The ideal restoration of endodontically treated teeth (ETT) has been widely and controversially discussed in the literature. Prevention of healthy dental structure is essential to help mechanical stabilization of tooth-restoration integrity, increase the amount of suitable surfaces for adhesion and thus positively affect the long-term success. ETT are affected by a higher risk of biomechanical failure than vital teeth. With the development of adhesive systems, the need for post-core restorations is also reduced. Especially for restoration of excessively damaged ETT, endocrowns have been used as an alternative to the conventional post-core and fixed partial dentures. Compared to conventional methods, good aesthetics, better mechanical performance, and less cost and clinic time are the advantages of endocrowns.

Chronic regurgitation of gastric acids in patients with gastroesophageal reflux disease may cause dental erosion, which can lead in combination with attrition or bruxism to extensive loss of coronal tooth tissue.

This study aimed to compare the effect of acid etching, sandblasting, or silica coating on the micro-shear bond strength of dual-cured resin cements to computer-aided design and computer-aided manufacturing (CAD/CAM) glass ceramic materials. Feldspathic, lithium disilicate, and zirconia-reinforced CAD/CAM ceramics were divided into four groups: control group (C), no surface treatment; hydrofluoric (HF) group, 5% HF acid-etched; sandblasting (SB) group, abraded with 50 µm aluminum oxide (Al₂O₃) particles; silica-coated (CJ) group, abraded with 30 µm silica-modified Al₂O₃ particles. Roughness values were obtained by using a profilometer. The cements were condensed on the surface-treated specimens and a micro-shear bond test was conducted. The ceramic material (p < 0.001) and surface treatment type (p < 0.001) significantly affected the micro-shear bond strength values. HF acid etching can be recommended for the surface pretreatment of feldspathic, lithium disilicate, and zirconia-reinforced CAD/CAM ceramics. Better bond strengths can be obtained with HF acid etching than with sandblasting and silica coating.

The aim of the present study was to determine the effect of different surface treatments on light transmission of aesthetic feldspathic ceramics used in CAD-CAM chairside restorations. Forty eight feldspatic ceramic test specimens were prepared from prefabricated CAD-CAM blocks by using a slow speed diamond saw. Test specimens were prepared and divided into 4 groups (n = 12). In the control group, no surface treatments were applied on the feldspathic ceramic surfaces. In the hydrofluoric acid group, the bonding surfaces of feldspathic ceramics were etched with 9.5 % hydrofluoric acid. In the sandblasting group the feldspathic ceramic surfaces were air-abraded with 30-μm alumium oxide (Al₂O₃) particles and Er:YAG laser was used to irradiate the ceramic surfaces. The incident light power given by the LED device and the transmitted light power through each ceramic sample was registered using a digital LED radiometer device. Each polymerization light had a light guide with 8-mm-diameter tips. Light transmission of feldspathic ceramic samples was determined by placing it on the radiometer and irradiating the specimen for 10 s at the highest setting for each light polymerization. All specimens were coated with gold using a sputter coater and examined under a field emission scanning electron microscope. Surface roughness measurement each group were evaluated with 3D optical surface and tactile profilometers. One-way ANOVA test results revealed that both surface conditioning method significantly affect the light transmittance (F:412.437; p < 0.001) and the surface roughness values (F:16.386; p < 0.001). Al₂O₃ and Er-YAG laser application reduced the light transmission significantly (p < 0.05). The laser and Al₂O₃ applications reduced the light transmission of 1.5 mm thickness feldspathic ceramic material below the value of 400 mW/cm² which is critical limit for safe polymerization.

There is limited information on the effect of melatonin on the cytotoxicity of dental materials. The study evaluated the cytotoxic effects of heat- and auto-polymerized acrylic resin, particulate filler composite resin and a thermoplastic material on L-929 fibroblast cell viability at different incubation periods in artificial saliva without and with melatonin. Disk-shaped specimens were prepared according to each manufacturer’s instructions and divided into two groups to be stored either in artificial saliva (AS) and AS with melatonin (ASM). The measurements were performed using an MTT (3-(4,5)-dimethylthiazol-2-yl)-2,5-diphenyl tetrazoliumbromide) assay, in which the L-929 mouse fibroblasts cell culture was used. For the MTT test, extracts were examined at 1, 24, 72 h and 1 and 2 weeks. Data were analyzed using 3-way ANOVA and Tukey’s tests. No significant difference was found between groups AS and ASM (F = 0.796; p = 0.373). Incubation period significantly affected all materials tested (p < 0.001). Storing resin-based materials in artificial saliva with melatonin solution for 24 h may reduce cytotoxic effects on the fibroblast cells for which the highest effect was observed. Soaking resin prosthesis or orthodontic appliances in artificial saliva with melatonin at least 24 h before intraoral use or rinsing medium containing melatonin may be recommended for decreasing the cytotoxicity of dental resin materials.