Cutting force and temperature are critical indicators for improving cutting performance and productivity. This study used an up-milling experiment to ascertain the effect of tool tooth number, cutting speed, and depth on the machinability of bamboo–plastic composite. We focused on the changes in the resultant force and cutting temperature under different milling conditions. A response surface methodology was used to build prediction models for the resultant force and temperature. A verification test was conducted to prove the model’s reliability. The empirical findings suggested that the number of tool teeth had the most significant impacts on both the resultant force and the cutting temperature, followed by the depth of cut and the cutting speed. Moreover, the resultant force and cutting temperature showed increasing trends with decreasing numbers of tool teeth and increasing cut depths. However, cutting speed had a negative relationship with the resultant force and a positive relationship with temperature. We also determined the optimal milling conditions with the lowest force and temperature: four tool teeth, 300 m/min cutting speed, and 0.5 mm depth. This parameter combination can be used in the industrial manufacture of bamboo–plastic composite to improve tool life and manufacturing productivity.

Beech wood is a material commonly used for furniture, and cutting performance is the key to improving product quality and enterprise benefits. In this work, beech milling experiments using diamond cutters were carried out, and the changes in cutting power, temperature, and surface roughness were examined using the factor analysis method. The main results of this work are listed as follows: Firstly, a higher cutting speed and depth led to higher cutting power, temperature, and surface roughness. Meanwhile, cutting power and surface roughness were negatively related to the rake angle; however, cutting temperature first increased and then decreased with the increase in rake angle. Furthermore, cutting depth had greatest impact on the cutting power and surface roughness, followed by rake angle and cutting speed. Cutting speed had the greatest contribution to the cutting temperature, followed by cutting depth and rake angle. Only the cutting depth had a significant contribution to both cutting power, temperature, and surface roughness. Finally, optimal cutting parameters were determined to be a rake angle of 15°, cutting speed of 54 m/s, and depth of 0.5 mm. These values best meet the multiple objectives of lower cutting power, temperature, and surface roughness, which relate to superior product quality and enterprise benefits.

Wood–plastic composites (WPCs) are important materials used in interior architectural decorations and landscape construction products. Enhancing the cutting performance of WPCs is of great significance for improving both production efficiency and product quality in factories. This study aims to elucidate the impact of fluorine nano-coating technology on the cutting performance of cemented carbide tools during the milling of WPCs. The main results are given as follows. The cutting force and surface roughness showed similar trends with the varied parameters; both increased with increasing cutting depth and decreased with increasing cutting speed. The fluorine nano-coating technology exerts a positive influence on the cutting performance in terms of lower cutting forces and surface roughness. Meanwhile, based on the analysis of variance results, the experimental factors of cutting speed, depth, and surface treatment had a significant contribution to both cutting force and surface roughness, and cutting depth had the greatest impact on cutting force and surface roughness, followed by cutting speed and tool surface treatment. In general, the cutting performance of WPCs can be improved by higher cutting speed and lower depth, with the tool surface treated with fluorine nano-coating.