The aim of this study was to provide an experimental investigation on the novel method for recycling chips of duplex stainless steel, with the addition of vanadium carbide, in order to produce metal/carbide composites from a high-energy mechanical milling process. Powders of duplex stainless steel with the addition of vanadium carbide were prepared by high-energy mechanical ball milling utilizing a planetary ball mill. For this proposal, experiments following a full factorial design with two replicates were planned, performed, and then analyzed. The four factors investigated in this study were rotation speed, milling time, powder to ball weight ratio and carbide percentage. For each factor, the experiments were conducted into two levels so that the internal behavior among them could be statistically estimated: 250 to 350 rpm for rotation speed, 10 to 50 h for milling time, 10:1 to 22:1 for powder to ball weight ratio, and 0 to 3% carbide percentage. In order to measure and characterize particle size, we utilized the analysis of particle size and a scanning electron microscopy. The results showed with the addition of carbide in the milling process cause an average of reduction in particle size when compared with the material without carbide added. All the four factors investigated in this study presented significant influence on the milling process of duplex stainless steel chips and the reduction of particle size. The statistical analysis showed that the addition of carbide in the process is the most influential factor, followed by the milling time, rotation speed and powder to ball weight ratio. Significant interaction effects among these factors were also identified.

In this study, the high energy mechanical milling was utilized to the production of duplex stainless steel powders from the recycling chips with and without the addition niobium carbide. The effect of milling time and addition carbide on the morphology, particle size and magnetic properties of the powders was investigated. The utilization of the powder metallurgy constitute an important alternative for the reuse of waste in the industrial sector. The milling was realized using a planetary ball mill for 20 hours at a milling speed of 350 rpm and ball-to-powder weight ratio of 15:1were used, and the (0% and 3 wt. %) niobium carbide (NbC) addition. Scanning electron microscopy and particle distribution analysis were used for characterization of morphology and measure of particle size. Also, to analyze the transformations of phases were investigated using the magnetic characterization and x-ray diffraction. The results indicated that the addition of niobium carbide results in the reduction of the particle size of steel of the order of 20%, besides the reduces the transformation of austenite into strain induced martensitic phase.

Due to the increased consumption of raw materials, energy, and the waste it generates, recycling has become very important and fundamental for the environment and the industrial sector. The production of duplex stainless–steel powders with the addition of vanadium carbide in the high energy mechanical milling process is a new method for recycling materials for the manufacture of components in the industrial sector. This study aims to reuse the chips from the duplex stainless–steel UNS S31803 by powder metallurgy with the addition of Vanadium carbide (VC). The mechanical milling was performed using a planetary ball mill for 50 h at a milling speed of 350 rpm and a ball-to-powder weight ratio of 20:1, and the addition of 3 wt % of VC. The material submitted to milling with an addition of carbide has a particle size of less than 140 μm. After milling, the sample went through a stress relief treatment performed at 1050 °C for 1 h and the isostatic compaction process loaded with 300 MPa. The sintered powders and material was characterized by scanning electron microscopy, X-ray diffraction, and micro-hardness tests. The milling process with an addition of 3% VC produced a particle size smaller than the initial chip size. The measurement of micrometric sizes obtained was between 26 and 132 μm. The sintered material had a measurement of porosity evaluated at 15%. The obtained density of the material was 84% compared to the initial density of the material as stainless–steel duplex UNS S31803. The value of the microhardness measurement was 232 HV. The material submitted for grinding presented the formation of a martensitic structure and after the thermal treatment, the presence of ferrite and austenite phases was observed. Thus, in conclusion, this study demonstrates the efficacy in the production of a metal-ceramic composite using a new method to recycle stainless–steel duplex UNS S31803 chips.

This study aims to analyze the efficiency of niobium and vanadium carbides in the high energy mechanical milling of aluminum bronze alloy. Two series of experiments were made following the same steps for both niobium carbide (NbC) and vanadium carbide (VC) additions: 30 g of chips were weighed and placed in a stainless steel jar with 3 % of carbide and 1 % of stearic acid for a mass/sphere relationship of 1:10. The milling was realized using a planetary ball mill for 10, 30 and 50 hours in an inert argon atmosphere at 300 rpm. Results shown in laser diffraction indicate a great reduction in the particle sizes of powders when VC is used. For 30 hours milling, D50 values ranged from 1580 µm with NbC to 182.3 µm with VC addition. The D50 values ranged from 251.5 µm with NbC to 52.26 µm with VC addition, for 50 hours milling. The scanning electron microscopy showed that in 10 hours of milling, the energy was not sufficient to achieve the shear of chips in both cases. For 30 hours, it's possible to observe particles with sizes between 100 µm and 800 µm with NbC addition while for the same milling time, with VC it's possible to see particles with different sizes, but with many shapes of fine particulates. For 50 hours milling, particles achieved the smaller sizes between 50 and 200 µm with NbC and ranging from 5 until 50 µm with VC addition.