Per- and polyfluoroalkyl substances (PFASs), used since the 1940s, are persistent and carcinogenic pollutants. Water is a major exposure route; effective removal is essential. While nanofiltration (NF) and reverse osmosis (RO) are effective but costly, ultrafiltration (UF) membranes offer advantages such as lower cost and higher flux, but their relatively large pore size makes them ineffective for PFAS compounds like perfluorooctane sulfonic acid (PFOS) and perfluorooctanoic acid (PFOA). Since PFAS removal depends on both pore size and surface properties, this study investigates the effect of polyelectrolyte multilayer coatings using poly(allylamine hydrochloride) (PAH) and poly(acrylic acid) (PAA) on the zeta potential of UF membranes. Pristine UF membranes showed limited performance (UP150: ~2% for both PFOS and PFOA; UP020: 34.4% PFOS, 24.1% PFOA), while coating significantly enhanced removal (coated UP150: 45.3% PFOS, 43.4% PFOA; coated UP020: 77.8% PFOS, 73.3% PFOA). The modified UF membranes achieved PFAS removal efficiencies significantly closer to NF membranes, though still below those of RO (e.g., BW30XLE: up to 91.0% PFOS, 88.3% PFOA; NP030: up to 81.0% PFOS, 79.3% PFOA). Findings emphasize the importance of membrane surface charge and suggest that modified UF membranes offer a promising, low-cost alternative for PFAS removal under low-pressure conditions.

The objective of this study is to improve the filtration efficiency of commercially available polyethersulfone (PES) ultrafiltration (UF) membranes, with a specific focus on removing natural organic matter (NOM) and preventing membrane fouling. The modification of UF membranes was accomplished by utilizing chitosan/multi-walled carbon nanotubes (CS/MWCNT-OH) and employing both dip and spin coating techniques. The membrane surface morphologies were evaluated using the Attenuated Total Reflectance Fourier Transform Infrared Spectroscopy (ATR-FTIR), Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM), and Energy-Dispersive X-ray Spectroscopy (EDX) techniques. Tests were carried out to assess the effectiveness of the membranes in a laboratory-scale system using two primary water sources from Istanbul, specifically the Melen River and Terkos Lake. Total organic carbon (TOC), UV254 absorbance, turbidity, and trihalomethane formation potential (THMFP) were all measured as part of a thorough analysis. The surface morphology investigations verified the effective deposition of MWCNT-OH nanoparticles onto the membrane surface. This was corroborated by the reduction in the water contact angle, showing an improvement in the hydrophilicity of the membrane. The modified membranes demonstrated much higher TOC removal rates compared to the original membranes. Specifically, the removal efficiencies for Melen River and Terkos Lake were 37.14% and 56.86%, respectively. Nevertheless, the alteration of the surface led to a decline in membrane flux as a result of the concurrent drop in pore size. To summarize, the results of this work highlights the considerable capability of surface modification using CS/MWCNT-OH to improve the performance and antifouling characteristics of commercial PES UF membranes.

This study investigates the molecular weight distribution (MWD) of wastewater generated from a medium-density fiberboard (MDF) production facility to better understand the size and nature of organic pollutants and to identify suitable treatment methods. Sequential membrane filtration was performed using membranes with molecular weight cut-offs (MWCO) of 500, 150, 50, 10, and 1 kDa, and the filtrates were analyzed for key water quality parameters. Results indicated that 57% of the COD originated from particles larger than 1 µm, 72% from those larger than 0.22 µm, and 21.17% from fractions retained by the 1 kDa membrane, while only 6.43% was below this threshold after pretreatment. These findings demonstrate that the organic load in MDF wastewater is predominantly associated with suspended solids and high-molecular-weight organics. The hybrid use of microfiltration (MF) and nanofiltration (NF) membranes showed a potential to remove more than 90% of the high COD load, highlighting the feasibility of membrane-based treatment as an effective option for MDF wastewater.