In the salt lake industry, large amounts of steamed ammonia liquid waste are discharged as byproducts. The conversion of the residues into high value-added vaterite-phase calcium carbonate products for industrial applications is highly desirable. In this research, the feasibility of preparing vaterite-phase CaCO₃ in different CaCl₂-CO₂-MOH-H₂O systems using steamed ammonia liquid waste was studied in the absence of additives. The effects of initial CaCl₂ concentration, stirring speed and CO₂ flow rate on the composition of the CaCO₃ crystal phase were investigated. The contents of vaterite were researched by the use of steamed ammonia liquid waste as a calcium source and pure calcium chloride as a contrast. The influence of the concentration of CNH₃·H₂O/C_Ca²⁺ on the carbonation ratio and crystal phase composition was studied. The reaction conditions on the content, particle size and morphology of vaterite influence were discussed. It was observed that single vaterite-phase CaCO₃ was favored in the CaCl₂-CO₂-NH₄OH-H₂O system. Additionally, the impurity ions in steamed ammonia liquid waste play a key role in the nucleation and crystallization of vaterite, which could affect the formation of single-phase vaterite. The obtained results provided a novel method for the preparation of single vaterite particles with the utilization of CO₂ and offered a selective method for the extensive utilization of steamed ammonia liquid waste.

In this study, the electronic structure of the galena surface was investigated using the first-principle calculation. The results of band structure, density of states, Mulliken population distribution, and frontier orbital analysis showed that galena was the p-type semiconductor of the direct band gap. During the formation of galena crystals, the 3p orbital of the S and the 6p orbital of the Pb played a primary role. Additionally, S atoms in galena quickly lose electrons and are oxidized, while Pb readily reacts with anions. The results of surface structure and electronic properties, such as surface relaxation, surface state energy levels, electronic density of states, and atomic charge distribution showed that the electronics in the 6p orbital of the Pb are transferred to the 3p orbital of the S in galena crystal. They caused the change of atomic valence states in lattice surfaces. The total electron number of the outermost surface layer was also higher than the bulk, giving the galena surface the properties of electron enrichment. This research is of great significance for developing new galena flotation reagents and for further in-depth exploration of the adsorption of reagents on the galena surface.

Benign design of alkali-activated slag/FA geopolymer paste has attracted increasing attention for optimizing its service performance. Therefore, the replacement of fly ash (FA) with 10 wt% silica fume (SF) is investigated by mechanical strength after freeze–thawing cycles and microstructure characterization. The results show that an appropriate dosage (30 wt%) of slag is necessary to prepare heat-free curing alkali-activated slag/FA geopolymer paste with excellent mechanical performance. The SF/slag/FA (SF:slag:FA = 10:30:60, wt%) geopolymer paste exerts an enhanced compressive and flexural strength of 95.2 and 3.2 MPa, respectively. Meanwhile, the doped 10 wt% SF facilitates the propagation of (N, C)-A-S-H chains, rather than the formation of C-S-H gels. It is evidenced by the absent exothermic peak at about 861 °C from the differential scanning calorimetry (DSC) curves. The pores volume and tortuosity also rise for the pore diameter < 20 nm from mercury intrusion porosimeter (MIP) results, corresponding to an improved freezing–thawing resistance with the residual compressive strength of 52.8 MPa and the weight loss of 10.5% after 300 freeze–thawing cycles. It explores a cost-effective and benign facile approach to designing heat-free curing alkali-activated slag/FA geopolymer paste with good freezing–thawing resistance.