric acid group, the bonding surfaces of feldspathic ceramics were etched with 9.5 % hydrofluoric acid. In the sandblasting group the feldspathic ceramic surfaces were air-abraded with 30-μm alumium oxide (Al₂O₃) particles and Er:YAG laser was used to irradiate the ceramic surfaces. The incident light power given by the LED device and the transmitted light power through each ceramic sample was registered using a digital LED radiometer device. Each polymerization light had a light guide with 8-mm-diameter tips. Light transmission of feldspathic ceramic samples was determined by placing it on the radiometer and irradiating the specimen for 10 s at the highest setting for each light polymerization. All specimens were coated with gold using a sputter coater and examined under a field emission scanning electron microscope. Surface roughness measurement each group were evaluated with 3D optical surface and tactile profilometers. One-way ANOVA test results revealed that both surface conditioning method significantly affect the light transmittance (F:412.437; p < 0.001) and the surface roughness values (F:16.386; p < 0.001). Al₂O₃ and Er-YAG laser application reduced the light transmission significantly (p < 0.05). The laser and Al₂O₃ applications reduced the light transmission of 1.5 mm thickness feldspathic ceramic material below the value of 400 mW/cm² which is critical limit for safe polymerization.

Background: This in vitro study evaluated the effect of amine-free initiator system and polymerization type on long-term color change of amine-free light-cure and dual-cure resin cements. Methods: Sixty disk-shaped specimens (10 × 1 mm) were prepared from six different amine-free resin cements; NX3 Nexus light-cure (LC) and dual-cure (DC), Variolink Veneer (LC) and Variolink II (DC), Relyx Veneer (LC) and Rely X Ultimate (DC). A feldspathic porcelain specimen (12 × 14 × 0.8 mm) was obtained from a CAD/CAM block (Cerec Blocks; Sirona Dental Systems GmbH, Bensheim, Germany) for color testing. The feldspathic specimen was placed on the resin cement disk and all measurements were performed without cementation. A spectrophotometer was used for color measurements. Specimens were subjected to thermal aging (5 °C and 55 °C; 5000 and 20,000 cycles). Specific color coordinate differences (ΔL, Δa, and Δb) and the total color differences (ΔE₀₀) were calculated after immersion in distilled water for different periods. Normality of data distribution was tested by using the Kolmogorov–Smirnov test. Data were statistically in a model of repeated measures, using multivariate tests and Tukey’s multiple comparison tests at a significance level of p < 0.05. Results: ∆E₀₀ values of resin cements were influenced by cycle periods, significantly (p < 0.05). The highest ΔE00 values for long term were obtained in the NX3 (DC) (3.49 ± 0.87) and the lowest in the NX3 (LC) (1.41 ± 0.81). NX3 (LC), Variolink (DC), RELY X (LC) resin cements showed clinically acceptable color change after long-term aging (∆E₀₀ < 1.8). Conclusion: Light-cure resin cements should be preferred for long-term color stability of full ceramic restorations.