This work investigates the effect of the addition of tungsten carbide (WC) particles as reinforcements to Ni (Inconel 625) versus Co (Stellite 6) alloys during deposition by laser cladding to form wear-resistant metal matrix composite (MMC) coatings. While the related literature often associates the presence of WC with the enhanced wear performance of MMC coatings, this work shows that such an effect is not universal as it may critically depend on the metallic matrix employed. Thus, to demonstrate whether the reinforcement and matrix act synergically in such a scenario or not, MMC coatings formed by Inconel 625 and Stellite 6, both with WC content ranging from 10% to 40%, were deposited under the same laser cladding setup on AISI 304 stainless steel substrates, being WC-free samples produced together for comparison basis. As expected, the hardness levels increased with more WC presence in both matrices, but the wear resistance was specifically evaluated by means of the metal wheel abrasion test (ASTM B611). The results revealed that the use of WC as a reinforcement indeed affects the matrix materials differently; for Stellite 6, the wear resistance increased with up to 20% of WC (in contrast to the hardness indication), whereas for Inconel 625, the wear resistance progressively decreased with more WC content. It was observed via scanning electron microscopy (SEM) that the WC particles within the Inconel 625 alloy tended to intensive cracking, being in this way more prone to detach from the matrix and hence representing a weakening factor for the effectiveness of the coatings produced. Thus, it is concluded that the addition of WC particles, as potential reinforcements for MMC coatings, is not always effective (synergic with the matrix) in providing wear resistance, hence, opposing the prevailing consensus. This outcome and its reasons will certainly help with insights into proper design of MMC coatings, starting with the importance of matrix material selection.

Laser beam powder bed fusion of metals (PBF-LB/M, or simply L-PBF) has emerged as one of the most competitive additive manufacturing technologies for producing complex metallic components with high precision, design freedom, and minimal material waste. Among the various categories of additive manufacturing processes, L-PBF stands out, paving the way for the execution of part designs with geometries previously considered unfeasible. Despite offering several advantages, parts with overhang features require the use of support structures to provide dimensional stability of the part. Support structures achieve this by resisting residual stresses generated during processing and assisting heat dissipation. Although the scientific community acknowledges the role of support structures in the success of L-PBF manufacturing, they have remained relatively underexplored in the literature. In this context, the present work investigated the impact of laser power and scanning speed on the dimensioning, integrity and tensile strength of single-walled block type support structures manufactured in AISI 316L stainless steel. The method proposed in this work is divided in two stages: processing parameter exploration, and mechanical characterization. The results indicated that support structures become more robust and resistant as laser power increases, and the opposite effect is observed with an increment in scanning speed. In addition, defects were detected at the interfaces between the bulk and support regions, which were crucial for the failure of the tensile test specimens. For a layer thickness corresponding to 0.060 mm, it was verified that the combination of laser power and scanning speed of 150 W and 500 mm/s resulted in the highest tensile resistance while respecting the dimensional deviation requirement.