To harvest and reuse low-temperature waste heat, we propose and realize an emergent concept—barocaloric thermal batteries based on the large inverse barocaloric effect of ammonium thiocyanate (NH ₄ SCN). Thermal charging is initialized upon pressurization through an order-to-disorder phase transition, and the discharging of 43 J g ⁻¹ takes place at depressurization, which is 11 times more than the input mechanical energy. The thermodynamic equilibrium nature of the pressure-restrained heat-carrying phase guarantees stable long-duration storage. The barocaloric thermal batteries reinforced by their solid microscopic mechanism are expected to substantially advance the ability to take advantage of waste heat.

High-entropy ceramics (HECs) have garnered considerable interest due to their exceptional mechanical properties and high-temperature stability. Nevertheless, their inherent brittleness significantly restricts industrial applications, posing a challenge to improving toughness without compromising hardness. This study investigates the role of SiC whiskers (SiCw) in simultaneously suppressing grain growth and enhancing the toughness of high-entropy (Ti_0.2Zr_0.2Hf_0.2Nb_0.2Ta_0.2)C (HEC) composites, while maintaining high hardness during high-pressure high-temperature (HPHT) sintering. HEC-SiCw composites were fabricated via HPHT (P = 5 GPa, T = 2000 °C), with SiCw contents ranging from 0 to 40 mol%. As the SiCw content increased, the growth of HEC grains was inhibited, and the fracture toughness progressively rose to a peak value (K_IC = 9.4 ± 1.2 MPa·m^1/2), representing an increase of approximately 184% compared to that of pure HEC, while Vickers hardness remained stable at 26 GPa. The enhancement in fracture toughness is attributed to the heterogeneous grain distribution and robust grain boundary strength, which facilitated a synergistic combination of transgranular and intergranular fracture mechanisms. These mechanisms induced crack deflection and whisker pull-out, effectively dissipating fracture energy and impeding crack propagation, thereby enhancing toughness. This study presents a novel approach to simultaneously refine grain size and improve toughness in HECs through HPHT processing, providing valuable insights for the development of next-generation ceramic composites.