This in vitro study evaluated the shear bond strength (SBS) of four CAD/CAM (Computer aided design/Computer aided manufacturing) polymer-based indirect composites bonded to dentin and microhybrid composite substrates using two resin cements. Gradia Plus (GP), Ceramage (Ce), Tescera ATL (TA), and Lava Ultimate (LA) were fabricated into cylindrical specimens (3 × 3 mm). Dentin substrates were obtained from extracted molars, while composite substrates were prepared from Filtek Z250 (4 mm × 2 mm). Bonding was performed using either a self-adhesive resin cement (RelyX U200; RU200) or a dual-cure adhesive resin cement (RelyX Ultimate; RU), resulting in 16 experimental groups (n = 12 per group). SBS was measured using a universal testing machine (1 mm/min), and failure modes were assessed under stereomicroscopy. Bond strength was significantly higher on composite substrates than on dentin (p < 0.001), primarily due to favorable polymer–polymer compatibility and matrix interdiffusion, which improved stress accommodation at the adhesive interface. TA and Ce showed superior adhesion when combined with RU, while LA exhibited the lowest values, particularly on dentin bonded with RU200. Overall, the dual-cure adhesive system provided stronger bonding than the self-adhesive system (p < 0.05). These findings highlight the influence of substrate type, composite architecture, and cement chemistry on interfacial performance in indirect polymer-based restorations.

Background: This in vitro study evaluated the effect of hydroxyapatite nanoparticle (nano-HAp) incorporation on surface roughness and Vickers hardness of a 3D-printed crown resin after thermocycling. Methods: Disk-shaped specimens (N = 84) were modified and fabricated with 0%, 1%, 2%, and 3% nano-HAp. Surface roughness (Ra) and Vickers hardness (VHN) were measured before and after thermocycling (5000 cycles). Surface morphology was qualitatively assessed using FE-SEM. Data were analyzed using two-way mixed-design ANOVA (α = 0.05). Results: Thermocycling increased surface roughness and reduced hardness in all groups. Ra values were highest in the 3% nano-HAp group after thermocycling (1.16 ± 0.47 µm). Baseline Vickers hardness differed significantly among nano-HAp concentrations, and hardness decreased after thermocycling in all groups; however, the 3% nano-HAp group exhibited the highest post-thermocycling hardness values (24.66 ± 1.51 VHN), which should be interpreted in the context of its higher baseline hardness. FE-SEM observations suggested increased surface irregularities with higher nano-HAp concentrations after thermocycling. Conclusions: Nano-HAp incorporation influenced both surface and mechanical properties, with 3% concentration showing higher hardness after aging but increased roughness.

Purpose: This research examines the release of mercury from dental amalgam restorations over time, analyzing the relationship between the number of restored surfaces and mercury levels in artificial saliva. Materials and Methods: An in vitro study was performed utilizing 224 plastic model teeth restored with dental amalgam. The teeth were categorized based on the number of surfaces restored, which ranged from Group 1 (1 surface) to Group 6 (48 surfaces). These were then immersed in artificial saliva, and the mercury levels were measured at intervals up to 30 days using atomic absorption spectrophotometry. Results: The release of mercury increased in correlation with both the number of restored surfaces and the passage of time. Significant differences were noted among the groups, with the highest release occurring in the group with the greatest number of surfaces. Mercury levels exhibited a consistent rise from baseline to day 30. Conclusions: The amount of mercury released from amalgam restorations increases in relation to both the number of restored surfaces and the duration of exposure.