This study aims to investigate the wear and corrosion–wear behavior of 17-4PH stainless steel specimens, both fabricated via Selective Laser Melting (SLM) and conventional bulk material, after undergoing Solution Treatment (S.T.) in a seawater medium. Microstructural observations indicated that solution treatment contributed to a more uniform distribution of martensitic structures on the sample surface. Moreover, the solution-treated specimens exhibited improved microstructural uniformity and structural stability. SLM specimens exhibit the elimination of fine particles and scanning track traces. Based on the results of dynamic polarization tests, SLM specimens demonstrate superior corrosion resistance. However, in corrosion–wear conditions, the bulk material outperforms the SLM specimens, primarily due to the presence of pores in the latter, which are detrimental under such environments. XPS analysis of the passive film structure indicates that the passive layer is mainly composed of FeO, Cr₂O₃, and NiO, with the inner layer predominantly consisting of chromium oxide. The Cr₂O₃ layer, formed by the reaction between chromium and oxygen, significantly enhances the corrosion resistance of the material due to its extremely low chemical reactivity and high stability.

Epoxy with low viscosity and good fluidity before curing has been widely applied in the packaging of electronic and electrical devices. Nevertheless, its low flexibility and toughness renders the requirement of property improvement before it can be widely acceptable in dynamic loading applications. This study investigates the possible use of 2-hydroxyethyl methacrylate (HEMA) toughening agent and nano-powders, such as alumina, silicon dioxide, and carbon black, to form epoxy composites for dynamic property improvement. Considering the different combinations of the nano-powders and HEMA toughener, the Taguchi method with an L9 orthogonal array was adopted for composition optimization. The dynamic storage modulus and loss tangent of the prepared specimen were measured by employing a dynamic mechanical analyzer. With polynomial regression, the curve-fitted relationships of the glass transition temperature and storage modulus with respect to the design factors were obtained. It was found that although the raise in the weight fraction of nano-powders was beneficial in increasing the rigidity of the epoxy composite, an optimal amount of HEMA toughener existed for its best damping improvement.

The performance improvement of advanced electronic packaging material is an important topic to meet the stringent demands of modern semiconductor devices. This paper studies the incorporation of nano-alumina powder and thermoplastic elastomer (TPE) into thermoplastic polystyrene matrix to tune the thermal and mechanical properties after injection molding process. In the sample preparation, acetone was employed as a solvent to avoid the powder escape into surrounding during the mechanical mixing in a twin-screw mixer. The pressure and shear force were able to mix the composite with good uniformity in compositions. The samples with different compositions were fabricated using injection molding. The measured results showed that adding 5 wt.% of TPE into the simple polystyrene was able to raise the melt flow index from 12.3 to 13.4 g/10 min while the thermal decomposition temperature remained nearly unchanged. Moreover, the addition of small amount of nano-alumina powder could quickly improve the mechanical property by raising its storage modulus. For example, the addition of 3 wt.% of nano-alumina powder had an increase of 7.3% in storage modulus. Over doping of nano-alumina powder in the composite, such as 10 wt.%, on the other hand, lowered the storage modulus from 2404 MPa to 2069 MPa. The experimental study demonstrated that the tuning in the polystyrene’s thermal and mechanical properties is feasible by composition modification with nano-alumina powder and TPE. The better concentration of the additives should be determined according to the specific applications.