Nanocrystalline cobalt oxide Co₃O₄ has been prepared by precipitation and subsequent thermal decomposition of a carbonate precursor, and has been characterized in detail using XRD, transmission electron microscopy, and FTIR spectroscopy. The sensory characteristics of the material towards carbon monoxide in the concentration range 6.7–20 ppm have been examined in both dry and humid air. A sensor signal is achieved in dry air at sufficiently low temperatures T = 80–120 °C, but the increase in relative humidity results in the disappearance of sensor signal in this temperature range. At temperatures above 200 °C the inversion of the sensor signal in dry air was observed. In the temperature interval 180–200 °C the sensor signal toward CO is nearly the same at 0, 20 and 60% r.h. The obtained results are discussed in relation with the specific features of the adsorption of CO, oxygen, and water molecules on the surface of Co₃O₄. The independence of the sensor signal from the air humidity combined with a sufficiently short response time at a moderate operating temperature makes Co₃O₄ a very promising material for CO detection in conditions of variable humidity.

A quantum memristor combines the memristive dynamics with the quantum behavior of the system. We analyze the idea of a quantum memristor based on ultracold ions trapped in a Paul trap. Corresponding input and output memristor signals are the ion electronic levels populations. We show that under certain conditions the output/input dependence is a hysteresis curve similar to classical memristive devices. This behavior becomes possible due to the partial decoherence provided by the feedback loop, which action depends on previous state of the system (memory). The feedback loop also introduces nonlinearity in the system. Ion-based quantum memristor possesses several advantages comparing to other platforms—photonic and superconducting circuits—due to the presence of a large number of electronic levels with different lifetimes as well as strong Coulomb coupling between ions in the trap. The implementation of the proposed ion-based quantum memristor will be a significant contribution to the novel direction of “quantum neural networks”.

We have studied the electroluminescence (EL) and photoluminescence (PL) of solar cells containing a-Si:H/c-Si heterojunctions. It is established that both the EL and PL properties of these cells are determined by the radiative recombination of nonequilibrium carriers in crystalline silicon (c-Si). The external EL energy yield (efficiency) of solar cells with a-Si:H/c-Si heterojunctions at room temperature amounts to 2.1% and exceeds the value reached in silicon diode structures. This large EL efficiency can be explained by good passivation of the surface of crystalline silicon and the corresponding increase in lifetime of minority carrier s in these solar cells.

Hybrid samples consisting of polymer poly-3(hexylthiophene) (P3HT) and silicon nanoparticles were prepared. It was found that the obtained samples were polymer matrixes with conglomerates of silicon nanoparticles of different sizes (10–10⁴ nm). It was found that, under illumination, the process of nonequilibrium charge carrier separation between the silicon nanoparticles and P3HT with subsequent localization of the hole in the polymer can be successfully detected using electron paramagnetic resonance (EPR) spectroscopy. It was established that the main type of paramagnetic centers in P3HT/silicon nanoparticles are positive polarons in P3HT. For comparison, samples consisting only of polymer and silicon nanoparticles were also investigated by the EPR technique. The polarons in the P3HT and P_b centers in the silicon nanoparticles were observed. The possibility of the conversion of solar energy into electric energy is shown using structures consisting of P3HT polymer and silicon nanoparticles prepared by different methods, including the electrochemical etching of a silicon single crystal in hydrofluoric acid solution and the laser ablation of single-crystal silicon in organic solvents. The results can be useful for solar cell development.

Влияние наночастиц кремния на проводимость полианилина