Composite and nanocomposite ceramics have achieved special interest in recent years when used for biomedical applications. They have demonstrated, in some cases, increased performance, reliability, and stability in vivo, with respect to pure monolithic ceramics. Current research aims at developing new compositions and architectures to further increase their properties. However, the ability to tailor the microstructure requires the careful control of all steps of manufacturing, from the synthesis of composite nanopowders, to their processing and sintering. This review aims at deepening understanding of the critical issues associated with the manufacturing of nanocomposite ceramics, focusing on the key role of the synthesis methods to develop homogeneous and tailored microstructures. In this frame, the authors have developed an innovative method, named “surface-coating process”, in which matrix oxide powders are coated with inorganic precursors of the second phase. The method is illustrated into two case studies; the former, on Zirconia Toughened Alumina (ZTA) materials for orthopedic applications, and the latter, on Zirconia-based composites for dental implants, discussing the advances and the potential of the method, which can become a valuable alternative to the current synthesis process already used at a clinical and industrial scale.

We study the shear rheological behavior of a commercial stereolithography paste containing ≈50 vol. % of zirconia particles (diameter ≈ 100 nm) with the aim to clarify physical mechanisms occurring during the “scraping” step of this yield stress fluid. Beyond a flow curve characterized by a high zero-shear viscosity accompanied with an overall shear-thinning behavior, we investigate in a systematic way the transient regime through start-up experiments. We demonstrate that a structural transition occurs between 10−2 and 10−1 s−1, resulting in an apparent interruption of the shear-thinning. The corresponding transient response presents a pronounced extra-growth of the shear stress before to stabilize at high strain amplitude and a negative first normal stress difference peak, both effects become stronger at higher shear rates. These observations are rationalized based on the high interparticle friction owing to the polyhedral shape and the roughness of the particles. In addition, relaxation tests following the start-up experiments reveal that the samples submitted to shear rates higher than 10−1 s−1 cannot relax the shear stress to the same level as in low shear rate experiments, suggesting a durable structural modification likely to impact the quality of the parts prior to their debinding and densification. Finally, we utilize orthogonal superposition rheology to illustrate how the application of an oscillatory deformation during the scraping procedure could help to reduce the shear-thinning interruption and improve the stereolithography processing as already observed empirically during scraping.