A novel carboxymethyl cellulose (CMC)-supported graphene oxide aerogel (CGOA) was fabricated from a cost-effective and abundant bituminous coal by a mild hydrothermal process and freeze-drying treatment. Such an aerogel has cross-linked graphene oxide layers supported by CMC, and therefore, displays high mechanical strength while having ultra-low density (8.257 mg·cm⁻³). The CGOA has a 3D interconnected porous structure, beneficial graphene framework defects and abundant oxygen-containing functional groups, which offer favorable diffusion channels and effective adsorption sites for the transport and adsorption of dye molecules. The adsorption performance of rhodamine B by an optimized CGOA shows a maximum monolayer adsorption capacity of 312.50 mg·g⁻¹, as determined by Langmuir isotherm parameters. This CGOA exhibited a better adsorption efficiency (99.99%) in alkaline solution, and satisfactory stability (90.60%) after three cycles. In addition, adsorption experiments on various dyes have revealed that CGOA have better adsorption capacities for cationic dyes than anionic dyes.

Plasma electrolytic oxidation (PEO) is normally carried out under conditions with electrolyte cooling. However, the effect of the temperature of the electrolytes on the PEO behavior and properties of the resulting coatings is seldom investigated. In this study, PEO of pure Al was carried out in a dilute aluminate electrolyte with the electrolyte temperature being controlled under low (~10–30 °C), medium (~40–50 °C) and high (~70–80 °C) temperature ranges, respectively. The morphology, microstructure, composition and phase component of the coatings fabricated under the different temperature ranges were analyzed by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The corrosion resistances of the coatings were evaluated by electrochemical methods. The hardness of the coatings and substrate following the PEO treatment in the different electrolyte temperature ranges were also tested. It was found that a higher electrolyte temperature resulted in a higher growth rate and rougher coatings. Moreover, the α-Al₂O₃ content was reduced as the electrolyte temperature increased. The highest corrosion resistance was registered for the coating obtained under the lowest temperature range, whereas the corrosion resistance of the coating obtained under the highest temperature range was the worst. The higher growth rate under high electrolyte temperatures was associated with the increased kinetics of the PEO reactions. However, the temperature of the electrolyte should be controlled under a suitable range to ensure reasonable coating properties.

Ti and its alloys have received wide attention in marine engineering. However, the limited anti-biofouling capability may hinder their wide application. In the present work, micro-arc oxidation (MAO) with and without the introduction of ultrasonic vibration (UV) has been conducted on metallic Ti substrate in an aqueous solution containing Na₂Cu-EDTA to produce a Cu-modified TiO₂ coating. Microstructural characterization reveals that the introduction of UV increased the thickness of the coating (ranging from ~13.5 μm to ~26.2 μm) compared to the coating (ranging from ~8.1 μm to ~12.8 μm) without UV. A relatively higher Cu content (~2.13 wt.%) of the coating with UV relative to the coating (~1.39 wt.%) without UV indicates that UV enhances the incorporation of Cu into TiO₂. Further, both electrochemical properties and the response to sulfate-reducing bacteria (SRB) were evaluated, revealing that UV introduction endows Cu-modified TiO₂ coating with enhanced corrosion resistance and antifouling capability. The present results suggest that ultrasound-auxiliary micro-arc oxidation (UMAO) obviously enhances the surface performance of Ti alloys for promising applications in marine engineering.

The limited antifouling capability of Ti-based components could jeopardize their applications in petroleum engineering. In this work, a Cu-enriched TiO₂ coating has been fabricated using an ultrasound-auxiliary micro-arc oxidation (UMAO) method. The Cu enrichment of TiO₂ affects its morphology, phase component and chemical configuration, leading to the slightly enhanced corrosion resistance of the Cu-enriched TiO₂ coating relative to that free of Cu. Finally, the antifouling capability against sulphate-reducing bacteria (SRB) is significantly improved by preventing the formation of biofilm after the Cu enrichment of TiO₂, which potentially widens its application in petroleum engineering.