The properties of unconventional blends of crystallizable and thermo-cross-linkable polychloroprene (CR) with polybutadiene (BR) were investigated in this study. The compositions were prepared using the method of reactive processing and cross-linking in the presence of nano-sized zinc (nZn). The purpose of the research was to assess the efficacy of nano-zinc as a curing agent of polychloroprene and polybutadiene (CR/BR) composites and to obtain rubber goods characterized by increased flame resistance. The blends were filled with nano-silica (aerosil) and fillers of natural origin (chalcedonite or silitin). The cross-linking process was characterized by determining the kinetics curves, the equilibrium swelling, and the Mooney–Rivlin elasticity constants. The morphology of the vulcanizate surface was specified by scanning electron microscopy (SEM). The dynamic and mechanical properties, flammability, and toxicity of gaseous substances involved in thermal decomposition were determined. Mass changes and thermal effects were studied using simultaneous thermal analysis (STA). It was confirmed that nano-zinc is an efficient curing agent for the polychloroprene and polybutadiene compositions, with a satisfactory degree of cross-linking (α_c = 0.10, CRI = 4.11 min⁻¹), good mechanical strength (TS_b = 5 MPa), satisfactory tear resistance (T_s = 2.9 N/mm), and very high flame resistance (OI = 30%, HRR_max = 283 kW/m²). Filled products could be used as non-combustible materials, confirming the low fire hazard (1/t_flashover = 3.5–6.4 kW/m²∙s). The most effective filler of the tested composites was nano-sized silica.

Snow cover constitutes a medium that can be used as a way of assessing air pollution. The chemical composition of snow layers from the same snowfall event reflects the composition of atmospheric aerosols and dry precipitates, depending on the properties of the adsorbing surface and prevailing weather conditions. Analyzing snow samples provides reliable insights into anthropogenic pollution accumulated in soil and groundwater of different land use type areas, as well as allows the evaluation of the degree and sources of environmental pollution. The aim of the research was to determine the distribution of polycyclic aromatic hydrocarbons in various sites of Zawoja village and identify their possible sources and factors influencing their differentiation. A total of 15 surface snow samples of the same thickness and snowfall origin were collected from different locations in the village in the winter of 2024. The samples were pre-concentrated by solid phase extraction and analyzed by gas chromatography—tandem mass spectrometry. The sampling set was invented, and the extraction procedure and analysis parameters were optimized. A spatial distribution map of PAHs was created. The contamination of ∑16PAHs varied from 710 to 2310 ng/L in melted snow with the highest concentrations detected in Zawoja Markowa by the border of the Babia Góra National Park, which is interpreted mainly as a result of the topographical setting. Medium molecular weight PAHs were the dominant fraction, which, combined with specific PAH ratios, indicate the combustion of biomass and coal as the main source of contamination.

This study investigates the combustion behavior of polycarbonate (PC) and polycarbonate–carbon nanotube (PC-CNT) composites in fluidized bed reactors. The primary objective was to evaluate the influence of carbon nanotubes (CNTs) on the thermal stability and combustion efficiency of PC. Simultaneous thermogravimetric and differential scanning calorimetry (TG-DSC) analyses were conducted under both air and oxygen-deficient conditions to assess decomposition temperature ranges and energetic effects. Additionally, a simultaneous TG-DSC analysis of the samples’ decomposition in a 2 vol.% O₂ atmosphere was carried out to simulate adverse combustion conditions that may occur in some combustion technologies, such as the accumulation of degraded material on the grate. Combustion experiments were performed in inert and catalytic fluidized beds, the latter incorporating Fe₂O₃-coated cenospheres to enhance catalytic activity. The results demonstrated that the presence of CNTs alters the combustion mechanism, reducing energy release in the initial degradation stage while significantly intensifying exothermic effects in subsequent stages. Under oxygen-deficient conditions, both PC and PC-CNT required higher temperatures and extended times for complete decomposition. The catalytic fluidized bed markedly improved combustion efficiency at lower temperatures, achieving up to 90% conversion at 550 °C, compared to inert beds that required 750 °C for similar efficiency.