Asphalt pavements are widely used in airports due to their excellent skid resistance, vibration damping, and ease of construction. However, traditional fog seal materials often suffer from insufficient adhesion between fine sand and the emulsified asphalt binder, resulting in limited durability of the maintenance effect. This study aims to optimize the design of traditional fog seal materials and systematically evaluate their surface and durability performance. Firstly, a composite modified emulsified asphalt was prepared as the sand suspension slurry for the sand-containing fog seal. Through the dry wheel abrasion test, the optimal fine aggregates content was determined for four different spraying amounts (0.8, 0.9, 1.0, and 1.1 kg/m²). When the proportion of fine aggregates increases, the spraying amount needs to be increased accordingly to ensure the wrapping effect. Subsequently, pavement performance evaluation was conducted based on several indicators, including surface curing time, British Pendulum Number (BPN) friction coefficient, permeability coefficient, and mass loss rate. The results showed that the designed sand-containing fog seal significantly reduced surface curing time and exhibited superior skid resistance and permeability property compared to styrene-butadiene rubber (SBR)-modified emulsified asphalt. After freeze–thaw cycles, the maximum decrease in friction coefficient was 10.2%, and the mass loss rate after abrasion was approximately 67%, which were lower than those of SBR-modified emulsified asphalt (22.2% and 81%, respectively). Finally, considering the comprehensive performance comparison and evaluation, the optimal mix proportion was determined as 1.0 kg/m² spraying amount with 30% fine aggregates content. The findings of this study provide practical support for improving the durability and service life of airport asphalt pavements.

Foamed asphalt cold recycled mixtures can provide an effective approach for the reutilization of reclaimed asphalt pavement (RAP), but conventional asphalt foaming technology primarily exploits matrix asphalt as the raw material. To address this issue, this study explores rubberized asphalt with cold recycling technology to develop a foamed rubber asphalt cold recycled mixture (FRCM). The semi-circular bending (SCB) test was employed to investigate its cracking resistance. Load–crack mouth opening displacement (CMOD)–time curves under various temperatures were analyzed, and digital image technique was resorted to monitor crack propagation and growth rates. Fracture toughness, fracture energy, and flexibility index were compared with those of traditional foamed matrix asphalt cold recycled mixture (FMCM). The results show that, under the same test temperature, the FRCM exhibits slower crack propagation; larger peak load; and higher fracture toughness, fracture energy, and flexibility index in comparison with the FMCM. These improvements are more pronounced at low temperatures. For both mixtures, fracture toughness and fracture energy are decreased with increasing the temperature, while the flexibility index shows the opposite trend. The rigid zone accounts for a larger portion of fracture energy at low temperatures. The findings provide technical references for improving the cracking resistance of cold recycled asphalt layers using rubberized asphalt.