High-entropy alloys are a new generation of materials that have attracted the interest of numerous scientists because of their unusual properties. It seems interesting to use these alloys in biomedical applications. However, for this purpose, the basic condition of corrosion resistance must be fulfilled. In this article, selected corrosion properties of self-composed high-entropy alloys are investigated and compared with conventional biomedical alloys, that is titanium alloys and stainless steels. Corrosive parameters were determined using the potentiodynamic method. X-ray diffraction studies were performed to characterize the crystal structures. Microstructures of the prepared materials were examined using a scanning electron microscope, and surface hardness was measured by the Vickers method. The results show that investigated high-entropy alloys are characterized by simple structures. Three out of four tested high-entropy alloys had better corrosion properties than conventional implant alloys used in medicine. The Al_0.7CoCrFeNi alloy was characterized by a corrosion potential of −224 mV and a corrosion current density of 0.9 μA/cm²; CoCrFeNiCu by −210 mV and 1.1 μA/cm²; TiAlFeCoNi by −435 mV and 4.6 μA/cm²; and Mn_0.5TiCuAlCr by −253 mV and 1.3 μA/cm², respectively. Therefore, the proposed high-entropy alloys can be considered as potential materials for biomedical applications, but this requires more studies to confirm their biocompatibility.

The paper presents the results of in vitro studies of fretting and fretting corrosion processes of Ti6Al4V implant alloy in the environment of natural saliva and self-made mucin-based artificial saliva solutions. The study was performed on a specially designed fretting pin-on-disc tester, which was combined with a set used for electrochemical research. The open circuit potential measurements and potentiodynamic method were used for corrosion tests. The worn surfaces were subjected to microscopic observations and an evaluation of wear. Results were interpreted using the dissipated energy and third-body approaches. The X-ray diffraction analysis showed that titanium oxides constitute over 80% of the friction products. Special attention was paid to the role of saliva and its substitutes, which in certain cases can lead to the intensification of fretting wear. On the basis of the received results, a new phenomenological model of fretting corrosion processes was proposed. This model involves the formation of an abrasive paste that is a combination of metal oxides and the organic components of saliva.