The main problem with ceramics used in cutting tools is related to the unpredictable failures caused by the brittle fracturing of ceramic inserts, which is critical for the intermittent milling of cyclic loading. A 125-mm-diameter eight-toothed end mill, with a mechanical fastening of ceramic inserts, was used as a cutting tool for milling hardened steel (102Cr6). For the experiments, square inserts of the Al₂O₃ + SiC ceramic were used and compared with the samples made of Al₂O₃ + TiC to confirm the obtained results. The samples were coated with diamond-like coating (DLC), TiZrN, and TiCrAlN coatings, and their bending strength and adhesion were investigated. Investigations into the friction coefficient of the samples and operational tests were also carried out. The effect of smoothing the microroughness and surface defects in comparison with uncoated inserts, which are characteristic of the abrasive processing of ceramics, was investigated and analyzed. The process developed by the authors of the coating process allows for the cleaning and activation of the surface of ceramic inserts using high-energy gas atoms. The impact of these particles on the cutting edge of the insert ensures its sharpening and reduces the radius of curvature of its cutting edges.

Problems with the laser additive manufacturing of metal parts related to its low efficiency are known to hamper its development and application. The method of selective laser melting of metallic powders can be improved by the installation of an additional laser beam modulator. This allows one to control the power density distribution optically in the laser beam, which can influence the character of heat and mass transfer in a molten pool during processing. The modulator contributes alternative modes of laser beam: Gaussian, flat top (top hat), and donut (bagel). The study of its influence includes a mathematical description and theoretical characterization of the modes, high-speed video monitoring and optical diagnostics, characterization of processing and the physical phenomena of selective laser melting, geometric characterization of single tracks, optical microscopy, and a discussion of the obtained dependences of the main selective laser melting (SLM) parameters and the field of its optimization. The single tracks were produced using the advanced technique of porosity lowering. The parameters of the obtained samples are presented in the form of 3D graphs. The further outlook and advanced applications are discussed.

Deposition of thin metallic films on dielectric substrates using a source of metal atom flow combined with a flow fast argon atoms has been investigated and the investigation results are presented. The fast atoms are produced due to charge-exchange collisions in a vacuum chamber of argon ions, which are accelerated by potential difference between the hollow-cathode glow-discharge plasma and an emissive grid and enter the chamber through the grid. The metal atoms produced due to ion sputtering of a metallic foil placed on the inner surface of the hollow cathode enter the chamber through the same grid. Substrate pretreatment and pulse-periodic bombardment of the growing film by ∼1-keV argon atoms both ensure adhesion of copper to glass up to 2 × 10⁷ Pa. The use of a hollow substrate holder, whose inner surface is also covered with the same foil, makes it possible to exclude losses of the depositing metal and allows recommendation of the equipment for beam-assisted deposition of precious metal films.

Experimental study of fast neutral atom and molecule beam sources with rectangular and circular cross-section of the beam up to 0.8 m2is carried out and the study results are presented. The fast...

Experimental study of a fast argon atom beam source is carried out and the study results are presented. The source comprises a 90-mm deep and 210-mm in diameter hollow cathode as well as a flat...