Identification of the elastoplastic material model for C–Mn steel, using finite element model of micro-indentation test developed by the authors and proposed algorithm of inverse analysis, is one of the objectives of the project. The micro-indentation experiment is widely described in the present paper, especially those parts, which are meaningful in getting input data for direct, further application in the numerical model of micro-indentation test and in the inverse procedure. Finite element solution connected with the inverse algorithm, which is based on the simplex method, is used to search for the unknown parameters of material model. Validation of the developed inverse algorithm is the particular objective of the present work. The present paper shows that material model determined using the inverse analysis is in agreement with that obtained from the tensile test. The results coincide also with the data available in the literature.

An NbN coating was produced on AISI 316L steel using reactive DC magnetron sputtering. The effects of oxidation of the NbN coating in air on the microstructure, mechanical properties, corrosion resistance, contact angle and bioactivity were investigated. Phase composition was determined using X-ray diffraction (XRD), the coatings’ cross-sectional microstructure and thickness including surface morphology using a scanning electron microscope (SEM), microhardness via the Vickers method, corrosion by means of a potentiodynamic polarisation test in Ringer’s solution and bioactivity by observation in an SBF solution, while the contact angle was studied using a goniometer. The NbN coating and the oxidised coating were shown to demonstrate a Ca/P ratio close to that of hydroxyapatite, as well as increased microhardness and corrosion resistance. The best combination of mechanical, corrosion, bioactivity and hydrophilic properties was demonstrated by the air oxidised NbN coating, which featured an orthorhombic Nb₂O₅ structure in the top, surface layer.

AISI 316L steel was subjected to nitrocarburizing under glow discharge conditions, which was followed by DLC (diamond-like carbon) coatings deposition using the same device. The coatings were applied under conditions of direct current and pulsed glow discharge. In order to determine the influence of the produced nitrocarbon austenite layer and the type of discharge on the microstructure and mechanical properties of the coatings, the following features were analysed: surface roughness, coating thickness, structure, chemical composition, adhesion and resistance to frictional wear. For comparison purposes, DLC coatings were also deposited on steel without a nitrocarburised layer. The obtained results indicate a significant influence of the type of glow discharge on the roughness, hardness, nitrogen content and of the nitrocarburised layer on the resistance to wear by friction and adhesion of the produced coatings.