In this work, the assessment of Azadirachta indica, Tagetes erecta, Chrysanthemum morifolium, and Lentinula edodes extracts as catalysts for the green synthesis of zinc oxide nanoparticles (ZnO NPs) was performed. The photocatalytic properties of ZnO NPs were investigated by the photodegradation of methylene blue (MB) dye under sunlight irradiation. UV-visible (UV-Vis) spectroscopy, Fourier Transform Infrared (FTIR) spectroscopy, Transmission Electron Microscopy (TEM), X-ray Diffraction (XRD), Thermogravimetric (TGA), and Brunauer-Emmett-Teller analysis (BET) were used for the characterization of samples. The XRD results indicate that all synthesized nanoparticles have a hexagonal wurtzite crystalline structure, which was confirmed by TEM. Further, TEM analysis proved the formation of spherical and hemispherical nanoparticles of ZnO with a size in the range of 14–32 nm, which were found in aggregate shape; such a size was well below the size of the particles synthesized with no extract (~43 nm). ZnO NPs produced with Tagetes erecta and Lentinula edodes showed the best photocatalytic activity, matching with the maximum adsorbed MB molecules (45.41 and 58.73%, respectively). MB was completely degraded in 45 min using Tagetes erecta and 120 min using Lentinula edodes when subjected to solar irradiation.

The success of orthopedic implants critically depends on achieving mechanical and biological compatibility with bone tissue. Traditional titanium implants often suffer from high stiffness, which induces stress shielding, a phenomenon that compromises implant integration and accelerates prosthetic loosening. This study introduces an innovative approach to mitigate these limitations by engineering a porous titanium substrate with a controlled microstructure. Utilizing sodium chloride as a spacer holder, an elution and sintering process was applied at 1250 °C under high vacuum conditions to reduce the material’s elastic modulus. By manipulating NaCl volume fractions (20%, 25%, 30%, and 35%), porous titanium samples were created with elastic moduli between 16.37 and 22.56 GPa, closely matching cortical bone properties (4 to 20 GPa). A hydroxyapatite coating applied via plasma thermal spraying further enhanced osseointegration of the material. Comprehensive characterization through X-ray diffraction, scanning electron microscopy, and compression testing validated the material’s structural integrity. In vitro cytotoxicity assessments using osteoblast cells demonstrated exceptional cell viability exceeding 70%, confirming the material’s biocompatibility. These findings represent a significant advancement in biomaterial design, offering a promising strategy for developing next-generation joint prostheses with superior mechanical and biological adaptation to bone tissue.

This study presents the green synthesis and comprehensive characterization of ZnO–Ag nanocomposites using an eco-friendly approach that incorporates aqueous Tagetes erecta extract via the co-precipitation method. The research systematically evaluates the effect of silver concentration (0.1–0.5%) on material properties and dual applications: solar photocatalytic degradation of methylene blue and antibacterial activity against both Gram-positive (Staphylococcus aureus) and Gram-negative (Escherichia coli) bacteria. Advanced characterization techniques, including UV-Vis, XRD, TEM, FTIR, and TGA, confirmed the successful formation of crystalline nanocomposites with spherical and hemispherical morphologies, consisting of hexagonal wurtzite ZnO and face-centered cubic Ag phases. Results demonstrate that strategic silver incorporation significantly enhances ZnO photocatalytic activity by improving charge separation and reducing recombination rates, with the ZnO–Ag (0.3%) nanocomposite exhibiting optimal performance, achieving complete methylene blue degradation within 25 min under solar irradiation. Antibacterial assays showed efficacy against the bacteria used, with a significantly stronger bactericidal effect against S. aureus than E. coli, especially for ZnO–Ag (0.2%) at a 250 μg/mL concentration. This study highlights the synergistic effect between ZnO, Ag, and bioactive compounds from Tagetes erecta, offering a sustainable approach for developing multifunctional nanomaterials with significant potential in environmental remediation and antibacterial applications.