X-ray absorption and emission spectroscopy, FTIR and DFT unravel the major Cu species in the activated Cu-SSZ-13 catalyst for NH ₃ -SCR.

Here we report the interpretation of all spectral features of Ce ${\mathit{L}}_3$ x-ray-absorption near-edge structure (XANES) of ${\mathrm{CeO}}_2$ over a 40 eV range. The local partial unoccupied density of states in the initial state and in the fully relaxed final state have been calculated by the full multiple-scattering approach. The wave function of the excited electron in the final states of the Ce ${\mathit{L}}_3$-edge XANES spectrum is found to be determined by the multiple-scattering processes in a large size cluster formed by at least 45 atoms. We predict, in good agreement with the experimental data, the crystal-field splitting of 5d states in the final state ${\mathrm{\Delta }}_{\mathit{f}}$=4.0±0.2 eV and its variation from the initial to the final state. The many-body final states for the 2p→5,ɛd transition, arising from the configuration interaction due to mixing of Ce 4f and O 2p valence orbitals, have been calculated taking into account the crystal-field splitting of the 5,ɛd states and they give a full explanation for the low-energy shoulder on the Ce ${\mathit{L}}_3$ x-ray-absorption spectrum white line that was the object of a long-standing discussion. The origin of the pre-edge peak at about 10 eV below the white line maximum is explained as due to transitions at the bottom of the conduction band.

Nanoscience enables researchers to develop new and cost-effective nanomaterials for energy, healthcare, and medical applications. Silver nanoparticles (Ag NPs) are currently increasingly synthesized for their superior physicochemical and electronic properties. Good knowledge of these characteristics allows the development of applications in all sensitive and essential fields in the service of humans and the environment. This review aims to summarize the Ag NPs synthesis methods, properties, applications, and future challenges. Generally, Ag NPs can be synthesized using physical, chemical, and biological routes. Due to the great and increasing demand for metal and metal oxide nanoparticles, researchers have invented a new, environmentally friendly, inexpensive synthetic method that replaces other methods with many defects. Studies of Ag NPs have increased after clear and substantial support from governments to develop nanotechnology. Ag NPs are the most widely due to their various potent properties. Thus, this comprehensive review discusses the different synthesis procedures and electronic applications of Ag NPs.

In this study, silver/silver oxide nanoparticles (Ag/Ag₂O NPs) were successfully biosynthesized using Phoenix dactylifera L. aqueous leaves extract. The effect of different plant extract/precursor contractions (volume ratio, v/v%) on Ag/Ag₂O NP formation, their optical properties, and photocatalytic activity towards azo dye degradation, i.e., Congo red (CR) and methylene blue (MB), were investigated. X-ray diffraction confirmed the crystalline nature of Ag/Ag₂O NPs with a crystallite size range from 28 to 39 nm. Scanning electron microscope images showed that the Ag/Ag₂O NPs have an oval and spherical shape. UV–vis spectroscopy showed that Ag/Ag₂O NPs have a direct bandgap of 2.07–2.86 eV and an indirect bandgap of 1.60–1.76 eV. Fourier transform infrared analysis suggests that the synthesized Ag/Ag₂O NPs might be stabilized through the interactions of -OH and C=O groups in the carbohydrates, flavonoids, tannins, and phenolic acids present in Phoenix dactylifera L. Interestingly, the prepared Ag/Ag₂O NPs showed high catalytic degradation activity for CR dye. The photocatalytic degradation of the azo dye was monitored spectrophotometrically in a wavelength range of 250–900 nm, and a high decolorization efficiency (84.50%) was obtained after 50 min of reaction. As a result, the use of Phoenix dactylifera L. aqueous leaves extract offers a cost-effective and eco-friendly method.