This study investigated how the water–cement ratio and silica fume concentration affect the compressive strength of cement mortars. This comprehensive study delved into the intricate interplay between water–cement ratio and silica fume concentration, examining their influence on cement-based mortars’ compressive strength and water absorption characteristics. The silica fume concentration was investigated, ranging from 5% to 15% of the cement weight. The investigation employed two distinct mixing techniques, mixing cement and silica fume, before extracting appropriate samples; alternatively, a magnetic stirrer was used to prepare samples by dissolving silica fume in water. The cement mortars were also prepared with three different water–cement ratios: 0.44, 0.47, and 0.5. The interesting findings of compressive tests illuminated a consistent trend across all curing days and mixing methods—a reduction in the water–cement ratio corresponded with a notable increase in compressive strength. However, it is essential to note that the influence of the mixing method on the compressive strength of cement-based mortars is based on the water–cement ratio. The results show that by using the suggested technological method, it was observed that samples prepared with water–cement ratios (W/C) of 0.47 and 0.44 exhibited higher compressive strengths compared to those prepared using the well-known standard mixing method. The compressive test results underscored that the water–cement ratio reduction consistently enhanced the compressive strength in every combination of curing days and mixing techniques. Furthermore, this reduction in the water–cement ratio was correlated with a decrease in water absorption of the mortar. Conversely, the water–cement ratio itself played a pivotal role in defining how the mixing technique affected the compressive strength and water absorption of cement-based mortars. This multifaceted exploration underscores the nuanced relationships between key variables, emphasizing the need for a comprehensive understanding of the intricate factors influencing the mechanical and absorptive properties of cement-based materials.

In this work, multi-walled carbon nanotubes (MWCNTs) have been synthesized using a modified method of solid-phase pyrolysis. The MWCNTs are effectively dispersed using a simple and facile method such as ultrasonic energy without and with surfactant for two different sonication times (15 min and 40 min). In the present study, the effect of MWCNT concentration (0.001, 0.01, 0.05, 0.1 wt.%) on the compressive strengths of cement mortars has been investigated. Compressive tests were carried out on an automatic pressure machine (C089) with a loading rate of 0.5 kN/s at the age of 7 days and 28 days. It is shown that the optimal value of the nanotubes’ concentration does not exist in the case of 15 min of sonication time, whereas the optimal value for 40 min of sonication time without and with surfactant is 0.01%. Moreover, in the absence of surfactants, the strength of the specimen over 7 days of hardening increased by 13%, and by 19.5% in the presence of surfactants. The compressive strength for a curing period of 28 days increased by 6.3% and 13.8%, respectively.

In this work, the effect of biosilica concentration and two different mixing methods with Portland cement on the compressive strength of cement-based mortars were investigated. The following values of the biosilica concentration of cement weight were investigated։ 2.5, 5, 7.5, and 10 wt.%. The mortar was prepared using the following two biosilica mixing methods: First, biosilica was mixed with cement and appropriate samples were prepared. For the other mixing method, samples were prepared by dissolving biosilica in water using a magnetic stirrer. Compressive tests were carried out on an automatic compression machine with a loading rate of 2.4 kN/s at the age of 7 and 28 days. It is shown that, for all cases, the compressive strength has the maximum value of 10% biosilica concentration. In particular, in the case of the first mixing method, the compressive strength of the specimen over 7 days of curing increased by 30.5%, and by 36.5% for a curing period of 28 days. In the case of the second mixing method, the compressive strength of the specimen over 7 days of curing increased by 23.4%, and by 47.3% for a curing period of 28 days. Additionally, using the first and second mixing methods, the water absorption parameters were reduced by 22% and 34%, respectively. Finally, it is worth noting that the obtained results were intend to provide valuable insights into optimizing biosilica incorporation in cement mortar. With the aim of contributing to the advancement of construction materials, this research delves into the intriguing application of biosilica in cement mortar, emphasizing the significant impact of mixing techniques on the resultant compressive strength.

In this work, the effect of multi-walled carbon nanotubes (MWCNT1, MWCNT2, and MWCNT3) with different outer diameters and specific surface areas on the mechanical and electrical properties of cement mortar have been investigated. Various concentrations of MWCNTs were used (0.05, 0.10, and 0.15%), the effective dispersion of which was carried out by an Ultrasonic machine (for 40 min with 160 W power and a 24 kHz frequency) using a surfactant. Composites have been processed with a biosilica content of 10% by weight of cement and without it. Compressive strength tests were carried out on days 7 and 28 of curing. The 7-day compressive strength of samples prepared without biosilica increased compared to the result of the control sample (6.4% for MWCNT1, 7.4% for MWCNT2, and 10.8% for MWCNT3), as did those using biosilica (6.7% in the case of MWCNT1, 29.2% for MWCNT2, and 2.1% for MWCNT3). Compressive strength tests of 28-day specimens yielded the following results: 21.7% for MWCNT1, 3.8% for MWCNT2, and 4.2% for MWCNT3 in the absence of biosilica and 8.5%, 12.6%, and 6.3% with biosilica, respectively. The maximum increase in compressive strength was observed in the composites treated with a 0.1% MWCNT concentration, while in the case of 0.05 and 0.15% concentrations, the compressive strengths were relatively low. The MWCNT-reinforced cement matrix obtained electrical properties due to the high electrical conductivity of these particles. The effect of MWCNT concentrations of 0.05, 0.10, and 0.15 wt% on the electrical properties of cement mortar, especially the bulk electrical resistivity and piezoresistive characteristics of cement mortar, was studied in this work. At a concentration of 0.05%, the lowest value of resistivity was obtained, and then it started to increase. The obtained results show that all investigated specimens have piezoresistive properties and that the measurements led to a deviation in fractional change in resistivity.

This study examines the influence of pyrolysis temperature on the physicochemical characteristics of malt-derived biochar (BC) and its effect on the performance of cement mortars. Malt biomass, a by-product of the brewing industry, was subjected to pyrolysis at 300 °C and 500 °C, followed by high-energy ball milling to produce nanoscale biochar. Characterization using FTIR, Raman spectroscopy, XRD, BET, SEM, and XRF revealed that BC500 possessed higher graphitic ordering, larger specific surface area (110 m₂/g), and smaller pore size compared to BC300, which exhibited greater hydrophobicity. Incorporation of BC500 into cement mortars at 0.25–1.0 wt.%, with and without superplasticizer, resulted in up to a 20.6% increase in compressive strength and a significant reduction in water absorption. These enhancements are attributed to the internal curing effect of biochar, its refined pore structure, and improved interfacial bonding with hydration products. The findings demonstrate that optimized malt biochar serves as a sustainable additive that improves the mechanical performance and durability of cementitious materials while advancing circular economy principles through the valorization of industrial malt waste and the mitigation of the environmental impact of cement production.

This work presents the types of waste of Armenian volcanic aluminosilicate tuff rocks extraction, as a component of the raw material of non-cement, artificial stone materials, the technical possibilities of their use, and the results of experiments for meeting the indicators of physical and mechanical characteristics of natural stone. Preliminary orientational experimental studies have specified the proportions of the raw materials in the compositions, the connections between the preparation of mixtures, the compaction of samples, and the shortest possible heat treatment regimes at temperatures up to 200 °C. Non-cement artificial stones were developed using tuff waste, with filler–composite binder ratios of 75/25 and 70/30, and a water/solid mass ratio of 0.10-to-0.12%. After 9 h of heat treatment, the density, water absorption, and compressive strength of non-cement artificial stone materials were determined. The results showed that these materials outperformed natural stone materials from the same deposits, in terms of the same physical and mechanical characteristics. The use of tuff waste resulted in increased densities, from 10.5 to 39%, decreased water absorption by 2 to 2.5 times, and increased compressive strength of non-cement artificial stone materials, from 15 to 30% compared to natural tuff stones. X-ray diffraction and SEM image studies were also carried out for the obtained non-cement artificial stones. The novelty in the developed technology of obtaining stone materials primarily revolves around the mixture preparation technology by using tuff waste materials and low-temperature heat treatment.