Ti and its alloys have received wide attention in marine engineering. However, the limited anti-biofouling capability may hinder their wide application. In the present work, micro-arc oxidation (MAO) with and without the introduction of ultrasonic vibration (UV) has been conducted on metallic Ti substrate in an aqueous solution containing Na₂Cu-EDTA to produce a Cu-modified TiO₂ coating. Microstructural characterization reveals that the introduction of UV increased the thickness of the coating (ranging from ~13.5 μm to ~26.2 μm) compared to the coating (ranging from ~8.1 μm to ~12.8 μm) without UV. A relatively higher Cu content (~2.13 wt.%) of the coating with UV relative to the coating (~1.39 wt.%) without UV indicates that UV enhances the incorporation of Cu into TiO₂. Further, both electrochemical properties and the response to sulfate-reducing bacteria (SRB) were evaluated, revealing that UV introduction endows Cu-modified TiO₂ coating with enhanced corrosion resistance and antifouling capability. The present results suggest that ultrasound-auxiliary micro-arc oxidation (UMAO) obviously enhances the surface performance of Ti alloys for promising applications in marine engineering.

As a promising material for petroleum industrial applications, titanium (Ti) and its alloys receive wide attention due to their outstanding physicochemical properties. However, the harsh industrial environment requires an antifouling surface with a desired corrosion resistance for Ti and its alloys. In order to achieve the desired antifouling properties, micro-arc oxidation (MAO) was used to prepare a Cu-doped TiO₂ coating. The microstructure of the Cu-doped TiO₂ coating was investigated by TF-XRD, SEM, and other characterization techniques, and its antifouling and anticorrosion properties were also tested. The results show the effects of the incorporation of Cu (~1.73 wt.%) into TiO₂ to form a Cu-doped TiO₂, namely, a Ti–Cu coating. The porosity (~4.8%) and average pore size (~0.42 μm) of the Ti–Cu coating are smaller than the porosity (~5.6%) and average pore size (~0.66 μm) of Ti–blank coating. In addition, there is a significant reduction in the amount of SRB adhesion on the Ti–Cu coating compared to the Ti–blank coating under the same conditions, while there is little difference in corrosion resistance between the two coatings. There, the addition of copper helps to improve the fouling resistance of TiO₂ coatings without compromising their corrosion resistance. Our work provides a practical method to improve the antifouling function of metallic Ti substrates, which could promote the application of Ti in the petroleum industry.