Novel yellow azo pyridone dye derivatives were synthesized for use in image-sensor color filters. The synthesized compounds have a basic chemical structure composed of azo, hydroxy, amide, and nitrile groups as well as different halide groups. New materials were evaluated on the basis of their optical, thermal, and surface properties under conditions mimicking those of a commercial device fabrication process. A comparison of their related performance revealed that, among the four prepared compounds, 5-((4,6-dichlorocyclohexa-2,4-dien-1-yl)diazenyl)-6-hydroxy-1,4-dimethyl-2-oxo-1,2-dihydropyridine-3-carbonitrile (Cl-PAMOPC) exhibited the best performance as an image-sensor color filter material, including a solubility greater than 0.1 wt% in propylene glycol monomethyl ether acetate solvent, a high decomposition temperature of 263 °C, and stable color difference values of 4.93 and 3.88 after a thermal treatment and a solvent-resistance test, respectively. The results suggest that Cl-PAMOPC can be used as a green dye additive in an image-sensor colorant.

We designed and synthesized new indolocarbazole-triazine derivatives, 9-di-tert-butyl-5,7-bis(4-(4,6-diphenyl-1,3,5-triazin-2-yl)phenyl)-5,7-dihydroindolo[2,3-b]carbazole (2TRZ-P-ICz) and 3,9-di-tert-butyl-5,7-bis(5′-(4,6-diphenyl-1,3,5-triazin-2-yl)-[1,1′:3′,1″-terphenyl]-2′-yl)-5,7-dihydroindolo[2,3-b]carbazole (2TRZ-TP-ICz), as new bipolar host materials for red phosphorescent OLEDs. In the film state, 2TRZ-P-ICz and 2TRZ-TP-ICz exhibited photoluminescence maxima at 480 nm and 488 nm, respectively. The dipole moment characteristics of the new compounds under various solvent conditions were investigated using the Lippert–Mataga equation. The results showed that the dipole moment of 2TRZ-P-ICz is 26.9D, while that of 2TRZ-TP-ICz is 21.3D. The delayed fluorescence lifetimes were 0.188 μs for 2TRZ-P-ICz and 2.080 μs for 2TRZ-TP-ICz, with 2TRZ-TP-ICz showing TADF characteristics. Additionally, 2TRZ-TP-ICz was found to have a ΔEST of less than 0.2 eV. The triplet energy levels of the newly synthesized bipolar host materials were found to be 2.72 and 2.75 eV, confirming their suitability for use in red phosphorescent OLEDs. To investigate the carrier mobility of the synthesized materials, hole-only devices and electron-only devices were fabricated and tested. The hole mobility value at 1V was found to be 3.43 × 10−3 cm2/Vs for 2TRZ-P-ICz and 2.16 × 10−3 cm2/Vs for 2TRZ-TP-ICz. For electron mobility at 1V, 2TRZ-P-ICz showed a value of 4.41 × 10−9 cm2/Vs, while 2TRZ-TP-ICz exhibited a value of 9.13 × 10−9 cm2/Vs. As a result, when the new material was used as a host in red phosphorescent OLEDs, 2TRZ-TP-ICz achieved a current efficiency of 9.92 cd/A, an external quantum efficiency of 13.7%, CIE coordinates of (0.679, 0.319), and an electroluminescence maximum wavelength of 626 nm.

We report the molecular design and synthesis of a novel selenium-containing multi-resonance thermally activated delayed fluorescence (MR-TADF) host material, 3,6-di-tert-butyl-9,16-dioxa-15-selena-4b-boraindeno[2,1-a]naphtho[3,2,1-de]anthracene (TDBA-SePh), for green and red phosphorescent organic light-emitting diodes (PhOLEDs). By incorporating selenium into the DOBNA-based MR-TADF backbone, the reverse intersystem crossing (RISC) process was effectively activated, leading to enhanced utilization of triplet excitons. The corresponding RISC rate was determined to be 3.91 × 10⁴ s⁻¹. When applied to PhOLED devices, TDBA-SePh-based green and red OLEDs exhibited higher external quantum efficiency (EQE) and reduced efficiency roll-off compared to conventional mCP-based host materials. At a luminance of 1000 cd m⁻², the green and red devices exhibited roll-off values of 2.5% and 4.3%, respectively. This improvement is attributed to the incorporation of selenium as a heteroatom, which accelerates the RISC process, thereby suppressing triplet-triplet annihilation (TTA). These results suggest that adopting a similar molecular design strategy can not only reduce efficiency roll-off but also enhance device efficiency and operational stability, offering significant potential for future OLED applications.

Three organic blue-light-emitting tetraphenylethylene (TPE) derivatives that exhibit aggregation-induced emission (AIE) were used as additives in the preparation of inorganic perovskite-structured green-light-emitting materials for three-color white-light emission. For these organic–inorganic light-emitting materials, two-color (blue and green) light-emitting films based on the CsPbBr₃ perovskite-structured green-light-emitting inorganic material were prepared. The three TPE derivatives were prepared by varying the number of bromide groups, and a distinct AIE effect was confirmed when the derivatives were dissolved in a water–tetrahydrofuran mixed solvent containing 90 vol% water. When 0.2 molar ratio of the 1,1,2,2-tetrakis(4-bromophenyl)ethylene (TeBrTPE) additive was mixed with nanocrystal-pinning toluene solvent, the green-light-emission photoluminescence quantum efficiency (PLQY) value at 535 nm was 47 times greater than that of the pure bulk CsPbBr₃ without additives and a blue emission at 475 nm was observed from the TeBrTPE itself. When a CBP:Ir(piq)₃ film was prepared on top of this layer, three PL peaks with maximum wavelength values of 470, 535, and 613 nm were confirmed. The film exhibited white-light emission with CIE color coordinates of (0.25, 0.36).

Two new deep-blue emitters with bipolar properties based on an organoboron acceptor and carbazole donor were newly synthesized: 2-(9H-carbazol-9-yl)-5-(2,12-di-tert-butyl-5,9-dioxa-13b-boranaphtho [3,2,1-de]anthracen-7-yl)-5H-benzo[b]carbazole (TDBA-BCZ) and 5-(2,12-di-tert-butyl-5,9-dioxa-13b-boranaphtho [3,2,1-de]anthracen-7-yl)-8-phenyl-5,8-dihydroindolo[2,3-c]carbazole (TDBA-PCZ). The two emitters showed deep-blue and real-blue photoluminescence emission in their solution and film states, respectively. The doped spin-coated films were prepared using synthesized materials and showed a root-mean-square roughness of less than 0.52 nm, indicating excellent surface morphology. The doped devices, fabricated via a solution process using TDBA-BCZ and TDBA-PCZ as the dopants, showed electroluminescence peaks at 428 and 461 nm, corresponding to the Commission Internationale de L’éclairage (CIE) coordinates of (0.161, 0.046) and (0.151, 0.155), respectively. The external quantum efficiency (EQE)/current efficiency (CE) of the solution-processed forward devices, with TDBA-BCZ and TDBA-PCZ as dopants, were 7.73%/8.67 cd/A and 10.58%/14.24 cd/A, respectively. An inverted OLED device fabricated using rod-shaped ZnO nanoparticles as an electron injection layer showed a CE of 1.09 cd/A and an EQE of 0.30%.

New blue-light-emitting materials, 2,7-Bis-[1,1′;3′,1″]terphenyl-spiro-fluorene[3,4]naphthalene (TP-AFF-TP) and spiro-fluorene[3,4]-5-terphenylnaphthalene (TP-ASF) were synthesized based on a fused core with anthracene and spirofluorene. The photoluminescence (PL) maximum values of TP-AFF-TP and TP-ASF in film states exhibited 477 nm and 467 nm within the blue region, respectively. Degradation temperature (T_d) values for TP-AFF-TP and TP-ASF were very high at 481 °C and 407 °C, respectively. TP-AFF-TP and TP-ASF exhibited power efficiencies (PE) of 1.03 lm/W and 2.39 lm/W, respectively, along with luminance efficiencies (LE) of 2.55 cd/A and 5.17 cd/A, respectively, in nondoped organic light-emitting diode (OLED) devices in which the newly synthesized compounds were employed as emissive layers. The achieved CIE values were (0.25, 0.45) for TP-AFF-TP and (0.17, 0.31) for TP-ASF. Furthermore, when TP-ASF was utilized as one of the emissive materials in solution-processed white OLED devices, the resultant device showcased a notably high LE of 3.13 cd/A, a PE of 2.69 lm/W, and a white CIE value of (0.30, 0.34).