In this work, a novel hybrid SERS platform incorporating hybrid core-shell (HyCoS) AuPd nanoparticles (NPs) and MoS₂ nanoplatelets has been successfully demonstrated for strong surface-enhanced Raman spectroscopy (SERS) enhancement of Rhodamine 6G (R6G). A significantly improved SERS signal of R6G is observed on the hybrid SERS platform by adapting both electromagnetic mechanism (EM) and chemical mechanism (CM) in a single platform. The EM enhancement originates from the unique plasmonic HyCoS AuPd NP template fabricated by the modified droplet epitaxy, which exhibits strong plasmon excitation of hotspots at the nanogaps of metallic NPs and abundant generation of electric fields by localized surface plasmon resonance (LSPR). Superior LSPR results from the coupling of distinctive AuPd core-shell NP and high-density background Au NPs. The CM enhancement is associated with the charge transfer from the MoS₂ nanoplatelets to the R6G. The direct contact via mixing approach with optimal mixing ratio can effectively facilitate the charges transfer to the HOMO and LUMO of R6G, leading to the orders of Raman signal amplification. The enhancement factor (EF) for the proposed hybrid platform reaches ~10¹⁰ for R6G on the hybrid SERS platform.

Hydrogen is one of the most promising green energy alternatives due to its high gravimetric energy density, zero-carbon emissions, and other advantages. In this work, a CoFeBP micro-flower (MF) electrocatalyst is fabricated as an advanced water-splitting electrocatalyst by a hydrothermal approach for hydrogen production with the highly efficient hydrogen evolution reaction (HER) and oxygen evolution reaction (OER). The fabrication process of the CoFeBP MF electrocatalyst is systematically optimized by thorough investigations on various hydrothermal synthesis and post-annealing parameters. The best optimized CoFeBP MF electrode demonstrates HER/OER overpotentials of 20 mV and 219 mV at 20 mA/cm². The CoFeBP MFs also exhibit a low 2-electrode (2-E) cell voltage of 1.60 V at 50 mA/cm², which is comparable to the benchmark electrodes of Pt/C and RuO₂. The CoFeBP MFs demonstrate excellent 2-E stability of over 100 h operation under harsh industrial operational conditions at 60 °C in 6 M KOH at a high current density of 1000 mA/cm². The flower-like morphology can offer a largely increased electrochemical active surface area (ECSA), and systematic post-annealing can lead to improved crystallinity in CoFeBP MFs.