Graphene modified TiO₂ composite photocatalysts have drawn increasing attention because of their high performance. Some significant advancements have been achieved with the continuous research, such as the corresponding photocatalytic mechanism that has been revealed. Specific influencing factors have been discovered and potential optimizing methods are proposed. The latest developments in graphene assisted TiO₂ composite photocatalysts are abstracted and discussed. Based on the primary reasons behind the observed phenomena of these composite photocatalysts, probable development directions and further optimizing strategies are presented. Moreover, several novel detective technologies—beyond the decomposition test—which can be used to judge the photocatalytic performances of the resulting photocatalysts are listed and analyzed. Although some objectives have been achieved, new challenges still exist and hinder the widespread application of graphene-TiO₂ composite photocatalysts, which deserves further study.

Graphene and its derivatives, with their unique two-dimensional structures and excellent physical and chemical properties, have been an international research hotspot both in the research community and industry. However, in application-oriented research in the oil and gas industry they have only drawn attention in the past several years. Their excellent optical, electrical, thermal and mechanical performance make them great candidates for use in oil and gas exploration, drilling, production, and transportation. Combined with the actual requirements for well working fluids, chemical enhanced oil recovery, heavy oil recovery, profile control and water shutoff, tracers, oily wastewater treatment, pipeline corrosion prevention treatment, and tools and apparatus, etc., this paper introduces the behavior in water and toxicity to organisms of graphene and its derivatives in detail, and comprehensively reviews the research progress of graphene materials in the upstream oil and gas industry. Based on this, suggestions were put forward for the future research. This work is useful to the in-depth mechanism research and application scope broadening research in the upstream oil and gas industry.

Carbon-silica composites with nanoporous structures were synthesized for the adsorption of volatile organic compounds (VOCs), taking tetraethyl orthosilicate (TEOS) as the silicon source and activated carbon powder as the carbon source. The preparation conditions were as follows: the pH of the reaction system was 5.5, the hydrophobic modification time was 50 h, and the dosage of activated carbon was 2 wt%. Infrared spectrum analysis showed that the activated carbon was dispersed in the pores of aerogel to form the carbon-silica composites material. The static adsorption experiments, dynamic adsorption-desorption experiments, and regeneration experiments show that the prepared carbon-silica composites have microporous and mesoporous structures, the adsorption capacity for n-hexane is better than that of conventional hydrophobic silica gel, and the desorption performance is better than that of activated carbon. It still has a high retention rate of adsorption capacity after multiple adsorption-desorption cycles. The prepared carbon-silica composites material has good industrial application prospects in oil vapor recovery, providing a new alternative for solving organic waste gas pollution.

An ordinary silica gel (SG-1) was chosen as the raw material and hydrophobically modified with trimethylchlorosilane under different microwave exposure. The orthogonal experiment was designed to screen the optimized modification method. The hydrophobic properties modified silica gel (SG-2) was analyzed by comparing the difference changes of surface chemistries. Then, the adsorption capacities of SG-1 and SG-2 to the n-hexane vapor and water vapor, respectively, were investigated and compared with the capacities of activated carbon and SG-3 (hydrophobically modified using the same composite modifier without microwave exposure). Meanwhile, there cyclable adsorptions of SG-2 to the two vapors were conducted while the desorptions of vacuum and heat was observed. The results showed that the effect of hydrophobic modification to SG-1 under microwave exposure was obvious and SG-2 also had a very good effect of adsorption for the n-hexane vapor. The modified silica gel shows great potential and effect for the recovery of volatile organic compounds with high content of water.