Additively-manufactured Ti-6Al-4V (Ti64) exhibits high strength but in some cases inferior elongation to those of conventionally manufactured materials. Post-processing of additively manufactured Ti64 components is investigated to modify the mechanical properties for specific applications while still utilizing the benefits of the additive manufacturing process. The mechanical properties and fatigue resistance of Ti64 samples made by electron beam melting were tested in the as-built state. Several heat treatments (up to 1000 °C) were performed to study their effect on the microstructure and mechanical properties. Phase content during heating was tested with high reliability by neutron diffraction at Los Alamos National Laboratory. Two different hot isostatic pressings (HIP) cycles were tested, one at low temperature (780 °C), the other is at the standard temperature (920 °C). The results show that lowering the HIP holding temperature retains the fine microstructure (~1% β phase) and the 0.2% proof stress of the as-built samples (1038 MPa), but gives rise to higher elongation (~14%) and better fatigue life. The material subjected to a higher HIP temperature had a coarser microstructure, more residual β phase (~2% difference), displayed slightly lower Vickers hardness (~15 HV_10N), 0.2% proof stress (~60 MPa) and ultimate stresses (~40 MPa) than the material HIP’ed at 780 °C, but had superior elongation (~6%) and fatigue resistance. Heat treatment at 1000 °C entirely altered the microstructure (~7% β phase), yield elongation of 13.7% but decrease the 0.2% proof-stress to 927 MPa. The results of the HIP at 780 °C imply it would be beneficial to lower the standard ASTM HIP temperature for Ti6Al4V additively manufactured by electron beam melting.

Using an electron beam melting (EBM) printing machine (Arcam A2X, Sweden), a matrix of 225 samples (15 rows and 15 columns) of Ti-6Al-4V was produced. The density of the specimens across the tray in the as-built condition was approximately 99.9% of the theoretical density of the alloy, ρ_T. Tensile strength, tensile elongation, and fatigue life were studied for the as-built samples. Location dependency of the mechanical properties along the build area was observed. Hot isostatic pressing (HIP) slightly increased the density to 99.99% of ρ_T but drastically improved the fatigue endurance and tensile elongation, probably due to the reduction in the size and the distribution of flaws. The microstructure of the as-built samples contained various defects (e.g., lack of fusion, porosity) that were not observed in the HIP-ed samples. HIP also reduced some of the location related variation in the mechanical properties values, observed in the as-printed condition.

Knowledge of the appearance of texture components and fibres in pole figures, in inverse pole figures and in Euler space is fundamental for texture analysis. For cubic crystal systems, such as steels, an extensive literature exists and, for example, the book by Matthies, Vinel & Helming [Standard Distributions in Texture Analysis: Maps for the Case of Cubic Orthorhomic Symmetry, (1987), Akademie-Verlag Berlin] provides an atlas to identify texture components. For lower crystal symmetries, however, equivalent comprehensive overviews that can serve as guidance for the interpretation of experimental textures do not exist. This paper closes this gap by providing a set of scripts for theMTEXpackage [Bachmann, Hielscher & Schaeben (2010).Solid State Phenom.160, 63–68] that allow the texture practitioner to compile such an atlas for a given material system, thus aiding orientation distribution function analysis also for non-cubic systems.

Among various off-equilibrium microstructures of additively manufactured Ti-6Al-4V alloy, electron beam powder bed fusion, in which three dimensional metallic objects are fabricated by melting the ingredient powder materials layer by layer on a pre-heated bed, results in a specimen that is nearly free of the preferred orientation of the $\alpha$-Ti phase as well as a low beta phase fraction of ~1 wt%. However, when further heat treatment of up to 1050 °C was applied to the material in our previous study, a strong texture aligning the hexagonal basal plane of $\alpha$ phase with the build direction and about 6% $\beta$ phase appeared at room temperature. In this study, to understand the mechanism of this heat treatment, the grain level microstructure of the additively manufactured Ti-6Al-4V was investigated using in situ high temperature EBSD up to 1000 °C, which allows the tracking of individual grains during a heat cycle. As a result, we found a random texture originating from the fine grains in the initial material and observed a significant suppression of $\alpha$ phase nucleation in the slow cooling after heating to 950 °C within the $\alpha$ and $\beta$ dual phase regime but close to the the $\beta$-transus temperature at ~980 °C, which led to a coarse microstructure. Furthermore, the texture resulting from phase transformation of the additively manufactured Ti-6Al-4V assuming nucleation at the grain boundaries was modeled, using the double Burgers orientation relationship for the first time. The model successfully reproduced the measured texture, suggesting that the texture enhancement of the $\alpha$ phase by the additional heat treatment derives also from the variant selection during the phase transformation and nucleation on grain boundaries.

Additive manufacturing is a novel and breakthrough technology by which parts can be manufactured for various purposes and services. As in any production process, the desired properties of additively manufactured components, particularly in electron beam melting processes, ultimately depend on the manufacturing process parameters. Process parameters should be designed accordingly to manufacture parts with specific and desired characteristics. This study focuses on examining the effect of process parameters, such as beam current and velocity, focus offset, and line offset, at three different values each, on the properties of Ti-6Al-4V alloy. The study on the effect of the process parameters on the as-built material’s performance was performed using the Taguchi approach using an L₉ (3⁴) orthogonal array. The properties of printed parts (density, surface roughness, elastic moduli, hardness, tensile characteristics, fractography, and microstructure) were tested. A wide range of properties was obtained and analyzed; namely, porosity varied from 8% to almost fully dense materials with density higher than 99.9% and a range of yield and ultimate tensile strength values and brittle samples with less than 1% elongation to ductile samples with an elongation greater than 16%. The overall performance of printed parts was determined based on an evaluation criterion. Several parameter combinations were found and yielded the fabrication of parts with high density and relatively fine microstructure. The comparison of the best parameter combinations determined in this study and the parameters recommended by the machine manufacturer showed that improved results were obtained, and even when using the optimal parameters, they can be improved even more. This result highlights the ability of the proposed DOE method to further develop existing results and even for development of manufacturing parameters for new materials.

The effects of the secondary processes of Hot Isostatic Pressing (HIP) at 920 °C and Heat Treatment (HT) at 1000 °C of Electron Beam-Melted (EBM) Ti–6Al–4V alloy on the microstructure and hydrogen embrittlement (HE) after electrochemical hydrogen charging (EC) were investigated. Comprehensive characterization, including microstructural analysis, X-ray diffraction (XRD), thermal desorption analysis, and mechanical testing, was conducted. After HIP, the β-phase morphology changed from discontinuous Widmanstätten to a more continuous structure, 10 times and ~1.5 times larger in length and width, respectively. Following HT, the β-phase morphology changed to a continuous “web-like” structure, ~4.5 times larger in width. Despite similar mechanical behavior in their non-hydrogenated state, the post-treated alloys exhibit increased susceptibility to HE due to enhanced hydrogen penetration into the bulk. It is shown that hydrogen content in the samples’ bulk is inversely dependent on surface hydride content. It is therefore concluded that the formed hydride surface layer is crucial for inhibiting further hydrogen penetration and adsorption into the bulk and thus for reducing HE susceptibility. The lack of a hydride surface layer in the samples subject to HIP and HT highlights the importance of choosing secondary treatment process parameters that will not increase the continuous β-phase morphology of EBM Ti–6Al–4V alloys in applications that involve electrochemical hydrogen environments.