In this work, graphene nanoplatelets (GNPs) were dispersed uniformly in aqueous solution using methylcellulose (MC) as a dispersing agent via ultrasonic processing. Homogenous GNP suspensions were incorporated into the cement matrix to investigate the effect of GNPs on the mechanical behavior of cement paste. The optimum concentration ratio of GNPs to MC was confirmed as 1:7 by ultraviolet visible spectroscopy (UV-Vis), and the optical microscope and transmission electron microscopy (TEM) images displayed remarkable dispersing performance. The GNP–cement composite exhibited better mechanical properties with the help of surface-modified GNPs. The flexural strength of cement paste increased up to 15%–24% with 0.05 wt % GNPs (by weight of cement). Meanwhile, the compressive strength of the GNP–cement composite increased up to 3%–8%. The X-ray diffraction (XRD) and thermal analysis (TG/DTG) demonstrated that the GNPs could accelerate the degree of hydration and increase the amount of hydration products, especially at an early age. Meanwhile, the lower porosity and finer pore size distribution of GNP–cement composite were detected by mercury intrusion porosimetry (MIP). In addition, scanning electron microscope (SEM) analysis showed the introduction of GNPs could impede the development of cracks and preserve the completeness of the matrix through the plicate morphology and tortuous behavior of GNPs.

Magnesium silicate hydrate (MSH) gel was formed by reacting magnesium oxide (MgO) with silica fume (SF) in distilled water. The MSH was prepared using a MgO/SF molar ratio of 1.0 (40:60 weight ratio). Samples were analyzed during hydration process up to 300 days at room temperature. The MSH characterization has been carried out using a range of analytical techniques. Quantitative analysis was achieved using thermogravimetric analysis (TG/DTG) with a de-convolution technology. The structure of MSH gel was characterized using solid state nuclear magnetic resonance (²⁹Si NMR) and Fourier transform infrared (FT-IR) spectroscopy. Transmission electron microscopy (TEM) was used to investigate MSH microstructure. Compared with natural magnesium silicate hydrate minerals, the structure of MSH gel is highly disordered and generates on the surface of particles, producing a shell structure with cavity. The molecular structure of MSH phase is layered. The results also show that the extent of polymerization of MSH gel is related to the solution pH during hydration.