Various oxirane monomers including alkyl ether or allyl-substituted ones such as 1-butene oxide, 1-hexene oxide, 1-octene oxide, butyl glycidyl ether, allyl glycidyl ether, and 2-ethylhexyl glycidyl ether were anionically copolymerized with CO₂ into polycarbonates using onium salts as initiator in the presence of triethylborane. All copolymerizations exhibited a “living” character, and the monomer consumption was monitored by in situ Fourier-transform infrared spectroscopy. The various polycarbonate samples obtained were characterized by ¹H NMR, GPC, and differential scanning calorimetry. In a second step, all-polycarbonate triblock copolymers demonstrating elastomeric behavior were obtained in one pot by sequential copolymerization of CO₂ with two different epoxides, using a difunctional initiator. 1-Octene oxide was first copolymerized with CO₂ to form the central soft poly(octene carbonate) block which was flanked by two external rigid poly(cyclohexene carbonate) blocks obtained through subsequent copolymerization of cyclohexene oxide with CO₂. Upon varying the ratio of 1-octene oxide to cyclohexene oxide and their respective ratios to the initiator, three all-polycarbonate triblock samples were prepared with molar masses of about 350 kg/mol and 22, 26, and 29 mol % hard block content, respectively. The resulting triblock copolymers were analyzed using ¹H NMR, GPC, thermogravimetric analysis, differential scanning calorimetry, and atomic force microscopy. All three samples demonstrated typical elastomeric behavior characterized by a high elongation at break and ultimate tensile strength in the same range as those of other natural and synthetic rubbers, in particular those used in applications such as tissue engineering.

Although the aza-Michael addition reaction on various unsaturated (di-)carboxylic acids and esters of, for example, itaconic acid, is well-known, the consecutive cyclization reaction has not received much attention in literature. The products of this aza-Michael cascade reaction, being mono- or di-carboxylic acid or ester functionalized N-alkyl-pyrrolidone structures, prove interesting for melt-polycondensation reactions as they exhibit excellent stability at elevated temperatures. In other words, this reaction is a toolbox for the generation of renewable monomers and, in turn, polymers with tunable physiological properties. Therefore, this work provides an overview of the state-of-the-art of the cascade aza-Michael addition-cyclization reactions on biobased unsaturated acids and esters, and their use in polymerization reactions. Furthermore, we extend this overview with the cascade aza-Michael addition-cyclization reaction of trans-trimethyl aconitate with di-amines to form a tetra-functional N-alkyl-bis-(pyrrolidone dimethylcarboxylate), which exhibits excellent thermal stability and could effectively be used as monomer in polycondensation reactions. Importantly, the aza-Michael addition reaction between primary amines and trans-trimethyl aconitate can be considered a click-reaction; it proceeds quantitatively within minutes under ambient conditions and follows the principles of green chemistry.

The synthesis of renewable 2,5-furandicarboxylic acid-based cross-linked poly(ester amide)s via the polymerization of a 2,5-furandicarboxylic acid based bis(2-oxazoline) monomer (2,5-bis(4,5-dihydrooxazol-2-yl)furan, 2,5-FDCAox) with sebacic acid is reported in this work. It is demonstrated that the amide groups in the 2,5-furandicarboxamide moiety are susceptible to participation in a branching reaction with 2-oxazoline rings. The corresponding enhanced reaction rate decreases the curing times for the preparation of cross-linked polymers compared to systems containing the isophthalic acid based alternative, 1,3-bis(4,5-dihydrooxazol-2-yl)benzene (IAox). The increased tendency to form branches or cross-links in 2,5-FDCAox based systems is attributed to the occurrence of intra-molecular hydrogen bonding of the 2,5-furandicarboxamide moiety. Such an intra-molecular hydrogen bond increases the nucleophilicity of the furanic amide group and makes it more susceptible to participation in an addition reaction with a 2-oxazoline ring. Furthermore, it is demonstrated that the rate of the branching reaction can be enhanced by the addition of triphenyl phosphite as catalyst, resulting in a further decrease of the curing times of the poly(ester amide)s synthesized in this study. Preliminary coating studies indicate that 2,5-furandicarboxylic acid based cross-linked poly(ester amide)s synthesized via the 2-oxazoline ring opening addition reactions with dicarboxylic acids are good candidates for the development of fully renewable cross-linked poly(ester amide)s.