Additive manufacturing, especially material extrusion (MEX), has received a lot of attention recently. The reasons for this are the numerous advantages compared to conventional manufacturing processes, which result in various new possibilities for product development and -design. By applying material layer by layer, parts with complex, load-path optimized geometries can be manufactured at neutral costs. To expand the application fields of MEX, high-strength and simultaneously lightweight materials are required which fulfill the requirements of highly resilient technical parts. For instance, the embedding of continuous carbon and flax fibers in a polymer matrix offers great potential for this. To achieve the highest possible variability with regard to the material combinations while ensuring simple and economical production, the fiber–matrix bonding should be carried out in one process step together with the actual parts manufacture. This paper deals with the adaptation and improvement of the 3D printer on the one hand and the characterization of 3D printed test specimens based on carbon and flax fibers on the other hand. For this purpose, the print head development for in-situ processing of contin uous fiber-reinforced parts with improved mechanical properties is described. It was determined that compared to neat polylactic acid (PLA), the continuous fiber-reinforced test specimens achieve up to 430% higher tensile strength and 890% higher tensile modulus for the carbon fiber reinforcement and an increase of up to 325% in tensile strength and 570% in tensile modulus for the flax fibers. Similar improvements in performance were achieved in the bending tests.

Multi-material additive manufacturing offers new design freedom for functional integration and opens new possibilities in innovative part design, for instance, a local integration of electrically conductive structures or heat radiant surfaces. Detailed experimental investigations on materials with three different fillers (carbon black (CB), carbon nanotubes (CNT) and nano copper wires) were conducted to identify process-specific influencing factors on electrical conductivity and resistive heating. In this regard, raster angle orientation, extrusion temperature, speed and flow rate were investigated. A variation of the raster angle (0°, ±45°, and 90°) shows the highest influence on resistivity. An angle of 0° had the lowest electrical resistance and the highest temperature increase due to resistive heating. The material filled with nano copper wires showed the highest electrical conductivity followed by the CNT filled material and materials filled with CB. Both current–voltage characteristics and voltage-dependent heat distribution of the surface temperature were determined by using a thermographic camera. The highest temperature increase was achieved by the CNT filled material. The materials filled with CB and nano copper wires showed increased electrical resistance depending on temperature. Based on the experiments, solution principles and design rules for additively manufactured electrically conductive structures are derived.

Three-dimensional printing used to be a rapid prototyping process, but nowadays it is establishing as an additive manufacturing (AM) process. One of these AM techniques is selective laser sintering (SLS), which most often involves partial melting of the particles and therefore belongs to the category of powder bed fusion processes. Much progress has been made in this field by research on process parameters like laser power, hatch distance, and scanning speed while still lacking a fundamental understanding of the powder deposition and its influence on parts. A critical issue for economic manufacturing is the building time of parts with good mechanical properties, which can be reduced by lower surface roughness due to less or missing post processing. Therefore, the influence of three blade shapes on powder bed surface roughness has been evaluated for PA12 powder with three different grain size distributions by using advanced X-ray micro computed tomography (XMT) and a confocal laser scanning microscope (LSM). Along with those methods, new techniques for powder characterization were tested and compared. Lowest roughness has been achieved with a flat blade, based on a higher compression due to a larger contact zone between blade and powder bed. Furthermore, an anisotropic effect of the mechanical properties resulting from different building directions has been detected which can be explained by varying amounts of solid contact paths through the powder bed depending on powder application direction. In addition, an optimal combination of process parameters with an even compression of the powder bed leads to low surface roughness, complementing the advantages of additive manufacturing.

A proven method to enhance the mechanical properties of additively manufactured plastic parts is the embedding of continuous fibers. Due to its great flexibility, continuous fiber-reinforced material extrusion allows fiber strands to be deposited along optimized paths. Nevertheless, the fibers have so far been embedded in the parts contour-based or on the basis of regular patterns. The outstanding strength and stiffness properties of the fibers in the longitudinal direction cannot be optimally utilized. Therefore, a method is proposed which allows to embed fibers along the principal stresses into the parts in a load-oriented manner. A G-code is generated from the calculated principal stress trajectories and the part geometry, which also takes into account the specific restrictions of the manufacturing technology used. A distinction is made between fiber paths and the matrix so that the average fiber volume content can be set in a defined way. To determine the mechanical properties, tensile and flexural tests are carried out on specimens consisting of carbon fiber-reinforced polyamide. In order to increase the influence of the principal stress-based fiber orientation, open-hole plates are used for the tensile tests, as this leads to variable stresses across the cross section. In addition, a digital image correlation system is used to determine the deformations during the mechanical tests. It was found that the peak load of the optimized open-hole plates was greater by a factor of 3 and the optimized flexural specimens by a factor of 1.9 than the comparison specimens with unidirectional fiber alignment.

Material composition complexity offered by material extrusion additive manufacturing offers new opportunities for function-driven part design. Nevertheless, since influencing factors on the interface strength between different materials are not well understood, this complexity is only used infrequently, in part, in design thereby restraining innovation. This paper proposes a systematical approach for identification and quantification of relevant adhesion phenomena that influence interface strength. For this reason, suited test specimen, which utilize the geometric freedom offered by additive manufacturing, are developed for roll peeling tests and peeling resistance of several combinations of rigid and flexible materials is determined. The results show that material choice especially regarding polarity as well as mechanical interlocking in regards to surface roughness and design features have high influence on the interface strength of multi-material parts manufactured by material extrusion. These results are explained through the relevant adhesion mechanisms that determine the interface strength in additively manufactured parts. Finally, criteria that predominantly affect interface strength are deduced and design recommendations for creating functional parts with ill-fitting material combinations are formulated.

An existing challenge in the use of continuous fiber reinforcements in additively manufactured parts is the limited availability of suitable fiber materials. This leads to a reduced adaptability of the mechanical properties to the load case. The increased design freedom of additive manufacturing allows the flexible deposition of fiber strands at defined positions, so that even different fiber materials can be easily combined in a printed part. In this work, therefore, an approach is taken to combine carbon and aramid fibers in printed composite parts to investigate their effects on mechanical properties. For this purpose, tensile, flexural and impact tests were performed on printed composite parts made of carbon and aramid fibers in a nylon matrix with five different mixing ratios. The tests showed that the use of hybrid composites for additive manufacturing is a reasonable approach to adapt the mechanical properties to the loading case at hand. The experiments showed that increasing the aramid fiber content resulted in an increase in impact strength, but a decrease in tensile and flexural strength and a decrease in stiffness. Microstructural investigations of the fracture surfaces showed that debonding and delamination were the main failure mechanisms. Finally, Rule of Hybrid Mixture equations were applied to predict the mechanical properties at different mixture ratios. This resulted in predicted values that differed from the experimentally determined values by an average of 5.6%.