This study examines the influence of pyrolysis temperature on the physicochemical characteristics of malt-derived biochar (BC) and its effect on the performance of cement mortars. Malt biomass, a by-product of the brewing industry, was subjected to pyrolysis at 300 °C and 500 °C, followed by high-energy ball milling to produce nanoscale biochar. Characterization using FTIR, Raman spectroscopy, XRD, BET, SEM, and XRF revealed that BC500 possessed higher graphitic ordering, larger specific surface area (110 m₂/g), and smaller pore size compared to BC300, which exhibited greater hydrophobicity. Incorporation of BC500 into cement mortars at 0.25–1.0 wt.%, with and without superplasticizer, resulted in up to a 20.6% increase in compressive strength and a significant reduction in water absorption. These enhancements are attributed to the internal curing effect of biochar, its refined pore structure, and improved interfacial bonding with hydration products. The findings demonstrate that optimized malt biochar serves as a sustainable additive that improves the mechanical performance and durability of cementitious materials while advancing circular economy principles through the valorization of industrial malt waste and the mitigation of the environmental impact of cement production.

The growing demand for sustainable construction materials has intensified efforts to reduce the environmental impact of Portland cement. This study investigates the effect of partial substitution of cement with metakaolin (MK, 5–15 wt.%) and biosilica (BS, 5 wt.%) on the physical, mechanical, and microstructural properties of cementitious mortars. The influence of a polycarboxylate ether-based superplasticizer (Mf) and ultrasonic treatment (ULT) was also evaluated. The mortars were characterized through setting time, density, water absorption, flexural and compressive strength tests, as well as FTIR and SEM analyses. Water absorption decreased from 12.21% to 9.8%, indicating improved pore refinement and densification. Flexural strength of all modified mortars exceeded that of the control mix: from 10.0% to 89.9% at 7 days, and from 4.7% to 50.4% at 28 days. The compressive strength improved markedly with MK and BS incorporation, from 20.8% to 51.3% at 7 days and from 9.7% to 35.2% at 28 days compared to the control sample. FTIR and SEM results confirmed enhanced pozzolanic activity and formation of C–S–H gel. The synergistic use of MK, BS, and Mf—especially with ultrasonic dispersion—yielded denser, stronger, and more sustainable cementitious composites.