Literature addressing the mechanical properties of kinesiology tape is quite scarce. There are no studies which focus on the mechanical characteristics of kinesiology tape, its mechanical properties, nor its adherence following the ISO international standard test methods for tape elongation. This study quantified the mechanical characteristics of 380 samples of kinesiology tape from 19 different brands and in 4 different colors using a dynamometer. Mechanical testing was controlled by UNE EN ISO 13934-1. Significant differences were found between tape brands in terms of grammage, maximum force tenacity, work, pre-elongation and percentage elongation (P < .001). Regarding kinesiology tape color, statistically significant differences were found between tape brands in terms of grammage, maximum force and tenacity (P < .001), work and pre-elongation (P < .05). When adherence was studied, statistically significant differences were found between tape brands in terms of maximum force and work (P < .001). The different kinesiology tapes presented different behaviors with regard to rupture and removal when applied to skin in dry state, wet state and after being submerged in artificial acidic sweat solution. Therefore, different kinesiology tape brands will produce different levels of strain even though the same elongation is used. Depending on the characteristics (body dimensions) and properties (skin elongation) of each subject in the sample, bandages with different elongations must be applied to achieve the same strain in all of the tapes and therefore produce the same effect. The absence of these data at this time limits the reliability of previous clinical studies, makes comparing their findings impossible and presents new challenges for research in this field.

Three-dimensional printing technology is being increasingly applied in a multitude of sectors. However, this technology is not generally applied in the same way as in other sectors, possibly due to the difficulty of adhesion between the polymer and the textile substrate. A textile garment is subjected to wear and tear during its lifetime, and a low tensile strength or rubbing resistance hinders a garment in most of the applications of this type of research. This study examined the influence of the characteristics of the cotton textile substrate, such as the weave structure and the yarn thickness, on the tensile strength of a 3D-printed element with conductive filament. Starting from the fabric with the highest tensile strength, different prints were made using this technology to incorporate conductive and heating properties into the fabric. The results validate the possibility of providing new properties to the textile by means of this technology; however, the correct selection of the textile used as a base substrate is important.

Turmeric has been widely studied as a color indicator for pH variations due to its halochromic properties. It has been tested in solution or included in some polymeric matrices. Some studies have demonstrated that its change in color is due to the tautomeric species of curcumin, and this property can be observed even if turmeric is assimilated in a film or nanofiber. Chitosan/polyethylene oxide (PEO) polymers have been tested in previous studies. Polyvinyl alcohol (PVA) nanofibers are used as potential carriers of drugs once they are insolubilized. The aim of this work is to cross-link PVA with citric acid (CA) to insolubilize the nanofibers and determine the effect on turmeric’s halochromic properties. The nanofibers were treated with a sodium hydroxide (NaOH) solution, and a chromatic study was undertaken to determine color change. The change in color was assessed by eye (subjective) and by spectroscopy (objective). The nanofibers were characterized, in addition to the colorimetric study, by Fourier transform infrared (FTIR) spectroscopy and scanning electron microscopy (SEM) as well. The results demonstrate how thermal treatment induces cross-linking between the nanofibers, allowing them to keep their shape once the NaOH solution is applied to them. The opposite effect (solubilization) can be observed for non-cross-linked (NCL) samples. Although the final color varied, the cross-linked (CL) nanofibers’ halochromic behavior was maintained. It was demonstrated that during cross-linking, ester groups are formed from the free carboxyl group in the cross-linked CA and the ketones present in the curcumin under acid conditions. So, CA acts as an acid catalyst to bond turmeric to the cross-linked PVA nanofibers.

Natural dyes, obtained from plants, insects/animals, and minerals, are renewable and sustainable bioresource products with minimum environmental impact. However, there are still many issues to solve related to natural dyes; consequently, synthetic dyes are still wildly used. Natural dyes have a low affinity towards the substrate cotton, so a solution had to be found: mordants. Mordants can also be harmful to the environment, which is why bio-mordants are used. The mordant used in this paper is chitosan. Cotton is pre-mordanted using the pad dyeing method. By using the exhaustion method, the fabric was coloured with red Camellia sinensis (tea) extracts. The colour, absorption of polyphenols and tannins, and ultraviolet protection (UPF) were tested. A comparison study was carried out between the cotton fabric and the cotton padded with chitosan at two different concentrations. The results are impressive. Cotton pre-mordanted with chitosan can absorb more polyphenols and tannins than cotton itself, and the colour fastness and UPF, once the fabric is laundered, demonstrate there is some kind of bonding between the fibre, quitosan, and active compounds from tea. The UPF was also doubled by using chitosan and the reddish colour obtained by Camellia sinensis extracts were darker on the cotton fabric. The increase in UPF protection on mordanted fabrics is higher than the gap obtained by colour difference, which means there are active compounds that do not confer colour, but enhance UPF protection.

The work is framed within Printed Electronics, an emerging technology for the manufacture of electronic products. Among the different printing methods, the roll-to-roll flexography technique is used because it allows continuous manufacturing and high productivity at low cost. Nevertheless, the incorporation of the flexography printing technique in the textile field is still very recent due to technical barriers such as the porosity of the surface, the durability and the ability to withstand washing. By using the flexography printing technique and conductive inks, different printings were performed onto woven fabrics. Specifically, the study is focused on investigating the influence of the structure of the woven fabric with different weave construction, interlacing coefficient, yarn number and fabric density on the conductivity of the printing. In the same way, the influence of the weft composition was studied by a comparison of different materials (cotton, polyester, and wool). Optical, SEM, color fastness to wash, color measurement using reflection spectrophotometer and multi-meter analyses concluded that woven fabrics have a lower conductivity due to the ink expansion through the inner part of the textile. Regarding weft composition, cotton performs worse due to the moisture absorption capacity of cellulosic fiber. A solution for improving conductivity on printed electronic textiles would be pre-treatment of the surface substrates by applying different chemical compounds that increase the adhesion of the ink, avoiding its absorption.

Environmental conditions, job tasks, and clothing choices influence the thermal comfort of workers. While it is impossible to control outdoor environmental conditions, selecting appropriate clothing for workers is feasible. Personal protective equipment often does not completely protect outdoor workers at high air temperatures. In such cases, cooling garments can help dissipate body heat and be worn with standard work clothes or uniforms. Currently, there is a lack of consensus in the literature regarding the characterisation of this type of garment. This study employed an innovative laboratory testing method that integrates a thermal manikin with a computer simulation program to assess the thermal sensation and comfort of various garment types in different activities and environmental conditions. This advanced approach enables a thorough evaluation of cooling garments that considers their physical properties and interactions with the human body. The findings confirm the efficacy of the tested cooling mechanisms, highlighting that the air circulation mechanism was the only one that consistently maintained user comfort across low, medium, and high metabolic activity levels. This study aims to assist users in selecting the most suitable cooling mechanism for the market based on the type of work or activity being performed.