This study is focused on the effect of basalt fiber on the road performance of the asphalt mixture. The road performance of asphalt mixture with different dosages of basalt fiber was comprehensively evaluated using Marshall Stability test, the wheel tracking test, the three-point bending beam test and the freezing-thaw splitting test. The road performance of lignin fiber reinforced asphalt mixture and polyester fiber reinforced asphalt mixture also were tested to compare with the road performance of basalt fiber reinforced asphalt mixture. The results showed that basalt fiber can enhance mechanical properties, the low-and high-temperature performance and water sensitivity of the asphalt mixture significantly. Considering the road performance and economic benefits, the appropriate dosage of basalt fiber is about 0.3%. Marshall Stability (MS), dynamic stability (DS), the maximum bending strain and the tensile strength ratio (TSR) of asphalt mixture with 0.3% basalt fiber were increased by 19.6%, 25.5%, 22.2% and 6.0%, respectively. Basalt fiber has certain advantages in improving the low-temperature performance of asphalt mixture by comparison with lignin fiber and polyester fiber.

The performance of an asphalt mixture will deteriorate under the condition of salt erosion, but there are different opinions on the mechanism of deterioration. Few studies have focused on the relation between the change of void characteristics and performance deterioration of an asphalt mixture exposed to salt erosion. To explore the relation between the air voids characteristics of an asphalt mixture and mechanical damage under salt erosion, the mechanical damage in an asphalt mixture was measured by splitting strength. The asphalt mixture specimens, immersion solutions, asphalt mortar, and aggregate were scanned with CT technology. To segment the voids, the Otsu method was used over asphalt mortar and solution range of CT values. A three-dimensional reconstruction of the CT image was performed with Mimics 20 software to calculate the asphalt mixture’s void characteristics. On this basis, the relationships between the change in void characteristics and splitting strength were analyzed. The results showed that the ideal calculated void fraction can be obtained by threshold segmentation of the image void/asphalt mortar interface with the local CT value Otsu method. Under the salt corrosion environment, the increase of open voids of an asphalt mixture is linearly correlated with the decrease of splitting strength, while salts’ crystallization in the open voids produces crystallization pressure, accelerating the volume growth of open voids. The early damage of an asphalt mixture suffered from the salt may be mainly physical damage. These results can provide a useful reference for the performance of damage research on asphalt mixtures in salt enrichment areas.

This article intends to study the influence of macrotexture and microtexture on the skid resistance of four types of aggregates. For this purpose, fractal dimension (D), root mean square height (R_q), and Polished Stone Value (PSV) were tested. The Pearson correlation coefficients between PSV and D or R_q in the interval of different polishing cycles were calculated and analyzed with correlation analysis. The relationships between PSV and R_q were also established. The results showed that the PSV development was approximately divided into 3 stages including accelerated attenuation stage, decelerated attenuation stage, and stabilization stage. There is a critical point of the entire polishing cycles. When the number of the polishing cycles exceeds this critical point, microtexture replaces macrotexture to play a major role in the skid resistance of aggregates. In the accelerated attenuation stage, macrotexture plays a major role in the skid resistance of aggregates. In the decelerated attenuation stage and stabilization stage, microtexture gradually plays a major role in the skid resistance of aggregates. Because of roughest microtexture in the stabilization stage, bauxite can provide the highest levels of skid resistance for high friction surface treatment over the long‐term period.

This study was intended to evaluate how citric acid influences the time-dependent rheological properties of magnesium oxychloride cement (MOC). For this purpose, rheological parameters, setting time, electrodeless resistivity, crystal phases, morphology, hydration product, and compressive strength were investigated. The results show that the addition of citric acid can improve the time-dependent rheological properties of MOC pastes due to the retarding effect of the citric acid. The citric acid dosages of 0.15, 0.25, and 0.35% can stabilize the rheological properties of MOC paste in 1, 2, and 3 h, respectively. The addition of citric acid prolonged the setting stage by introducing free ${\mathrm{H}}^{+}$ that weakened the flocculated structure of MOC paste and delayed the formation of $5\mathrm{MgO}·{\mathrm{MgCl}}_2·8{\mathrm{H}}_2\mathrm{O}$ . The early compressive strength was significantly decreased with increasing dosages of citric acid; however, the citric acid had less of a negative effect on the late compressive strength.

This article is intended to investigate the microwave heating performance of asphalt mixtures containing magnetite powders (MPAM). For this purpose, the surface temperatures of asphalt mixtures containing different dosages of magnetite powders were measured during microwave heating. The low-temperature bending test and water sensitivity test were also conducted to evaluate the performance of MPAM. Heating rate and reflection loss of different thicknesses of MPAM were determined using a microwave heating test and arch reflectivity test, respectively. The results showed that because its main components are triiron tetroxide and iron oxide, which have excellent microwave-absorbing properties, magnetite powders can be used as microwave absorbers to improve the ability of microwave absorption and increase the heating rate of asphalt mixtures. The heating rate of the asphalt mixtures increased with the increase of the amount of magnetite powder. The addition of magnetite powder improved the low-temperature properties of the asphalt mixture, but it reduced the water stability of the asphalt mixture. Considering that the microwave-absorbing asphalt mixture used for melting snow and ice should have good water stability, the recommended dosage of magnetite powders was 60%. The microwave-absorbing properties of MPAM were related to its thickness in the pavement structure and frequency of microwaves. In order to greatly enhance the absorbing efficiency, future work should be focused on matching thickness and matching frequency.