In recent years, the requirements for technical components have been increasing steadily. This development is intensified by the desire for products with lower weight, smaller size and extended functionality, but at the same time higher resistance against specific loads. Mono-material components manufactured according to established processes reach their limits regarding conflicting requirements. It is, for example, hardly possible to combine excellent mechanical properties with lightweight construction using mono-materials. Thus, a significant increase in production quality, lightweight design, functionality and efficiency can only be reached by combining different materials in one component. The superior aim of the Collaborative Research Centre (CRC) 1153 is to develop novel process chains for the production of hybrid solid components. In contrast to existing process chains in bulk metal forming, in which the joining process takes place during forming or at the end of the process chain, the CRC 1153 uses tailored semi-finished workpieces which are joined before the forming process. This results in a geometric and thermomechanical influence on the joining zone during the forming process which cannot be created by conventional joining techniques. The present work gives an overview of the CRC and the Tailored Forming approach including the applied joining, forming and finishing processes as well as a short summary of the accompanying design and evaluation methods.

A novel co-extrusion process for the production of coaxially reinforced hollow profiles has been developed. Using this process, hybrid hollow profiles made of the aluminum alloy EN AW-6082 and the case-hardening steel 20MnCr5 (AISI 5120) were produced, which can be forged into hybrid bearing bushings by subsequent die forging. For the purpose of co-extrusion, a modular tooling concept was developed where steel tubes made of 20MnCr5 are fed laterally into the tool. This LACE (lateral angular co-extrusion) process allows for a variation of the volume fraction of the reinforcement by using steel tubes with different wall thicknesses, which enabled the production of compound profiles having reinforcement contents of either 14 vol.% or 34 vol.%. The shear strength of the bonding area of these samples was determined in push-out tests. Additionally, mechanical testing of segments of the hybrid profiles using shear compression tests was employed to provide information about the influence of different bonding mechanisms on the strength of the composite zone.

The current study introduces a method for manufacturing steel–aluminum bearing bushings by compound forging. To study the process, cylindrical bimetal workpieces consisting of steel AISI 4820 (1.7147, 20MnCr5) in the internal diameter and aluminum 6082 (3.2315, AlSi1MgMn) in the external diameter were used. The forming of compounds consisting of dissimilar materials is challenging due to their different thermophysical and mechanical properties. The specific heating concept discussed in this article was developed in order to achieve sufficient formability for both materials simultaneously. By means of tailored heating, the bimetal workpieces were successfully formed to a bearing bushing geometry using two different strategies with different heating durations. A metallurgical bond without any forging defects, e.g., gaps and cracks, was observed in areas of high deformation. The steel–aluminum interface was subsequently examined by optical microscopy, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). It was found that the examined forming process, which utilized steel–aluminum workpieces having no metallurgical bond prior to forming, led to the formation of insular intermetallic phases along the joining zone with a maximum thickness of approximately 5–7 µm. The results of the EDS analysis indicated a prevailing Fe_xAl_y phase in the resulting intermetallic layer.

The combination of light metals and steels allows for new lightweight components with wear-resistant functional surfaces. Within the Collaborative Research Centre 1153 novel process chains are developed for the manufacture of such hybrid components. Here, the production process of a hybrid bearing bushing made of the aluminium alloy EN AW-6082 and the case-hardened steel 20MnCr5 is developed. Hybrid semi-finished products are an attractive alternative to conventional ones resulting from massive forming processes where the individual components are joined after the forming process. The actual hybrid semi-finished products were manufactured using a lateral angular co-extrusion (LACE) process. The bearing bushings are subsequently produced by die forging. In the present study, a tool concept for the LACE process is described, which renders the continuous joining of a steel rod with an aluminium tube possible. During the LACE process, the rod is fed into the extrusion die at an angle of approx. 90°. Metallographic analysis of the hybrid profile showed that the mechanical bonding between the different materials begins about 75 mm after the edge of the aluminium sheath. In order to improve the bonding strength, the steel rod is to be preheated during extrusion. Systematic investigations using a dilatometer, considering the maximum possible co-extrusion process parameters, were carried out. The variable parameters for the dilatometer experiments were determined by numerical simulation. In order to form a bond between the materials, the oxide layer needs to be disrupted during the co-extrusion process. In an attempt to better understand this effect, a modified sample geometry with chamfered steel was developed for the dilatometer experiments. The influence of the process parameters on the formation of the intermetallic phase at the interface was analysed by scanning electron microscopy and X-ray diffraction.

The use of lightweight materials is one possibility to limit the weight of vehicles and to reduce CO₂ emissions. However, the mechanical properties and weight-saving potential of mono-materials are limited. Material compounds can overcome this challenge by combining the advantages of different materials in one component. Lateral angular co-extrusion (LACE) allows the production of coaxial semi-finished products consisting of aluminum and steel. In this study, a finite element model of the LACE process was built up and validated by experimental investigations. A high degree of agreement between the calculated and experimentally determined forces, temperatures, and the geometrical shape of the hybrid profiles was achieved. In order to determine suitable parameters for further extrusion experiments, the influence of different process parameters on material flow and extrusion force was investigated in a numerical parametric study. Both the temperature and extrusion ratio showed a significant influence on the occurring maximum extrusion force as well as the material flow inside the LACE tool. The maximum force of 2.5 MN of the employed extrusion press was not exceeded. An uneven material flow was observed in the welding chamber, leading to an asymmetric position of the steel rod in the aluminum matrix.

Multi-material bulk metal components allow for a resource efficient and functionally structured component design, with a load adaptation achieved in certain functional areas by using similar and dissimilar material combinations. One possibility for the production of hybrid bulk metal components is Tailored Forming, in which pre-joined semi-finished products are hot-formed using novel process chains. By means of Tailored Forming, the properties of the joining zone are geometrically and thermomechanically influenced during the forming process. Based on this motivation, forming processes (die forging, impact extrusion) coupled with adapted inductive heating strategies were designed using numerical simulations and successfully realised in the following work in order to produce demonstrator components with serial or coaxial material arrangements. The quality of the joining zone was investigated through metallographic and SEM imaging, tensile tests and life cycle tests. By selecting suitable materials, it was possible to achieve weight savings of 22% for a pinion shaft and up to 40% for a bearing bush in the material combination of steel and aluminium with sufficient strength for the respective application. It was shown that the intermetallic phases formed after friction welding barely grow during the forming process. By adjusting the heat treatment of the aluminium, the growth of the IMP can also be reduced in this process step. Furthermore, for steel-steel components alloy savings of up to 51% with regard to chromium could be achieved when using low-alloy steel as a substitute for high-alloy steel parts in less loaded sections. The welded microstructure of a cladded bearing washer could be transformed into a homogeneous fine-grained microstructure by forming. The lifetime of tailored formed washers nearly reached those of high-alloyed mono-material components.