Silver nanoparticles (AgNPs) play an important role in the medical field due to their potent antimicrobial activity. This, together with the constant emergence of resistance to antimicrobial drugs, means AgNPs are often investigated as an alternative to solve this problem. In this article, we analyzed the antifungal and antiamoebic effects of a recently described type of AgNP, silver nanorings (AgNRs), and compared them with other types of AgNPs. Tests of the activity of AgNPs against various fungal and amoebic species were carried out. In all cases, AgNPs showed a high biocidal effect, although with fungi this depended on the species involved. Antifungal activity was detected by the conditioning of culture media or water but this effect was not dependent on the release of Ag ions. On the other hand, the proliferation of Acanthamoeba castellanii trophozoites was reduced by silver nanorings (AgNRs) and silver nanowires (AgNWs), with AgNWs being capable of totally inhibiting the germination of A. castellanii cysts. AgNRs constitute a new type of AgNP with an antifungal and antiacanthamoebic activity. These results open the door to new and effective antimicrobial therapies as an alternative to the use of antifungals or antiamoebic drugs, thus avoiding the constant appearance of resistance and the difficulty of eradicating infections.

In this work, silicon oxide based coatings with embedded graphene nanoplatelets (content ranging from 1.8 wt.% to 7.2 wt.%) have been developed following the sol-gel route, using AISI430 stainless steel as substrate and dip and roll-to-roll as coating techniques. The tribological and corrosion behaviour of these coatings have been evaluated and compared to bare steel. Concerning tribological behaviour, the coefficient of friction and wear print were significantly reduced with increasing the graphene nanoplatelets content. Regarding corrosion, all coatings showed improved corrosion behaviour compared to bare steel. However, higher concentration of nanoplatelets revealed a negative effect on the corrosion resistance, probably due to aggregation. Taking into account these two counteracting effects, as final part of this work, a bilayer coating with different graphene content has been proposed and fabricated. A top layer, with high graphene nanoplatelets concentration has allowed enhanced tribological properties whereas bottom layer, with no graphene nanoplatelets assures corrosion inhibition under harsh environments.